Melt Spinning Process Optimization of Polyethylene Terephthalate Fiber Structure and Properties from Tetron Cotton Knitted Fabric.

Polyester/cotton fabrics with different proportions of Tetron Cotton, TC (35% Cotton/65% PET), and Chief Value Cotton, CVC (60% Cotton/40% PET), were investigated by removing the cotton component under various phosphoric acidic conditions including the use of cellulase enzymes. The remaining polyethylene terephthalate (PET) component was spun using the melt spinning method. Only 85% H3PO4-Enz_TC could be spun into consistent filament fibers. The effects of Acid-Enz TC (obtained from a powder preparation of 85% H3PO4-Enz_TC) at different weight amounts (1, 2, 5, and 10 %wt) blending with WF-rPET powder prepared by white recycled polyester fabric were evaluated for fiber spinnability at different winding speeds of 1000 and 1500 m/min. The results revealed that recycled PET fiber spun by adding Acid-Enz_TC up to 10 %wt gave uniformly distributed filament fibers. A comparative study of the physical, thermal, and mechanical properties also investigated the relationship between the effect of Acid-Enz_TC and the structure of the obtained fibers. Acid-Enz_TC:WF-rPET (5:95) was the optimal ratio. The thermal values were analyzed by DSC and TGA and crystallinity was analyzed by XRD, with mechanical strength closed to 100% WF-rPET. The FTIR analysis of the functional groups showed the removal of cotton from the blended fabrics. Other factors such as the Acid-Enz_TC component in WF-rPET, extraction conditions, purity, thermal, chemical, and exposure experiences also affected the formability and properties of recycled PET made from non-single-component raw materials. This study advanced the understanding of recycling PET from TC fabrics by strategically removing cotton from polyester-cotton blends and then recycling using controlled conditions and processes via the melt spinning method.

Bamboo Pulp Toughening Poly (Lactic Acid) Composite Using Reactive Epoxy Resin.

A novel poly (lactic acid) (PLA) composite with excellent mechanical properties, toughness, thermal stability, and water resistance was developed using a reactive melt-blending technique. PLA was melt mixed with epoxy resin (EPOXY) and bamboo pulp (PULP) to improve its reaction and mechanical properties. FTIR analysis confirmed the successful reaction of the PLA/EPOXY/PULP composites; the epoxy groups of EPOXY reacted with the -COOH groups of PLA and the -OH groups of PULP. The PLA/EPOXY/PULP5 composite showed a high tensile strength (67 MPa) and high toughness of 762 folding cycles, whereas the highest tensile strength was 77 MPa in the PLA/EPOXY5/PULP20 sample. SEM images presented a gap between the PLA and PULP; gap size decreased with the addition of EPOXY. The Tg of the PLA decreased with the EPOXY plasticizer effect, whereas the Tm did not significantly change. PULP induced crystallinity and increased Vicat softening of the PLA/PULP and PLA/EPOXY/PULP composites. The EPOXY reaction of the PLA/PULP composites improved their tensile properties, toughness, thermal stability, and water resistance.

Enhancement in mechanical and antimicrobial properties of epoxidized natural rubber via reactive blending with chlorhexidine gluconate.

An epoxidized natural rubber (ENR) blend with chlorhexidine gluconate (CHG) was prepared using a two-roll mill at 130 °C. CHG was added at concentrations of 0.2, 0.5, 1, 2, 5, and 10% (w/w) as an antimicrobial additive. The ENR blend with 10% (w/w) CHG showed the best tensile strength, elastic recovery, and Shore A hardness. The ENR/CHG blend exhibited a smooth fracture surface. The appearance of a new peak in the Fourier transform infrared spectrum confirmed that the amino groups of CHG reacted with the epoxy groups of ENR. The ENR with 10% CHG exhibited an inhibition zone against Staphylococcus aureus. The proposed blending improved the mechanical properties, elasticity, morphology, and antimicrobial properties of the ENR.

Effect of Recycling PET Fabric and Bottle Grade on r-PET Fiber Structure.

PET knitted fabric was melted and cooled by hot pressing at 250 °C to obtain a compacted sheet. Only white PET fabric (WF_PET) was used to study the recycling process by compression and grinding to powder and then melt spinning at different take-up speeds compared to PET bottle grade (BO_PET). PET knitted fabric had good fiber formability and was better suited for melt spinning of recycled PET (r-PET) fibers than the bottle grade. Thermal and mechanical properties of r-PET fibers improved in terms of crystallinity and tensile strength with increasing take-up speed (500 to 1500 m/min). Fading and color changes from the original fabric were relatively small compared with PET bottle grade. Results indicated that fiber structure and properties can be used as a guideline for improving and developing r-PET fibers from textile waste.