Growth of Less than 20 nm SnO Nanowires Using an Anodic Aluminum Oxide Template for Gas Sensing.

Stannous oxide (SnO) nanowires were synthesized by a template and catalyst-free thermal oxidation process. After annealing a Sn nanowires-embedded anodic aluminum oxide (AAO) template in air, we obtained a large amount of SnO nanowires. SnO nanowires were first prepared by electrochemical deposition and an oxidization method based on an AAO template. The preparation of SnO nanowires used aluminum sheet (purity 99.999%) and then a two-step anodization procedure to obtain a raw alumina mold. Finally, transparent alumina molds (AAO template) were obtained by reaming, soaking with phosphoric acid for 20 min, and a stripping process. We got a pore size of < 20 nm on the transparent alumina mold. In order to meet electroplating needs, we produced a platinum film on the bottom surface of the AAO template by using a sputtering method as the electrode of electroplating deposition. The structure was characterized by X-ray diffraction (XRD). High resolution transmission electron microscopy (HRTEM) and field emission scanning electron microscopy (FESEM) with X-ray energy dispersive spectrometer (EDS) were used to observe the morphology. The EDS spectrum showed that components of the materials were Sn and O. FE-SEM results showed the synthesized SnO nanowires have an approximate length of ~10-20 µm with a highly aspect ratio of > 500. SnO nanowires with a Sn/O atomic ratio of ~1:1 were observed from EDS. The crystal structure of SnO nanowires showed that all the peaks within the spectrum lead to SnO with a tetragonal structure. This study may lead to the use of the 1D structure nanowires into electronic nanodevices and/or sensors, thus leading to nano-based functional structures.

Manipulating the Temperature of Sulfurization to Synthesize α-NiS Nanosphere Film for Long-Term Preservation of Non-enzymatic Glucose Sensors.

In this study, alpha nickel sulfide (α-NiS) nanosphere films have been successfully synthesized by electroplating the nickel nanosheet film on the indium tin oxide (ITO) glass substrate and sulfuring nickel-coated ITO glass substrate. First, we electrodeposited the nickel nanosheet films on the ITO glass substrates which were cut into a 0.5 × 1 cm2 size. Second, the nanosheet nickel films were annealed in vacuum-sealed glass ampoules with sulfur sheets at different annealing temperatures (300, 400, and 500 °C) for 4 h in vacuum-sealed glass ampoules. The α-NiS films were investigated by using X-ray diffraction (XRD), variable vacuum scanning electron microscopy (VVSEM), field emission scanning electron microscopy/energy dispersive spectrometer (FE-SEM/EDS), cyclic voltammogram (CV), electrochemical impedance spectroscopy (EIS), ultraviolet/visible/near-infrared (UV/Visible/NIR) spectra, and photoluminescence (PL) spectra. Many nanospheres were observed on the surface of the α-NiS films at the annealing temperature 400 °C for 4 h. We also used the high-resolution transmission electron microscopy (HR-TEM) for the analysis of the α-NiS nanospheres. We demonstrated that our α-NiS nanosphere film had a linear current response to different glucose concentrations. Additionally, our α-NiS nanosphere films were preserved at room temperature for five and a half years and were still useful for detecting glucose at low concentration.

Synthesis and characterization of single-crystalline zinc tin oxide nanowires.

Crystalline zinc tin oxide (ZTO; zinc oxide with heavy tin doping of 33 at.%) nanowires were first synthesized using the electrodeposition and heat treatment method based on an anodic aluminum oxide (AAO) membrane, which has an average diameter of about 60 nm. According to the field emission scanning electron microscopy (FE-SEM) results, the synthesized ZTO nanowires are highly ordered and have high wire packing densities. The length of ZTO nanowires is about 4 µm, and the aspect ratio is around 67. ZTO nanowires with a Zn/(Zn + Sn) atomic ratio of 0.67 (approximately 2/3) were observed from an energy dispersive spectrometer (EDS). X-ray diffraction (XRD) and corresponding selected area electron diffraction (SAED) patterns demonstrated that the ZTO nanowire is hexagonal single-crystalline. The study of ultraviolet/visible/near-infrared (UV/Vis/NIR) absorption showed that the ZTO nanowire is a wide-band semiconductor with a band gap energy of 3.7 eV.