Enhancement in external quantum efficiency of AlGaInP red µ-LED using chemical solution treatment process.

To investigate the effects of their surface recovery and optical properties, extremely small sized (12 µm × 12 µm mesa area) red AlGaInP micro light emitting diodes ([Formula: see text] LED) were fabricated using a diluted hydrofluoric acid (HF) surface etch treatment. After the chemical treatment, the external quantum efficiencies (EQEs) of [Formula: see text]-LED at low and high injection current regions have been improved by 35.48% and 12.86%, respectively. The different phenomena of EQEs have a complex relationship between the suppression of non-radiative recombination originating from the etching damage of the surface and the improvement of light extraction of the sidewalls. The constant enhancement of EQE at a high injection current it is attributed to the expansion of the active region's sidewall surface area by the selective etching of AlInP layers. The improved EQE at a low injection current is related to the minimization of the surface recombination caused by plasma damage from the surface. High-resolution transmission electron microscopy (HR-TEM) revealed physical defects on the sidewall surface, such as plasma-induced lattice disorder and impurity contamination damage, were eliminated using chemical treatment. This study suggests that chemical surface treatment using diluted HF acid can be an effective method for enhancing the [Formula: see text]-LED performance.

Temperature-dependent resonance energy transfer from semiconductor quantum wells to graphene.

Resonance energy transfer (RET) has been employed for interpreting the energy interaction of graphene combined with semiconductor materials such as nanoparticles and quantum-well (QW) heterostructures. Especially, for the application of graphene as a transparent electrode for semiconductor light emitting diodes, the mechanism of exciton recombination processes such as RET in graphene-semiconductor QW heterojunctions should be understood clearly. Here, we characterized the temperature-dependent RET behaviors in graphene/semiconductor QW heterostructures. We then observed the tuning of the RET efficiency from 5% to 30% in graphene/QW heterostructures with ∼60 nm dipole-dipole coupled distance at temperatures of 300 to 10 K. This survey allows us to identify the roles of localized and free excitons in the RET process from the QWs to graphene as a function of temperature.