Thermal, magnetic and electronic properties of non-centrosymmetric YbPt2B.

Ternary YbPt2B crystallizes in the non-centrosymmetric hexagonal CePt2B-type structure (space group P6(2)22). Electrical resistivity, specific heat and magnetic measurements reveal a magnetic instability at 5.6 K. Furthermore, a spin-reorientation of presumably a ferromagnetic type occurs around 1.5 K. The behaviour at low temperature is governed by a rather weak Kondo effect, T(K) ⩽ 1 K, in the presence of strong crystalline electric field splitting, with a doublet ground state. Besides, the complex magnetic behaviour presumably results from a Dzyaloshinskii-Moriya interaction triggered by the absence of inversion symmetry in the crystal structure. Scaling according to the de Gennes factor traces back magnetic ordering in YbPt2B to the Rudermann-Kittel-Kasuya-Yoshida (RKKY) interaction and the smooth evolution of the lattice constants and the unit cell volume of REPt2B (RE = rare earths) refers to the 4f(13) electronic configuration of Yb in YbPt2B.

Cage-forming compounds in the Ba-Rh-Ge system: from thermoelectrics to superconductivity.

Phase relations and solidification behavior in the Ge-rich part of the phase diagram have been determined in two isothermal sections at 700 and 750 °C and in a liquidus projection. A reaction scheme has been derived in the form of a Schulz-Scheil diagram. Phase equilibria are characterized by three ternary compounds: τ(1)-BaRhGe(3) (BaNiSn(3)-type) and two novel phases, τ(2)-Ba(3)Rh(4)Ge(16) and τ(3)-Ba(5)Rh(15)Ge(36-x), both forming in peritectic reactions. The crystal structures of τ(2) and τ(3) have been elucidated from single-crystal X-ray intensity data and were found to crystallize in unique structure types: Ba(3)Rh(4)Ge(16) is tetragonal (I4/mmm, a = 0.65643(2) nm, c = 2.20367(8) nm, and R(F) = 0.0273), whereas atoms in Ba(5)Rh(15)Ge(36-x) (x = 0.25) arrange in a large orthorhombic unit cell (Fddd, a = 0.84570(2) nm, b = 1.4725(2) nm, c = 6.644(3) nm, and R(F) = 0.034). The body-centered-cubic superstructure of binary Ba(8)Ge(43)□(3) was observed to extend at 800 °C to Ba(8)Rh(0.6)Ge(43)□(2.4), while the clathrate type I phase, κ(I)-Ba(8)Rh(x)Ge(46-x-y)□(y), reveals a maximum solubility of x = 1.2 Rh atoms in the structure at a vacancy level of y = 2.0. The cubic lattice parameter increases with increasing Rh content. Clathrate I decomposes eutectoidally at 740 °C: κ(I) ⇔ (Ge) + κ(IX) + τ(2). A very small solubility range is observed at 750 °C for the clathrate IX, κ(IX)-Ba(6)Rh(x)Ge(25-x) (x ∼ 0.16). Density functional theory calculations have been performed to derive the enthalpies of formation and densities of states for various compositions Ba(8)Rh(x)Ge(46-x) (x = 0-6). The physical properties have been investigated for the phases κ(I), τ(1), τ(2), and τ(3), documenting a change from thermoelectric (κ(I)) to superconducting behavior (τ(2)). The electrical resistivity of κ(I)-Ba(8)Rh(1.2)Ge(42.8)□(2.0) increases almost linearly with the temperature from room temperature to 730 K, and the Seebeck coefficient is negative throughout the same temperature range. τ(1)-BaRhGe(3) has a typical metallic electrical resistivity. A superconducting transition at T(C) = 6.5 K was observed for τ(2)-Ba(3)Rh(4)Ge(16), whereas τ(3)-Ba(5)Rh(15)Ge(35.75) showed metallic-like behavior down to 4 K.