RESUMO
The development trends in the energy sector clearly indicate an increase in the share of biomass and alternative fuels fed for combustion in power boilers, which results in the imposition of many unfavourable factors and a demanding working environment. During the operation of the energy system, this means a sharp increase in corrosion of the gas-tight pipe walls and coils by the destructive action of chlorine and sulphur. Implementing advanced surface protection in addition to the selection of materials of better quality and resistance to difficult working conditions would significantly reduce their wear by high temperature corrosion. Thermally sprayed coatings offer a great opportunity to protect machine components and energy systems against corrosion, erosion, impact load and abrasive wear. This article presents the test results of high-temperature corrosion resistance of coatings made with Ni-Cr-B-Si and Ni-B-Si alloy powders on a boiler steel substrate. Samples with sprayed coatings were exposed to an atmosphere with a composition of N2 + 9% O2 + 0.08% SO2 + 0.15% HCl at 800 °C for 250, 500, 750 and 1000 h. Tests results of coatings made of Ni-Cr-B-Si alloys subjected to the influence of a corrosive environment showed the formation of a layer of scale on the surface, composed mainly of Cr2O3 oxide, which was a passive layer, reducing the rate of corrosion. Coatings sprayed with Ni-B-Si alloys showed significantly lower corrosion resistance. It was found that the developed technology of subsonic flame spraying with powders of the Ni-Cr-B-Si type allows the production of coatings compliant with the requirements of the energy industry, which allows their use as anti-corrosion protection on boiler elements intended for waste disposal and biomass combustion.
RESUMO
This paper presents the synergy of the effect of two surface engineering technologies-magnetron sputtering (MS-PVD) and atomic layer deposition (ALD) on the structure and properties of 316L steel. Recent studies indicate that PVD coatings, despite their thickness of a few micrometers, have many discontinuities and structural defects, which may lead to pitting corrosion after time. Applying an ALD layer to a PVD coating seals its structure and contributes to extending the service life of the coating. Investigations of the structure and morphology of the produced layers were carried out using a scanning electron microscope (SEM) and atomic force microscope (AFM). In addition, the structure of the coatings was investigated on the cross-section using a scanning-transmission electron microscope S/TEM. The tribological properties of the materials studied were determined by the ball-on-disc method. The corrosion resistance of the tested materials was determined by the electrochemical potentiodynamic method by recording the polarization curves of the anodes. Additional information about the electrochemical properties of the tested samples, including the quality, their tightness, and their resistivity, was obtained by electrochemical impedance spectroscopy (EIS). In addition, the main mechanisms of corrosion and tribological wear were determined by SEM observations after corrosion tests and after tribological tests. The study showed that the fabrication of hybrid layers by MS-PVD and ALD techniques allows obtaining coatings with electrochemical properties superior to those of layers fabricated by only one method.
RESUMO
This paper aimed to investigate the structure and physicochemical and tribological properties of ZnO coatings deposited by ALD on 316L stainless steel for biomedical applications. To obtain ZnO films, diethylzinc (DEZ) and water were used as ALD precursors. Zinc oxide layers were deposited at the same temperature of 200 °C using three types of ALD cycles: 500, 1000 and 1500. The structure and morphology of ZnO coatings were examined using SEM and AFM microscopes. The XRD and GIXRD methods were used for the phase analysis of the obtained coatings. To determine the resistance to pitting corrosion, potentiodynamic investigations and impedance spectroscopy were conducted in a Ringer solution at a temperature of 37 °C. The obtained results showed that the number of ALD cycles had a significant impact on the structure, morphology and corrosion resistance of the ZnO layers. It was found that after increasing the coating thickness of the ZnO on the material, its electrochemical properties determining the corrosion resistance also increased. Moreover, on the basis of the ball-on-plate tribological investigations, we found a significant reduction in the friction coefficient of the samples with the investigated coatings in relation to the noncoated substrates.