Intermediate states on the way to edge-sharing BO4 tetrahedra in M6B22O39·H2O (M=Fe, Co).

The new borates Fe(II)(6)B(22)O(39)·H(2)O (colourless) and Co(II)(6)B(22)O(39)·H(2)O (dichroic: red/bluish) were synthesised under the high-pressure/high-temperature conditions of 6 GPa and 880 °C (Fe)/950 °C (Co) in a Walker-type multi-anvil apparatus. The compounds crystallise in the orthorhombic space group Pmn2(1) (Z=2) with the lattice parameters a=771.9(2), b=823.4(2), c=1768.0(4) pm, V=1.1237(4) nm(3), R(1)=0.0476, wR(2)=0.0902 (all data) for Fe(6)B(22)O(39)·H(2)O and a=770.1(2), b=817.6(2), c=1746.9(4) pm, V=1.0999(4) nm(3), R(1)=0.0513, wR(2)=0.0939 (all data) for Co(6)B(22)O(39)·H(2)O. The new structure type of M(6)B(22)O(39)·H(2)O (M=Fe, Co) is built up from corner-sharing BO(4) tetrahedra and BO(3) groups, the latter being distorted and close to BO(4) tetrahedra if additional oxygen atoms of the neighbouring BO(4) tetrahedra are considered in the coordination sphere. This situation can be regarded as an intermediate state in the formation of edge-sharing tetrahedra. The structure consists of corrugated multiple layers interconnected by BO(3)/BO(4) groups to form Z-shaped channels. Inside these channels, iron and cobalt show octahedral (M1, M3, M4, M5) and strongly distorted tetrahedral (M2, M6) coordination by oxygen atoms. Co(II)(6)B(22)O(39)·H(2)O is dichroic and the low symmetry of the chromophore [Co(II)O(4)] is reflected by the polarised absorption spectra (Δ(t)=4650 cm(-1), B=878 cm(-1)).

Synthesis and crystal structure of the new high-pressure phase CdB2O4.

The use of high-pressure/high-temperature conditions (7.5 GPa and 1100 degrees C; Walker-type multianvil apparatus) led to the synthesis of a new cadmium borate CdB2O4, starting from stoichiometric mixtures of the oxides. The crystal structure was determined on the basis of single crystal X-ray diffraction data, to reveal the hexagonal space group P6(3) with a=885.2(2), c=716.72(8) pm, Z=8, R1=0.0178, and wR2=0.0388 (all data). CdB2O4 is built up from interconnected layers of BO4-tetrahedra and exhibits for the first time the basic structure of a family of compounds, represented by BaGa2O4, KAlSiO4, KGeAlO4, KCoPO4, CaP2N4 and the recently discovered SrP2N4. The lack of superstructure ordering in CdB2O4 was confirmed by electron diffraction. Additionally, a B--O--B angle of 180 degrees was found in this borate for the first time.