From rational design of organometallic precursors to optimized synthesis of core/shell Ge/GeO2 nanoparticles.

The synthesis of germanium nanoparticles has been carried out, thanks to the design of novel aminoiminate germanium(II) precursors: (ATI)GeZ (with Z = OMe, NPh2, and ATI = N,N'-diisopropyl-aminotroponiminate) and (Am)2Ge (Am = N,N'-bis(trimethylsilyl)phenyl amidinate). These complexes were fully characterized by spectroscopic techniques as well as single crystal X-ray diffraction. The thermolysis of both complexes yielded NPs which display similar features that are a Ge/GeO2 core/shell structure with a mean diameter close to 5 nm with a narrow size distribution (<15%). Whereas the high temperatures (>300 °C) classically reported in the literature for the preparation of germanium-based NPs were necessary for thermolysis of the complexes (ATI)GeZ, the use of amidinate-based precursors allows the preparation at an unprecedented low temperature (160 °C) for the thermolytic route. As suggested by a mechanistic study, the lower reactivity of (ATI)GeZ (for which the concomitant use of high temperature and acidic reagent is required) was explained in terms of lower ring strain compared to the case of (Am)2Ge.

Influence of chemical treatments on adhesion properties of hemp fibres.

In addition to be an environmentally friendly material, hemp fibres are also inexpensive reinforcements in thermoplastics or concrete composites, due to their intrinsic mechanical, thermal and acoustic properties. The morphology of hemp fibres has been chemically modified in order to enhance the matrix/fibre interface and has been examined by Scanning Electron Microscopy (SEM). In this paper, Gas Chromatography (GC) and Atomic Force Microscopy (AFM) were used to investigate the influence of treatments on the composition of hemp fibres and also on the micro-adhesive interactions between a silica colloidal probe and the surface of the fibres using Chemical Force Microscopy (CFM). Microscopy studies and chemical analysis showed that each treatment tends to lead to a morphology of interconnected web-like structure of hemp fibres. It was found that on an average, the adhesion force, contribution of capillary force and Van der Waals' forces, is higher in the case of NaOH treatment.