Site-specific atom probe tomography (APT) from aluminum alloys has been limited by sample preparation issues. Indeed, Ga, which is conventionally used in focused-ion beam (FIB) preparations, has a high affinity for Al grain boundaries and causes their embrittlement. This leads to high concentrations of Ga at grain boundaries after specimen preparation, unreliable compositional analyses and low specimen yield. Here, to tackle this problem, we propose to use cryo-FIB for APT specimen preparation specifically from grain boundaries in a commercial Al-alloy. We demonstrate how this setup, easily implementable on conventional Ga-FIB instruments, is efficient to prevent Ga diffusion to grain boundaries. Specimens were prepared at room temperature and at cryogenic temperature (below approx. 90K) are compared, and we confirm that at room temperature, a compositional enrichment above 15 at.% of Ga is found at the grain boundary, whereas no enrichment could be detected for the cryo-prepared sample. We propose that this is due to the decrease of the diffusion rate of Ga at low temperature. The present results could have a high impact on the understanding of aluminum and Al-alloys.

Data on the impact of increasing the W amount on the mass density and compressive properties of Ni-W alloys processed by spark plasma sintering.

Bulk Ni-W alloys having composite-like microstructures are processed by spark plasma sintering (SPS) route of Ni and W powder blends as reported in a recent study of Sadat et al. (2016) (DOI of original article: doi:10.1016/j.matdes.2015.10.083) [1]. The present dataset deals with determination of mass density and evaluation of room temperature compressive mechanical properties as function of the amount of W (%wt. basis). The presented data concern: (i) measurement of the mass of each investigated Ni-W alloy which is subsequently used to compute the mass density of the alloy and (ii) the raw (stress (MPa) and strain ([Formula: see text])) data, which can be subsequently used for stress/ strain plots.