Corrosion Behavior and Biocompatibility of Hot-Extruded Mg-Zn-Ga-(Y) Biodegradable Alloys.

Fixation screws and other temporary magnesium alloy fixation devices are used in orthopedic practice because of their biodegradability, biocompatibility and acceptable biodegradation rates. The substitution of dissolving implant by tissues during the healing process is one of the main requirements for biodegradable implants. Previously, clinical tests showed the effectiveness of Ga ions on bone tissue regeneration. This work is the first systematic study on the corrosion rate and biocompatibility of Mg-Zn-Ga-(Y) alloys prepared by hot extrusion, where Ga is an additional major alloying element, efficient as a bone-resorption inhibitor. Most investigated alloys have a low corrosion rate in Hanks' solution close to ~0.2 mm/year. No cytotoxic effects of Mg-2Zn-2Ga (wt.%) alloy on MG63 cells were observed. Thus, considering the high corrosion resistance and good biocompatibility, the Mg-2Zn-2Ga alloy is possible for applications in osteosynthesis implants with improved bone tissue regeneration ability.

Structure, Biodegradation, and In Vitro Bioactivity of Zn-1%Mg Alloy Strengthened by High-Pressure Torsion.

The effect of high-pressure torsion (HPT) on the microstructure, phase composition, mechanical characteristics, degradation rate, and bioactive properties of the Zn-1%Mg alloy is studied. An ultrafine-grained (UFG) structure with an average grain size of α-Zn equal to 890 ± 26 nm and grains and subgrains of the Mg2Zn11 and MgZn2 phases with a size of 50-100 nm are formed after HPT. This UFG structure leads to an increase in the ultimate tensile strength of the alloy by ~3 times with an increase in elongation to 6.3 ± 3.3% due to the formation of a basal texture. The study of corrosion resistance did not show a significant effect of HPT on the degradation rate of the alloy. In addition, no significant changes in the bioactivity of the alloy after HPT: hemolysis, cellular colonization and Escherichia coli growth inhibition.

Microstructure and Mechanical Properties of Hot-Extruded Mg-Zn-Ga-(Y) Biodegradable Alloys.

Magnesium alloys are attractive candidates for use as temporary fixation devices in osteosynthesis because they have a density and Young's modulus similar to those of cortical bone. One of the main requirements for biodegradable implants is its substitution by tissues during the healing process. In this article, the Mg-Zn-Ga-(Y) alloys were investigated that potentially can increase the bone growth rate by release of Ga ions during the degradation process. Previously, the effectiveness of Ga ions on bone tissue regeneration has been proved by clinical tests. This work is the first systematic study on the microstructure and mechanical properties of Mg-Zn-Y alloys containing Ga as an additional major alloying element prepared by the hot-extrusion process. The microstructure and phase composition of the Mg-Zn-Ga-(Y) alloys in as-cast, heat-treated, and extruded conditions were analyzed. In addition, it was shown that the use of hot extrusion produces Mg-Zn-Ga-(Y) alloys with favorable mechanical properties. The tensile yield strength, ultimate tensile strength, and elongation at fracture of the MgZn4Ga4 alloy extruded at 150 °C were 256 MPa, 343 MPa, and 14.2%, respectively. Overall, MgZn4Ga4 alloy is a perspective for applications in implants for osteosynthesis with improved bone regeneration ability.

Effect of Heat Treatment on the Mechanical and Corrosion Properties of Mg-Zn-Ga Biodegradable Mg Alloys.

Mg alloys have mechanical properties similar to those of human bones, and have been studied extensively because of their potential use in biodegradable medical implants. In this study, the influence of different heat treatment regimens on the microstructure and mechanical and corrosion properties of biodegradable Mg-Zn-Ga alloys was investigated, because Ga is effective in the treatment of disorders associated with accelerated bone loss. Solid-solution heat treatment (SSHT) enhanced the mechanical properties of these alloys, and a low corrosion rate in Hanks' solution was achieved because of the decrease in the cathodic-phase content after SSHT. Thus, the Mg-4 wt.% Zn-4 wt.% Ga-0.5 wt.% Y alloy after 18 h of SSHT at 350 °C (ultimate tensile strength: 207 MPa; yield strength: 97 MPa; elongation at fracture: 7.5%; corrosion rate: 0.27 mm/year) was recommended for low-loaded orthopedic implants.