This work focuses on the synthesis of LiFePO4-PANI hybrid materials and studies their electrochemical properties (capacity, cyclability and rate capability) for use in lithium ion batteries. PANI synthesis and optimization was carried out by chemical oxidation (self-assembly process), using ammonium persulfate (APS) and H3PO4, obtaining a material with a high degree of crystallinity. For the synthesis of the LiFePO4-PANI hybrid, a thermal treatment of LiFePO4 particles was carried out in a furnace with polyaniline (PANI) and lithium acetate (AcOLi)-coated particles, using Ar/H2 atmosphere. The pristine and synthetized powders were characterized by XRD, SEM, IR and TGA. The electrochemical characterizations were carried out by using CV, EIS and galvanostatic methods, obtaining a capacity of 95 mAhg-1 for PANI, 120 mAhg-1 for LiFePO4 and 145 mAhg-1 for LiFePO4-PANI, at a charge/discharge rate of 0.1 C. At a charge/discharge rate of 2 C, the capacities were 70 mAhg-1 for LiFePO4 and 100 mAhg-1 for LiFePO4-PANI, showing that the PANI also had a favorable effect on the rate capability.
RESUMO
The crystal structure of the title compound, [Ni3(C8H4O4)3(C3H7NO)4], is a two-dimensional coordination network formed by trinuclear linear Ni3(tp)3(DMF)4 units (tp = terephthalate = benzene-1,4-di-carboxyl-ate and DMF = di-methyl-formamide) displaying a characteristic coordination mode of acetate groups in polynuclear metal-organic compounds. Individual trinuclear units are connected through tp anions in a triangular network that forms layers. One of the DMF ligands points outwards and provides inter-actions with equivalent planes above and below, leaving the second ligand in a structural void much larger than the DMF mol-ecule, which shows positional disorder. Parallel planes are connected mainly through weak C-Hâ¯O, Hâ¯H and Hâ¯C inter-actions between DMF mol-ecules, as shown by Hirshfeld surface analysis.