Simultaneous spray coating of interacting species: general rules governing the poly(styrene sulfonate)/poly(allylamine) system.

Simultaneous spraying of two solutions of interacting species onto a substrate held vertically leads to the formation of nanometer-sized coatings. Here we investigate the simultaneous spraying of poly(styrene sulfonate) (PSS) and poly(allylamine hydrochloride) (PAH) solutions leading to the formation of a film composed of PSS/PAH complexes. The thickness of this film increases linearly with the cumulative spraying time. For a given spraying rate of PAH (respectively PSS), the growth rate of the film depends strongly upon the PSS/PAH ratio and passes through a maximum for a PSS/PAH ratio lying between 0.55 and 0.8. For a PSS/PAH ratio that is maintained constant, the growth speed of the film increases linearly with the spraying rate of polyelectrolyte of both solutions. Using X-ray photoelectron spectroscopy, we find that the film composition is almost independent of the PSS/PAH (spayed) ratio, with composition very close to 1:1 in PSS:PAH film. The 1:1 PSS:PAH composition is explained by the fact that the simultaneous spraying experiments are carried out with salt-free solutions; thus, electroneutrality in the film requires exact matching of the charges carried by the polyanions and the polycations. Zeta potential measurements reveal that, depending on whether the PSS/PAH spraying rate ratio lies below or above the optimal spraying rate ratio, the film acquires a positive or a negative excess charge. We also find that the overall film morphology, investigated by AFM, is independent of the spraying rate ratio and appears to be composed of nanometer-sized grains which are typically in the 100 nm range.

Influence of the polyelectrolyte molecular weight on exponentially growing multilayer films in the linear regime.

Alternated deposition of polyanions and polycations on a charged solid substrate leads to the buildup of polyelectrolyte multilayer (PEM) films. Two types of PEM films were reported in the literature: films whose thickness increases linearly and films whose thickness increases exponentially with the number of deposition steps. However, it was recently found that, for exponentially growing films, the exponential increase of the film thickness takes place only during the initially deposited pairs of layers and is then followed by a linear increase. In this study, we investigate the growth process of hyaluronic acid/poly(L-lysine) (HA/PLL) and poly(L-glutamic acid)/poly(allylamine) (PGA/PAH) films, two films whose growth is initially exponential, when the growth process enters the linear regime. We focus, in particular, on the influence of the molecular weight (Mw) of the polyelectrolytes. For both systems, we find that the film thickness increment per polyanion/polycation deposition step in the linear growth regime is fairly independent of the molecular weights of the polyelectrolytes. We also find that when the (HA/PLL)n films are constructed with low molecular weight PLL, these chains can diffuse into the entire film during each buildup cycle, even for very thick films, whereas the PLL diffusion of high molecular weight chains is restricted to the upper part of the film. Our results lead to refinement of the buildup mechanism model, introduced previously for the exponentially growing films, which is based on the existence of three zones over the entire film thickness. The mechanism no longer needs all the "in" and "out" diffusing polyanions or polycations to be involved in the buildup process to explain the linear growth regime but merely relies on the interaction between the polyelectrolytes with an upper zone of the film. This zone is constituted of polyanion/polycation complexes which are "loosely bound" and rich in the polyelectrolyte deposited during the former deposition step.

Mechanically responsive films of variable hydrophobicity made of polyelectrolyte multilayers.

Mechanically responsive surfaces that allow to switch reversibly from a hydrophobic to a hydrophilic substrate are reported. The surfaces are constituted of polyelectrolyte multilayers deposited on modified charged silicone sheets. n bilayers of poly(allylamine)-Nafion (PAH-Naf) and m bilayers of poly(allylamine)-poly(acrylic acid) (PAH-PAA) composed the multilayers. A (PAH-Naf)(n) film possesses a water contact angle of around 105 degrees, whereas the contact angle of a (PAH-Naf)(4)-(PAH-PAA)(m) multilayer is around 50 degrees. When such a film with m < 5 and terminated by PAA is stretched out, its water contact angle increases up to around 100 degrees. Successive elongation/retraction cycles allow the water contact angle to alternate reversibly between 100 and 57 degrees indicating the reversible mechanical responsive nature of the film.

Polyelectrolyte multilayer films with pegylated polypeptides as a new type of anti-microbial protection for biomaterials.

Adhesion of bacteria at the surface of implanted materials is the first step in microbial infection, leading to post-surgical complications. In order to reduce this adhesion, we show that poly(L-lysine)/poly(L-glutamic acid) (PLL/PGA) multilayers ending by several PLL/PGA-g-PEG bilayers can be used, PGA-g-PEG corresponding to PGA grafted by poly(ethylene glycol). Streaming potential and quartz crystal microbalance-dissipation measurements were used to characterize the buildup of these films. The multilayer films terminated by PGA and PGA-g-PEG were found to adsorb an extremely small amount of serum proteins as compared to a bare silica surface but the PGA ending films do not reduce bacterial adhesion. On the other hand, the adhesion of Escherichia coli bacteria is reduced by 72% on films ending by one (PLL/PGA-g-PEG) bilayer and by 92% for films ending by three (PLL/PGA-g-PEG) bilayers compared to bare substrate. Thus, our results show the ability of PGA-g-PEG to be inserted into multilayer films and to drastically reduce both protein adsorption and bacterial adhesion. This kind of anti-adhesive films represents a new and very simple method to coat any type of biomaterials for protection against bacterial adhesion and therefore limiting its pathological consequences.

Cell interactions with polyelectrolyte multilayer films.

The short-term interactions of chondrosarcoma cells with polyelectrolyte multilayer films built up by the alternate adsorption of poly(L-lysine) (PLL) and poly(L-glutamic acid) (PGA) was studied in the presence and in the absence of serum. The films and their interaction with serum proteins were first characterized by means of optical waveguide lightmode spectroscopy, quartz crystal microbalance, and zeta potential measurements. In a serum-containing medium, the detachment forces measured by the micropipet technique were about eight times smaller on PGA-ending than on PLL-ending films. For these latter ones, the adhesion force decreased when the film thickness increased. In a serum-free medium, the differences between the negative- and positive-ending films were enhanced: adhesion forces on PLL-ending films were 40-100% higher, whereas no cellular adherence was found on PGA-terminating films. PGA-ending films were found to prevent the adsorption of serum proteins, whereas important protein adsorption was always observed on PLL-ending films. These results show how cell interactions with polyelectrolyte films can be tuned by the type of the outermost layer, the presence of proteins, and the number of layers in the film.