Tuning the structure and physiochemical properties of sodium alginate and chitosan composite films through sodium tripolyphosphate (STPP) crosslinking.

Sodium tripolyphosphate (STPP), an inorganic and non-toxic polyphosphate, has potential applications as a crosslinking agent in the fabrication of edible films. This study utilized STPP in the development of sodium alginate-chitosan composite films, with a focus on their suitability for food packaging applications. The results indicate that the incorporation of STPP led to an increase in film thickness (from 0.048 ± 0.004 to 0.078 ± 0.008 mm), elongation at break (from 11.50 ± 1.49 % to 15.88 ± 2.14 %), water permeation (from 0.364 ± 0.010 to 0.521 ± 0.021 gmm/(m2h*kPa)), and moisture content (from 25.98 ± 0.20 % to 28.12 ± 0.17 %). In contrast, there was a decrease in tensile strength (from 30.23 ± 2.08 to 25.60 ± 1.22 MPa) and swelling index (from 752.9 ± 17.1 to 533.5 ± 8.9 %). Scanning electron microscopy (SEM) analysis revealed the formation of distinctive needle-like microcrystals with the incorporation of STPP. Fourier-transform infrared spectroscopy (FTIR) analysis indicated intermolecular interactions between STPP and the film-forming biopolymers. The data obtained from Thermogravimetric analysis (TGA) and Differential Scanning Calorimetry (DSC) demonstrated enhanced thermal stability of STPP-loaded films at elevated temperatures. Furthermore, the films exhibited increased DPPH scavenging activity with the addition of STPP. This study underscores the potential of STPP as a crosslinking agent for the development of composite edible films, suggesting applications in the field of food packaging.

Pectin/sodium alginate films tailored with Acetyl-11-keto-beta-boswellic acid for active packaging.

The present study aimed to develop food packaging films by using a combination of pectin (PE) and sodium alginate (SA) enriched with Acetyl-11-keto-beta-boswellic acid (AKBA) as a functional or active ingredient. The fabricated films underwent comprehensive evaluation of their morphological, chemical, mechanical, barrier, optical, thermal, antioxidant, and antimicrobial properties. SEM and FTIR analysis showed that AKBA had good compatibility with film-forming components. The AKBA-loaded film samples exhibited a decrease in their barrier properties and tensile strength, but enhancements in both elongation at break and thickness values was observed. With the addition of AKBA, a significant increase (p < 0.05) in the ultraviolet barrier properties of the films and total colour variation (ΔE) was observed. TGA analysis of the films unveiled an improvement in thermal resistance with the incorporation of AKBA. Moreover, the films loaded with AKBA exhibited potent antioxidant activity in the ABTS and DPPH assay methods. Disk diffusion analysis showed the antimicrobial activity of AKBA-loaded films against P. aeruginosa, highlighting the potential of AKBA as a natural antimicrobial agent for the safety of food products. The results demonstrate the practical application of PE and SA active films loaded with AKBA, particularly within the food packaging industry.