The effect of lanthanoid (Ln = Nd, Sm, Ho) substitution on the structural and physical properties of the infinite-layer iron oxide SrFeO2 was investigated by X-ray diffraction (XRD) at ambient and high pressure, neutron diffraction, and 57Fe Mössbauer spectroscopy. Ln for Sr substituted samples up to â¼30% were synthesized by topochemical reduction using CaH2. While the introduction of the smaller Ln3+ ion reduces the a axis as expected, we found an unusual expansion of the c axis as well as the volume. Rietveld refinements along with pair distribution function analysis revealed the incorporation of oxygen atoms between FeO2 layers with a charge-compensated composition of (Sr1-xLnx)FeO2+x/2, which accounts for the failed electron doping to the FeO2 layer. The incorporated partial apical oxygen or the pyramidal coordination induces incoherent buckling of the FeO2 sheet, leading to a significant reduction of the Néel temperature. High-pressure XRD experiments for (Sr0.75Ho0.25)FeO2.125 suggest a possible stabilization of an intermediate spin state in comparison with SrFeO2, revealing a certain contribution of the in-plane Fe-O distance to the pressure-induced transition.
RESUMO
The rock salt (B1) structure of binary oxides or chalcogenides transforms to the CsCl (B2) structure under high pressure, with critical pressures P(s) depending on the cation to anion size ratio (R(c)/R(a)). We investigated structural changes of A(2)MO(3) (A = Sr, Ca; M = Cu, Pd) comprising alternate 7-fold B1 AO blocks and corner-shared MO(2) square-planar chains under pressure. All of the examined compounds exhibit a structural transition at P(s) = 29-41 GPa involving a change in the A-site geometry to an 8-fold B2 coordination. This observation demonstrates, together with the high pressure study on the structurally related Sr(3)Fe(2)O(5), that the B1-to-B2 transition generally occurs in these intergrowth structures. An empirical relation of P(s) and the R(c)/R(a) ratio for the binary system holds well for the intergrowth structure also, which means that P(s) is predominantly determined by the rock salt blocks. However, a large deviation from the relation is found in LaSrNiO(3.4), where oxygen atoms partially occupy the apical site of the MO(4) square plane. We predict furthermore the occurrence of the same structural transition for Ruddlesden-Popper-type layered perovskite oxides (AO)(AMO(3))(n), under higher pressures. For investigating the effect on the physical properties, an electrical resistivity of Sr(2)CuO(3) is studied.