RESUMO
In the realm of surgical and dental applications, hyaluronic acid (HA) braided threads show significant therapeutic potential due to their incorporation of pharmaceutical active ingredients. This study primarily focuses on resolving the crucial challenge of devising a deposition method that can ensure both precision and uniformity in the content of the active ingredient Octenidine dihydrochloride (OCT) within each segment of the threads. Our objective in this study was to develop a continuous deposition method for OCT onto a braided thread composed of 24 hyaluronic acid-based fibers, aiming for a specific OCT content of 0.125 µg/mm, while maintaining a maximum allowable deviation of ±15% in OCT content. The motivation behind designing this novel method stemmed from the necessity of employing a volatile solvent for the active agent. Conventional wetting methods proved unsuitable due to fluctuations in the solution's concentration during deposition, and alternative methods known to us demanded intricate technical implementations. The newly introduced method offers distinct advantages, including its online processing speed, scalability potential, and cost-efficiency of the active agent solution. Additionally, it minimizes the impact on the natural polymer thread, preserving energy by obviating the need for complete thread saturation. Our research and precise apparatus development resulted in achieving the desired thread properties, with an OCT content of (1.51 ± 0.09) µg per 12 mm thread piece. These findings not only validate the suitability of this innovative method for depositing active agents but also extend its potential applicability beyond dental care.
RESUMO
This paper presents technological modifications of an electrostatic spinning device, which significantly increase the thickness homogeneity (i.e., quality) of produced layers by creating auxiliary dynamic electric fields in the vicinity of the spinning and collector electrodes. A moving body was installed above the needleless spinning electrode, which destabilized the standing wave occurring on the free surface of the spinning solution. Furthermore, an endless belt design was used for the collector electrode instead of a roll-to-roll design, which made it possible to substantially increase the surface speed of the substrate and, therefore, the dynamics of the electric field at the place of collection of the fibers being spun. As a result, the coefficient of variation of the area weight of 912 samples cut out from the deposited nanofibrous layer, which was (1000 × 500) mm2 in size and had an average area weight of (17.2 ± 0.8) g/m2, was less than 4.5%. These results were obtained only when the dynamics of both the spinning and collector electrodes were increased at the same time. These modifications resulted in a significant increase in the quality of deposited nanofibrous layers up to the standard required for their use in pharmaceutical applications.
RESUMO
A composite nanofibrous layer containing collagen and hydroxyapatite was deposited on selected surface areas of titanium acetabular cups. The layer was deposited on the irregular surface of these 3D objects using a specially developed electrospinning system designed to ensure the stability of the spinning process and to produce a layer approximately 100 micrometers thick with an adequate thickness uniformity. It was verified that the layer had the intended nanostructured morphology throughout its entire thickness and that the prepared layer sufficiently adhered to the smooth surface of the model titanium implants even after all the post-deposition sterilization and stabilization treatments were performed. The resulting layers had an average thickness of (110 ± 30) micrometers and an average fiber diameter of (170 ± 49) nanometers. They were produced using a relatively simple and cost-effective technology and yet they were verifiably biocompatible and structurally stable. Collagen- and hydroxyapatite-based composite nanostructured surface modifications represent promising surface treatment options for metal implants.
Assuntos
Nanoestruturas , Eletricidade Estática , Nanoestruturas/química , Nanoestruturas/ultraestrutura , Análise Espectral RamanRESUMO
Non-invasive optical diagnostic methods allow important information about studied systems to be obtained in a non-destructive way. Complete diagnosis requires information about the chemical composition as well as the morphological structure of a sample. We report on the development of an opto-mechanical probe that combines Raman spectroscopy (RS) and optical coherence tomography (OCT), two methods that provide all the crucial information needed for a non-invasive diagnosis. The aim of this paper is to introduce the technical design, construction and optimization of a dual opto-mechanical probe combining two in-house developed devices for confocal RS and OCT. The unique benefit of the probe is a gradual acquisition of OCT and RS data, which allows to use the acquired OCT images to pinpoint locations of interest for RS measurements. The parameters and the correct functioning of the probe were verified by RS scanning of various samples (silicon wafer and ex vivo tissue) based on their OCT images - lateral as well as depth scanning was performed. Both the OCT and RS systems were developed, optimized and tested with the ultimate aim of verifying the functionality of the probe. Picture: Schematic illustration and visualization of the developed RS-OCT probe.