In Vitro Comparison of Differences in Setting Time of Premixed Calcium Silicate-Based Mineral Trioxide Aggregate According to Moisture Content of Gypsum.

Recently, a paste-type premixed calcium silicate-based mineral trioxide aggregate (MTA) product that quickly solidifies through a pozzolanic reaction was introduced to replace existing MTA, which has the disadvantage of a long setting time. In this study, we evaluated the effect of moisture content in the root canal on the setting time of premixed calcium silicate-based MTA in a simulated root canal environment using Endoseal MTA and Well-Root ST, among commercially available products. The setting time was measured according to ISO 6876/2012. A mold made using grades 2, 3, and 4 dental gypsum according to the classification of ISO 6873/2013 was used to reproduce the difference in moisture environment. Differences in moisture content were measured using micro-computed X-ray tomography (micro-CT). The micro-CT results showed that the moisture content was the highest and lowest in the grade 2 and 4 gypsum molds, respectively. Moreover, the setting time indicated by the manufacturer was the shortest for the grade 2 gypsum mold. Hence, the differences in moisture content significantly affect the setting time of MTA. This result can help set future experimental conditions and develop premixed calcium silicate-based MTA products.

Mechanical Properties of Dental Alloys According to Manufacturing Process.

The purpose of this study is to investigate the effect of the fabrication method of dental prosthesis on the mechanical properties. Casting was produced using the lost wax casting method, and milling was designed using a CAD/CAM program. The 3D printing method used the SLS technique to create a three-dimensional structure by sintering metal powder with a laser. When making the specimen, the specimen was oriented at 0, 30, 60, and 90 degrees. All test specimens complied with the requirements of the international standard ISO 22674 for dental alloys. Tensile strength was measured for yield strength, modulus of elasticity and elongation by applying a load until fracture of the specimen at a crosshead speed of 1.5 ± 0.5 mm/min (n = 6, modulus of elasticity n = 3). After the tensile test, the cross section of the fractured specimen was observed with a scanning electron microscope, and the statistics of the data were analyzed with a statistical program SPSS (IBM Corp. Released 2020. IBM SPSS Statistics for Windows, Version 27.0. Armonk, NY, USA: IBM Corp.) and using Anova and multiple comparison post-tests (scheffe method). The yield strength was the highest at 1042 MPa at an angle of 0 degrees in the specimen produced by 3D printing method, and the elongation was the highest at 14% at an angle of 90 degrees in the specimen produced by 3D printing method. The modulus of elasticity was the highest at 235 GPa in the milled specimen. In particular, the 3D printing group showed a difference in yield strength and elongation according to the build direction. The introduction of various advanced technologies and digital equipment is expected to bring high prospects for the growth of the dental market.

Evaluation of the Milling Accuracy of Zirconia-Reinforced Lithium Silicate Crowns Fabricated Using the Dental Medical Device System: A Three-Dimensional Analysis.

This study aimed to analyze the milling accuracy of lithium disilicate and zirconia-reinforced silicate crown fabricated using chairside computer-aided design/manufacturing (CAD/CAM) system. Mandibular left first premolar was selected for abutment. A master model was obtained for digital impression using an intraoral scanner, and crowns were designed using a CAD software design program. Amber Mill (AM), IPS e max CAD (IPS), and CELTRA DUO (CEL) were used in the CAD/CAM system, and a total 45 crowns (15 crowns each for AM, IPS, and CEL) was fabricated. Milling accuracy was analyzed with respect to trueness, measured by superimposing CAD design data and scan data through a three-dimensional program to compare the outer and inner surfaces and internal and external parts, thereby acquiring both quantitative and qualitative data. Data were analyzed using the non-parametric test and Kruskal-Wallis H test. In addition, the Mann-Whitney U test was used by applying the level of significance (0.05/3 = 0.016) adjusted by post-analysis Bonferroni correction. All the measured parts of the lithium disilicate and zirconia-reinforced silicate crowns showed statistically significant differences (p < 0.05). The lithium disilicate (AM and IPS) materials showed superior milling accuracy than the zirconia-reinforced lithium silicate (CEL) materials.

Influence of Orthodontic Anchor Screw Anchorage Method on the Stability of Artificial Bone: An In Vitro Study.

This study aims to compare the torque values for various lengths of the titanium-based orthodontic anchor screw (OAS), different anchorage methods and varying artificial bone densities after predrilling. Furthermore, the effects of these parameters on bone stability are evaluated. A total of 144 OASs were prepared with a diameter of 1.6 mm and heights of 6, 8 and 10 mm. Artificial bones were selected according to their density, corresponding to Grades 50, 40 and 30. Torque values for the automatic device and manual anchorage methods exhibited a statistically significant difference for the same-sized OAS, according to the bone density of the artificial bones (p < 0.05). However, when insertion torque was at the maximum rotations, there was no significant difference in the torque values for the Grade 30 artificial bone (p > 0.05). When the torque values of both anchorage methods were statistically compared with the mean difference for each group, the results of the manual anchorage method were significantly higher than those of the automatic device anchorage method (p < 0.05). A statistically significant difference was observed in the bone stability resulting from different OAS anchorage methods and artificial bone lengths. These findings suggest that the automatic anchorage method should be used when fixing the OAS.

Microscale diffusion measurements and simulation of a scaffold with a permeable strut.

Electrospun nanofibrous structures provide good performance to scaffolds in tissue engineering. We measured the local diffusion coefficients of 3-kDa FITC-dextran in line patterns of electrospun nanofibrous structures fabricated by the direct-write electrospinning (DWES) technique using the fluorescence recovery after photobleaching (FRAP) method. No significant differences were detected between DWES line patterns fabricated with polymer supplied at flow rates of 0.1 and 0.5 mL/h. The oxygen diffusion coefficients of samples were estimated to be ~92%-94% of the oxygen diffusion coefficient in water based on the measured diffusion coefficient of 3-kDa FITC-dextran. We also simulated cell growth and distribution within spatially patterned scaffolds with struts consisting of either oxygen-permeable or non-permeable material. The permeable strut scaffolds exhibited enhanced cell growth. Saturated depths at which cells could grow to confluence were 15% deeper for the permeable strut scaffolds than for the non-permeable strut scaffold.