Development of antimicrobial coatings by atmospheric pressure plasma using a guanidine-based precursor.

Antimicrobial coatings deposited onto ultra high molecular weight polyethylene (UHMWPE) films were investigated using an atmospheric pressure - plasma enhanced chemical vapor deposition (AP-PECVD) process. Varying concentrations of a guanidine-based liquid precursor, 1,1,3,3-tetramethylguanidine, were used, and different deposition conditions were studied. Attenuated total reflectance - Fourier Transform Infrared (ATR-FTIR) spectroscopy and X-ray Photoelectron Spectroscopy (XPS) were used to study the chemical structure and elemental composition of the coatings. Conformity, morphology, and coating thickness were assessed through SEM and AFM. Optimal AP-PECVD parameters were chosen and applied to deposit guanidine coatings onto woven fabrics. The coatings exhibited high antimicrobial activity against Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus) based on a modified-AATCC 100 test standard, where 2-5 log reductions were achieved.

Hydrogel, aerogel and film of cellulose nanofibrils functionalized with silver nanoparticles.

In this work, we describe hydrogels, aerogels and films of nanofibrillated cellulose (NFC) functionalized with metal nanoparticles using silver as an example. The TEMPO process used to produce NFC generates negatively charged surface carboxylate groups that provide high binding capability to transition metal species such as Ag(+). The gelation of NFC triggered by transition monovalent metal ions was revealed for the first time. The interaction was utilized to bind Ag(+) on the NFC surface and simultaneously induce formation of NFC-Ag(+) hydrogels, where Ag(+) was slowly reduced to Ag nanoparticles by hydroxyl groups on NFC without additional reducing agent. The NFC-Ag(+) hydrogel was initiated by strong association of carboxylate groups on NFC with Ag(+) and sufficient NFC surface charge reduction. The stiff hydrogel has a storage modulus leveled off at a plateau value of ~6800Pa. Porous aerogels and flat thin films comprising a continuous matrix of NFC were decorated with Ag nanoparticles through freeze-drying or solution-casting of NFC-Ag(+) dispersions with low contents of Ag(+), respectively, followed by UV reduction. The presence of Ag species on NFC reduced coalescence of nanofibrils in the film formation as revealed from AFM phase images.