Effect of ultrasonic instrumentation on the bond strength of crowns cemented with zinc phosphate cement to natural teeth. An in vitro study.

Several studies have reported the benefits of sonic and/or ultrasonic instrumentation for root debridement, with most of them focusing on changes in periodontal clinical parameters. The present study investigated possible alterations in the tensile bond strength of crowns cemented with zinc phosphate cement to natural teeth after ultrasonic instrumentation. Forty recently extracted intact human third molars were selected, cleaned and stored in physiologic serum at 4 degrees C. They received standard preparations, at a 16 masculine convergence angle, and AgPd alloy crowns. The crowns were cemented with zinc phosphate cement and then divided into four groups of 10 teeth each. Each group was then subdivided into two subgroups, with one of the subgroups being submitted to 5,000 thermal cycles ranging from 55 +/- 2 to 5 +/- 2 degrees C, while the other was not. Each group was submitted to ultrasonic instrumentation for different periods of time: group 1 - 0 min (control), group 2 - 5 min, group 3 - 10 min, and group 4 - 15 min. Tensile bond strength tests were performed with an Instron testing machine (model 4310). Statistical analysis was performed using ANOVA and Tukey's test at the 5% level of significance. A significant reduction in the tensile bond strength of crowns cemented with zinc phosphate and submitted to thermal cycles was observed at 15 min (196.75 N versus 0 min = 452.01 N, 5 min = 444.23 N and 10 min = 470.85 N). Thermal cycling and ultrasonic instrumentation for 15 min caused a significant reduction in tensile bond strength (p < .05).

Effect of ultrasonic instrumentation on the bond strength of crowns cemented with zinc phosphate cement to natural teeth: an in vitro study

Several studies have reported the benefits of sonic and/or ultrasonic instrumentation for root debridement, with most of them focusing on changes in periodontal clinical parameters. The present study investigated possible alterations in the tensile bond strength of crowns cemented with zinc phosphate cement to natural teeth after ultrasonic instrumentation. Forty recently extracted intact human third molars were selected, cleaned and stored in physiologic serum at 4°C. They received standard preparations, at a 16º convergence angle, and AgPd alloy crowns. The crowns were cemented with zinc phosphate cement and then divided into four groups of 10 teeth each. Each group was then subdivided into two subgroups, with one of the subgroups being submitted to 5,000 thermal cycles ranging from 55 ± 2 to 5 ± 2°C, while the other was not. Each group was submitted to ultrasonic instrumentation for different periods of time: group 1 - 0 min (control), group 2 - 5 min, group 3 - 10 min, and group 4 - 15 min. Tensile bond strength tests were performed with an Instron testing machine (model 4310). Statistical analysis was performed using ANOVA and Tukey's test at the 5 percent level of significance. A significant reduction in the tensile bond strength of crowns cemented with zinc phosphate and submitted to thermal cycles was observed at 15 min (196.75 N versus 0 min = 452.01 N, 5 min = 444.23 N and 10 min = 470.85 N). Thermal cycling and ultrasonic instrumentation for 15 min caused a significant reduction in tensile bond strength (p < .05).

Estudo da influência da ciclagem mecânica sobre a resistência de união ao cisalhamento entre uma cerâmica de recobrimento estético e duas cerâmicas infiltradas por vidro / Evaluation of the influence of cyclic loading on shear bond strength between one glass veneer ceramic and two glass-infiltrated ceramics

