Synergic Effect of Metal and Fluorine Doping on the Structural and Electrical Properties of La5.4MoO11.1-Based Materials.

Cationic and anionic frameworks of La5.4MoO11.1 proton conductors have been modified by means of metal (Ti4+, Zr4+, and Nb5+) and fluorine (F-) doping. This synergic effect leads to the stabilization of high-symmetry and single-phase polymorphs. The materials have been fully characterized by structural techniques, such as X-ray and neutron powder diffraction and transmission electron microscopy. The fluorine content was determined by ion chromatography. Impedance spectroscopy analysis under different atmospheres (dry and wet N2 and O2 and wet 5% H2-Ar) showed an improvement in the electronic conductivity under reducing conditions, making these materials potential candidates for hydrogen separation membranes.

Metal-Doping of La5.4MoO11.1 Proton Conductors: Impact on the Structure and Electrical Properties.

La5.4MoO11.1 proton conductors with different metal doping (Ca2+, Sr2+, Ba2+, Ti4+, Zr4+, and Nb5+) have been prepared and structurally and electrically characterized. Different polymorphs are stabilized depending on the doping and cooling rate used during the synthesis process. The most interesting results are obtained for Nb-doping, La5.4Mo1- xNb xO11.1- x/2, where single compounds are obtained in the compositional range 0 ≤ x ≤ 0.2. These materials are fully characterized by structural techniques such as X-ray and neutron powder diffraction and transmission electron microscopy, which independently confirm the changes of polymorphism. Scanning electron microscopy and impedance spectroscopy measurements in dry/wet gases (N2, O2, and 5% H2-Ar) showed an enhancement of the sinterability and electrical properties of the materials after Nb-doping. Conductivity measurements under very reducing conditions revealed that these materials are mixed ionic-electronic conductors, making them potential candidates for hydrogen separation membranes.