Layered Structure in the Crystalline Adsorption Layer and the Leaching Process of Poly(vinyl alcohol) Revealed by Neutron Reflectivity.

We investigated the structure of the crystalline adsorption layer of poly(vinyl alcohol) (PVA) in hot water by neutron reflectivity in two cases: when the adsorption layer is exposed on the substrate by leaching the upper bulk layer and when it is deeply embedded between a relatively thick PVA film and substrate. In both cases, the PVA adsorption layer consists of three layers on the Si substrate. The bottom layer, consisting of amorphous chains that are strongly constrained on the substrate, is not swollen even in hot water at 90 °C. The middle layer, consisting of amorphous chains that are much more mobile compared with those in the bottom layer, has no freedom to assume a crystalline form. Only the molecular chains in the top layer are crystallizable in the adsorption layer, leading to a heterogeneous layered structure in the film thickness direction. This layered structure is attributed to the crystallizable chains of PVA during the formation of the adsorption layer driven by hydrogen bonding. However, the structure and dynamics in the adsorption layer may differ in both cases because the molecular chains in the vicinity of the surface seem to be affected by surface effects even in the adsorption layer.

Fine-Structure Analysis of Perhydropolysilazane-Derived Nano Layers in Deep-Buried Condition Using Polarized Neutron Reflectometry.

A large background scattering originating from the sample matrix is a major obstacle for fine-structure analysis of a nanometric layer buried in a bulk material. As polarization analysis can decrease undesired scattering in a neutron reflectivity (NR) profile, we performed NR experiments with polarization analysis on a polypropylene (PP)/perhydropolysilazane-derived SiO2 (PDS)/Si substrate sample, having a deep-buried layer of SiO2 to elucidate the fine structure of the nano-PDS layer. This method offers unique possibilities for increasing the amplitude of the Kiessig fringes in the higher scattering vector (Qz) region of the NR profiles in the sample by decreasing the undesired background scattering. Fitting and Fourier transform analysis results of the NR data indicated that the synthesized PDS layer remained between the PP plate and Si substrate with a thickness of approximately 109 Å. Furthermore, the scattering length density of the PDS layer, obtained from the background subtracted data appeared to be more accurate than that obtained from the raw data. Although the density of the PDS layer was lower than that of natural SiO2, the PDS thin layer had adequate mechanical strength to maintain a uniform PDS layer in the depth-direction under the deep-buried condition.