Este estudo avaliou a influência da ciclagem mecânica na resistência de união ao cisalhamento entre cerâmicas infiltradas por vidro para infra-estrutura (In-Ceram Alumina û Vita Zahnfabrik e In-Ceram Zircônia - Vita Zahnfabrik) e uma cerâmica vítrea de recobrimento (VITA VM7 - Vita Zahnfabrik). Foram preparadas vinte e quatro amostras cilíndricas nas dimensões de 4mm de diâmetro por 5mm de altura para cada cerâmica de infra-estrutura. Posteriormente, a cerâmica de recobrimento estético foi aplicada, resultando em corpos-de-prova com 4mm de diâmetro e 9mm de altura, os quais foram divididos em 4 grupos: ICA; ICAM; ICZ e ICZM. Os grupos ICAM e ICZM receberam ciclagem mecânica, com força de 50N, freqüência de 1Hz, durante 20000 ciclos. O ensaio de cisalhamento foi realizado em máquina de ensaio universal (modelo DL û 1000, EMIC û Equipamentos e Sistemas LTDA., São José dos Pinhais û PR û Brasil) com velocidade de 0,5mm/min e as amostras carregadas até a fratura. As interfaces das amostras pós-fratura foram analisadas em estereomicroscópio (20x) e microscopia eletrônica de varredura. As médias e desvios padrão obtidos foram: ICA (30,04 ± 11,74); ICAM (32,17 ± 9,59); ICZ (44,33 ± 11,47); ICZM (43,52 ± 8,33). Os dados obtidos (MPa) foram analisados estatisticamente por meio de análise de variância (ANOVA) dois fatores e teste de Tukey (P<0,05). Os resultados mostraram diferença estatisticamente significante entre os grupos In-Ceram Alumina e In-Ceram Zircônia, porém a ciclagem mecânica não influenciou na resistência de união entre as cerâmicas de infra-estrutura e de recobrimento estético estudadas

Estudo da lateração dimensional de um silicone polimerizado por reação de condensação / Investigation of the dimensional change of a condensation silicone

O objetivo deste trabalho foi avaliar a influência das características morfológicas da parede axial dos preparos em relaçãoà alteração dimensional de um silicone plimerizado por reação de condensação. Para isso, foi utilizado um modelo padrão em alumínio, co 04 pilares angulados de 7,5mm de altura, 9mm de largura e angulações: 0 graus (p1), 6 graus (P2), 16 graus (P3) e 6 graus com retenção na cervical (P4). A técnica de moldsagem utilizada foi a do material em consistência densa e fluida em dois estágios, com casquetes metálicos para alívio, o que originou espessura padronizada de 2,0mm para moldagem final. Foram obtidos 11 moldews (Silon 2APS, Dentsply), os quais preenchidos por gesso tipo IV (Durone, Dentsply), originaram os corpos-de-prova que, posteriormente, foram mensurados em um projetor de perfil (Jopnes & Lanson-mod.Epic-30E-Springfield, vermont-USA), com ampliação de 10x e resolução da ordem de 0,001mm. Posteriormente, esses valores foram comparados ao modelo padrão, submetidos à análise do intervalo de confiança e teste t student, sob nível de significância de 5%. Obtiveram-s eos seguintes valores para a largura dos corpos-de-prova: p1 (9,143+-0,061); p2 (9,066 +-0,094); p3(8,974+-0,084) e p4 (7,772+-0,311). Verificou-se diferença estatisticamente significante para a largura entre os pilares p1, p2 e p4, sendo que os corpos-de-provaq apresentaram-se mais largos do que o modelo padrão. Porém não houve diferença estatisticamente significante para a latura dos corpos-de-prova. Concluiu-se quwe quanto maior a angulação do preparo, menor a alteração dimensional

Estudo comparativo da alteração dimensional entre um silicone convencional e um de auto-mistura polimerizados por reação de condensação / Comparative study of dimensional changes between a conventional and an automixed condensation silicone

