RESUMO
Urethane acrylate (UA) was synthesized from various di-polyols, such as poly(tetrahydrofuran) (PTMG, Mn = 1000), poly(ethylene glycol) (PEG, Mn = 1000), and poly(propylene glycol) (PPG, Mn = 1000), for use as a polymer binder for paint. Polymethyl methacrylate (PMMA) and UA were blended to form an acrylic resin with high transmittance and stress-strain curve. When PMMA was blended with UA, a network structure was formed due to physical entanglement between the two polymers, increasing the mechanical properties. UA was synthesized by forming a prepolymer using di-polyol and hexamethylene diisocyanate, which were chain structure monomers, and capping them with 2-hydroxyethyl methacrylate to provide an acryl group. Fourier transform infrared spectroscopy was used to observe the changes in functional groups, and gel permeation chromatography was used to confirm that the three series showed similar molecular weight and PDI values. The yellowing phenomenon that appears mainly in the curing reaction of the polymer binder was solved, and the mechanical properties according to the effects of the polyol used in the main chain were compared. The content of the blended UA was quantified using ultravioletvisible spectroscopy at a wavelength of 370 nm based on 5, 10, 15, and 20 wt%, and the shear strength and tensile strength were evaluated using specimens in a suitable mode. The ratio for producing the polymer binder was optimized. The mechanical properties of the polymer binder with 5-10 wt% UA were improved in all series.
RESUMO
Triol acrylic-urethane (t-AU) was synthesized from an addition reaction using trimethylolpropane, hexamethylene diisocyanate, and 2-hydroxyethyl methacrylate. The novel acrylic-urethane polymer was applied to a high-performance binder to prepare a reliable road marking paint. Acrylic-urethane polymer binder formulations were designed to optimize the effect of t-AU on the physical properties. The t-AU content in the formulation affected the adhesion and optical properties. The improvement in the adhesive performance and transparency ability for road markings was attributed to the optimal chemical structure or design of the acrylic-urethane polymer. The synthesis of t-AU was confirmed by Fourier transform infrared spectroscopy, and molecular weight and polydispersity index (PDI; PDI = Mw/Mn) measurements. The tensile and shear strength, hardness, gel fraction, crosslink density, contact angle, and transmittance of the acrylic-urethane polymer binder (AUP) were evaluated by curing at room temperature using a redox initiator system. An optimized AUP by adding 5 wt.% t-AU provides a viable alternative to high-performance binders in road marking paints.
RESUMO
In the current study, an acrylic polymer binder applicable to road signs was successfully developed by mixing various acrylic, acrylate-type, and photoinitiator-based monomer species at different acrylate series/silicone acrylate ratios. An amorphous acrylic monomer was used, and the distance between the polymers was increased to improve transparency. The binder was designed with the purpose of reducing the yellowing phenomenon due to resonance by excluding the aromatic ring structure, which is the main cause of yellowing. The optical properties of the binder were determined according to the content of n-butyl methacrylate/methyl methacrylate and the composition of the crosslinking agent in the formulation. Allyl glycidyl ether and dilauroyl peroxide were used to improve the yellowing problem of benzoyl peroxide, an aromatic photoinitiator. Adding a silicone-based trivalent acrylic monomer, 3-(trimethoxysilyl)propyl methacrylate (TMSPMA), was also found to have a significant effect on the transparency, shear properties, and water resistance of the binder. When 15 wt% TMSPMA was added, the best water repellency and mechanical properties were exhibited. The surface morphology of the improved binder and the peeling part were confirmed using field emission scanning electron microscopy. The acrylic polymer developed in this study can be applied in the coating and adhesive industries.
RESUMO
Polyurethane pressure-sensitive adhesives (PU-PSAs) with satisfactory tack, cohesion, and removability were newly developed through the synthetic process by reacting methylene diisocyanate, poly(ethylene glycol) (PEG), and a 1,4-butanediol chain extender based on the different HDI/HDI trimer ratios. The sticking properties of PU-PSAs depended on both the HDI/HDI trimer ratio and crosslinking-agent composition in the formulation. The molecular weight (MW) dependence of adhesion in PU-PSA was observed in the range of 1000 < Mn < 3000, suggesting that the increase in MW limits the pressure-sensitive adhesion of these samples. The differences in the crosslinking-density significantly affected the cohesion, adhesion, and tack in PU-PSA. The formulation of 50 wt.% 600PEG and 50 wt.% crosslinking-agent and an HDI/HDI trimer ratio of 1.0 led to the optimal balance between the adhesion and cohesion properties owing to the sufficient tack, high 180-peel strength, and good cohesion.
RESUMO
An acryl-functionalized polyurethane (PU) series was successfully synthesized using poly(tetramethylene ether) glycol-methylene diphenyl diisocyanate (PTMG-MDI) oligomer based on urethane methacrylates to control the flexibility of photo-cured 3D printing architectures. The mass ratio of acryl-urethane prepolymer: 1,4-butanediol (BD) chain-extender: diphenyl(2,4,6-trimethylbenzoyl) phosphine oxide (TPO) photoinitiator was 10:0.25:1. To produce suitably hard and precisely curved 3D architectures, the optimal UV absorbance and exposure energy of the acryl-PTMG-MDI resin were controlled precisely. Owing to the optimized viscosity of the acryl-PTMG-MDI resins, they could be printed readily by digital light processing (DLP) to form precisely curved 3D architectures after mixing with 1,6-hexanediol diacrylate (HDDA). The acryl-PTMG-MDI formulations showed much better flexural resolution than the neat resins. The printed 3D structure exhibited high surface hardness, good mechanical strength, and high elasticity for flexible applications in consumer/industrial and biomedical fields.
RESUMO
Photo-cured 3D architectures are successfully printed using the designed waterborne polyurethane-acrylate (WPUA) formulation. A WPUA series is synthesized in the presence of polycaprolactone diol (PCL) and 4,4'-methylene dicyclohexyl diisocyanate (H12MDI) as the soft segment part, dimethylolbutanoic acid (DMBA) as the emulsifier, and triethylamine (TEA) as the neutralizer, as a function of prepolymer molecular weight. The compatibility of WPUA and the photo-activating acryl monomer is as a key factor to guarantee the high resolution of 3D digital light processing (DLP) printing. The optimized blending formulations are tuned by using triacrylate monomers instead of diacrylate derivatives. For the high-accuracy and fine features of 3D DLP printing, WPUA are designed to be a suitable molecular structure for a 385 nm wavelength source, and the target viscosity is achieved in the range from 150 to 250 Cp. Photo-cured 3D architectures based on WPUA exhibit good flexural strength and high resolution.