Improving Thermal Stability of Polyurethane through the Addition of Hyperbranched Polysiloxane.

Polydimethylsiloxane with hydroxy groups was functionalized to form functionalized polydimethylsiloxane, which subsequently underwent an addition reaction with isophorone diisocyanate to form the prepolymer. Next, 3-aminopropyltriethoxysilane (APTS) reacted with 3-glycidoxypropyltrimethoxysilane (GPTS) to produce bridged polysilsesquioxanes, and sol-gel technology was employed to form hyperbranched polysiloxane nanoparticles with hydroxy groups, APTS-GPTS, which was used as the additive. The hyperbranched polysiloxane and the prepolymer containing NCO functional groups then underwent an addition reaction to produce the hybrid materials. Fourier-transform infrared spectroscopy and 29Si nuclear magnetic resonance were used to characterize the structure of the polyurethane hybrid. Regarding thermal stability, after the hyperbranched polysiloxane nanoparticles was introduced, the integral procedural decomposition temperature increased from 348 °C for polyurethane matrix to 859 °C for the hybrid material. The results reveal that the thermal stability of the hybrid material substantially increased by approximately 247%.

Preparation and Flame Retardance of Polyurethane Composites Containing Microencapsulated Melamine Polyphosphate.

A new microencapsulated flame retardant containing melamine polyphosphate (MPP) and 4,4'-oxydianiline-formaldehyde (OF) resin as the core and shell materials, respectively, was synthesized by in situ polymerization. 29Si NMR was used to measure the condensation density of polyurethane containing silicon compound (Si-PU). The structures and properties of the microencapsulated melamine polyphosphate (OFMPP) were characterized using X-ray photoelectron spectroscopy, scanning electron microscopy and water solubility. Thermal behavior of the OFMPP was systematically analyzed through thermogravimetric analysis. Flame retardance tests such as the limiting oxygen index and UL-94 were employed to evaluate the effect of composition variation on the MPP and OFMPP in polyurethane composites. The results indicated that the microencapsulation of MPP with the OF resin improved hydrophobicity and that the flame retardance of the Si-PU/OFMPP composite (limiting oxygen index, LOI = 32%) was higher than that of the Si-PU/MPP composite (LOI = 27%) at the same additive loading (30 wt %).