O objetivo deste trabalho foi avaliar a alteração dimensional de um silicone polimerizado por reação de condensação convencional e outro em auto-mistura. Para isso, foi empregado um modelo padrão com quatro pilares angulados, tendo um deles um sulco em forma de ôvõ na região cervical. A técnica de moldagem utilizada foi a do material em consistência densa e fluida em dois estágios, com casquetes metálicos para alívio, o que originou espessura padronizada de 2,0mm para moldagem final. Foram obtidos doze modelos em gesso pedra tipo IV (Durone - Dentsply Indústria e Comércio Ltda., Petrópolis-BRASIL) para cada condição experimental estudada. Os modelos foram mensurados em um projetor de perfil (Jones & Lanson-mod.Epic-30E-Springfield, Vermont-USA), com ampliação de 10x e suas medidas comparadas às do modelo padrão. Os resultados obtidos foram submetidos aos testes estatísticos de Kruskal-Wallis e de Dunn, ao nível de significância de 5%. Verificou-se que houve diferença estatisticamente significante para a largura entre os pilares com angulação de 16o (p3) e com sulco em forma de ôvõ (p4) dos corpos-de-prova obtidos com o silicone de auto-mistura e os pilares cilíndricos (p1) e com angulação de 6o (p2) dos corpos-de-prova obtidos com o silicone convencional. Sendo que os pilares p3 e p4 do grupo auto-mistura apresentaram-se mais largos do que p1 e p2 do grupo convencional. Porém não houve diferença estatisticamente significante para a altura dos corpos-de-prova.

Avaliação radiográfica do espaço residual apical de retentores intra-radiculares confeccionados a partir das técnicas de moldagem e modelagem / Residual apical space radiographic evaluation of intra radicular retainer obtained by moulding and moulage technique

Retentores intra-radiculares metálicos fundidos podem ser obtidos através de técnicas de moldagem e modelagem. Freqüentemente verifica-se um espaço entre o pino radicular e o remanescente do material obturador endodôntico (Falleiros, Collesi, 1988), viabilizando a contaminação da região periodontal, via canal acessório ou lateral não preenchido pelo material obturador (Shillingburg, Kessler, 1991).O objetivo deste trabalho foi comparar, radiograficamente, o espaço residual apical entre retentores intra-radiculares metálicos fundidos, confeccionados por meio das técnicas direta (modelagem) e indireta (moldagem), e o remanescente de material obturador do canal radicular. Para o levantamento dos dados deste trabalho, foram enviados para Cirurgiões-dentista questionário e filme radiográfico periapical duplo para a tomada radiográfica após cimentação do retentor intra-radicular e o espaço residual foi mensurado no software Image Tool 1.27. Houve diferença estatisticamente significante entre as técnicas de confecção dos retentores intra-raduculares. Verificou-se que o espaço residual apical foi menor nos retentores obtidos pela técnica de moldagem. Concluiu-se que a existência do espaço residual apical foi maior na técnica de modelagem que na de moldagem

Influência da sinvastatina na reparação óssea de mandíbulas de ratas / Influence of the sinvastatin on bone regeneration of mandibles of rats

O objetivo deste trabalho foi avaliar os efeitos da sinvastatina na reparação óssea guiada em mandíbulas de ratas através da densitometria óptica e análise histológica. Foram utilizadas 35 ratas, nas quais foi confeccionado um defeito ósseo bicortical no ângulo da mandíbula, que foi recoberto por barreira de politetrafluoretileno nas faces vestibular e lingual. Após a cirurgia, os animais foram divididos em 4 grupos tratados com 20mg/kg/dia de sinvastatina, via oral, durante 15 ou 30 dias e 3 grupos de controle. Os animais foram sacrificados 15, 30 ou 60 dias após a cirurgia, sendo a mandíbula removida para realização de densitometria óptica e análise histológica. Todos os espécimes foram submetidos à análise de variância (ANOVA) e teste de Tukey. Os resultados demonstraram que não houve diferença entre os grupos tratado e controle e que a média de neoformação óssea foi maior nos grupos sacrificados em 60 dias, seguidas pelas médias dos grupos de 30 e 15 dias. Conclui-se que a sinvastatina não teve efeito sobre o processo de reparo do tecido ósseo e que a quantidade de neoformação óssea aumentou conforme o tempo de observação