Insights into the Origin of Activity Enhancement via Tuning Electronic Structure of Cu2O towards Electrocatalytic Ammonia Synthesis.

The insight of the activity phase and reaction mechanism is vital for developing high-performance ammonia synthesis electrocatalysts. In this study, the origin of the electronic-dependent activity for the model Cu2O catalyst toward ammonia electrosynthesis with nitrate was probed. The modulation of the electronic state and oxygen vacancy content of Cu2O was realized by doping with halogen elements (Cl, Br, I). The electrocatalytic experiments showed that the activity of the ammonia production depends strongly on the electronic states in Cu2O. With increased electronic state defects in Cu2O, the ammonia synthesis performance increased first and then decreased. The Cu2O/Br with electronic defects in the middle showed the highest ammonia yield of 11.4 g h-1 g-1 at -1.0 V (vs. RHE), indicating that the pattern of change in optimal ammonia activity is consistent with the phenomenon of volcano curves in reaction chemistry. This work highlights a promising route for designing NO3-RR to NH3 catalysts.

FeIII Chelated with Humic Acid with Easy Synthesis Conditions and Good Performance as Anode Materials for Lithium-Ion Batteries.

In this work, we prepared a green, cheap material by chelating humic acid with ferric ions (HA-Fe) and used it as an anode material in LIBs for the first time. From the SEM, TEM, XPS, XRD, and nitrogen adsorption-desorption experimental results, it was found that the ferric ion can chelate with humic acid successfully under mild conditions and can increase the surface area of materials. Taking advantage of the chelation between the ferric ions and HA, the capacity of HA-Fe is 586 mAh·g-1 at 0.1 A·g-1 after 1000 cycles. Moreover, benefitting from the chelation effect, the activation degree of HA-Fe (about 8 times) is seriously improved compared with pure HA material (about 2 times) during the change-discharge process. The capacity retention ratio of HA-Fe is 55.63% when the current density increased from 0.05 A·g-1 to 1 A·g-1, which is higher than that of HA (32.55%) and Fe (24.85%). In the end, the storage mechanism of HA-Fe was investigated with ex-situ XPS measurements, and it was found that the C=O and C=C bonds are the activation sites for storage Li ions but have different redox voltages.