Stress analysis of clasps made of glass fiber-reinforced composite material using three-dimensional finite element method: influence of shape in cross and longitudinal sections of circumferential clasp arms.

The purpose of this study was to investigate the effects of different cross-sectional shapes and presence of taper on stress distribution in clasp arms made of glass fiber-reinforced composite (FRC) material. Stress analysis of clasps was performed under a constant load (5 N) using a three-dimensional finite element method with due consideration to the anisotropy of unidirectional FRC material. Results were then compared with clasp arms made of metal- an isotropic material. It was found that both FRC clasps and metal clasps yielded similar results. As for the displacement of clasp arms with a basic cross-sectional shape under a load of 5 N, the amount of displacement showed that FRC clasps provided sufficient retentive force required for clinical application.

Application of a glass fiber-reinforced composite material to clasps--the effects of immersion and repeated loading.

The aim of this study was to investigate the effects of water immersion and repeated loading on the mechanical properties of a glass fiber-reinforced composite (FRC) material. Measurements for three-point flexural tests were made at three different temperatures and cross-head speeds, while measurements for fatigue tests were made under three different loads in air or water at 37 degrees C after each cycle. The flexural strength and elastic modulus of the immersed specimens were significantly lower than those of the dry specimens at the same cross-head speed and temperature. On the whole, the values were inferior to those of metal. The deflection increased significantly as the load increased, but there were no significant differences between the values of dry and immersed specimens. With increasing load and number of cycles, the permanent deformation of both specimens increased significantly. The permanent deformation was similar to that of Co-Cr alloy. Based on the results of this study, it is recommended that more effort be devoted to exploring and devising shapes that would render FRC clasp arms with mechanical and physical properties that differ favorably from those of metal.