RESUMO
Four imidazolium-based ionic liquids (IL; 1-butyl-3-methylimidazolium chloride, 1-carboxymethyl-3-methylimidazolium chloride, 1,3-dicarboxymethylimidazolium chloride and 1-(2-hydroxyethyl) -3-methylimidazolium chloride) were tested as compatibilizers of microcrystalline cellulose (MCC). Subsequently, ethanolic IL solutions were prepared; MCC was mixed, and the mixtures were left to evaporate the ethanol at ambient conditions. These modified MCC were characterized and applied as reinforcements (5.0 and 10 phr) in an epoxy resin aiming to manufacture biobased composites with enhanced performances. The IL did not significantly modify the morphological and structural characteristics of such reinforcements. Regarding the thermal stability, the slight increase was associated with the MCC-IL affinity. The IL-modified MCC-epoxy composites presented improved mechanical responses, such as flexural strength (≈22.5%) and toughness behavior (≈18.6%), compared with pure epoxy. Such improvement was also obtained for the viscoelastic response, where the storage modulus at the glassy state depended on the MCC amount and IL type. These differences were associated with stronger hydrogen bonding between IL and epoxy hardener or the IL with MCC, causing a "bridging" effect between MCC and epoxy matrix.
RESUMO
This study evaluates the hybridization effect of S2-glass/aramid on polyurethane (PU) composites produced by vacuum infusion. Different laminates were produced with similar thickness (around 2.5 mm), using, as reinforcement, only aramid fabrics (five layers, named as K5) or only S2-glass fabrics (eight layers, named as G8). Furthermore, hybridization was obtained by manufacturing symmetrical hybrid inter-ply laminates, with four S2-glass layers and two of aramid, (G2K)S and (KG2)S. The mechanical response of the laminates was evaluated in tensile, interlaminar shear strength, dynamical mechanical analysis and quasi-static indentation tests, and related to their morphological characteristics. The main results show that the pure glass composites presented less voids, but a higher density as well as higher tensile stiffness and strength. The aramid laminates showed a high capability for absorbing impact energy (ca. 30% higher than the pure glass laminates), and the hybrid laminates had intermediate properties. More importantly, this work shows the possibility of using a polyurethane matrix for vacuum infusion processing, effective even for aramid/S2-glass hybrid composites with thermoset polyurethane resin. This study is therefore promising for impact absorption in applications such as protective armor. The studied hybrid laminate may display a suitable set of properties and greater energy absorption capability and penetration resistance for impact applications.
RESUMO
Sandwich panels (SP) are very promising components for structures as they ally high levels of specific stiffness and strength. Civil, marine and automotive industries are some examples of the sectors that use SPs frequently. This work demonstrates the potential of manufacturing Z-pin-reinforced foam core SPs, using a design strategy that indicated optimal values for both pin position and angle, keeping the same pin diameter as determined in a previous study. A simple search algorithm was applied to optimize each design, ensuring maximum flexural stiffness. Designs using optimal pin position, optimal pin angle and optimal values for both parameters are herein investigated using numerical and experimental approaches. The optimal pin position yielded an increase in flexural stiffness of around 8.0% when compared to the non-optimized design. In this same comparison, the optimal pin angle by itself increased the flexural stiffness by about 63.0%. Besides, the highest increase in the maximum load was found for those composites, molded with optimized levels of pin position and pin angle, which synergistically contributed to this result. All results were demonstrated with numerical and experimental results and there was a good agreement between them.