Weldability and Mechanical Properties of Pure Copper Foils Welded by Blue Diode Laser.

The need to manufacture components out of copper is significantly increasing, particularly in the solar technology, semiconductor, and electric vehicle sectors. In the past few decades, infrared laser (IR) and green laser (GL) have been the primary technologies used to address this demand, especially for small or thin components. However, with the increased demand for energy saving, alternative joint techniques such as blue diode laser (BDL) are being actively explored. In this paper, bead-on-plate welding experiments on 0.2 mm thick pure copper samples employing a BDL are presented. Two sets of parameters were carefully selected in this investigation, namely Cu-1: Power (P) = 200 W; Speed (s) = 1 mm/s; and angle = 0°, and Cu-2: P = 200 W; s = 5 mm/s; and angle = 10°. The results from both sets of parameters produced defect-free full penetration welds. Hardness test results indicated relatively softer weld zones compared with the base metal. Tensile test samples fractured in the weld zones. Overall, the samples welded with Cu-1 parameters showed better mechanical properties, such as strength and elongation, than those welded with the Cu-2 parameters. The tensile strength and elongation obtained from Cu-1 were marginally lower than those of the unwelded pure copper. The outcomes from this research provide an alternative welding technique that is able to produce reliable, strong, and precise joints, particularly for small and thin components, which can be very challenging to produce.

Preheated (Heat-Assisted) Clinching Process for Al/CFRP Cross-Tension Specimens.

Effects of processing parameters on preheated (heat-assisted) clinching process to join aluminum alloy 5052-H32 (AA5052) and thermoplastic carbon-fiber-reinforced-plastic (TP-CFRP) sheets for cross-tension (CT) specimens were first studied. Preheating was critical since brittle TP-CFRP could be softened to avoid fracturing or cracking during clinching process. Four processing parameters, including punching force, die depth, heating mode, and heating temperature, were considered. Quasi-static tests and microscope observations were taken to evaluate AA5052/TP-CFRP clinch joints in CT specimens and determine appropriate processing parameters for fatigue tests. Finally, fatigue data and failure mode of clinch joints in CT specimens were obtained and discussed.

Design of Friction Stir Spot Welding Tools by Using a Novel Thermal-Mechanical Approach.

A simple thermal-mechanical model for friction stir spot welding (FSSW) was developed to obtain similar weld performance for different weld tools. Use of the thermal-mechanical model and a combined approach enabled the design of weld tools for various sizes but similar qualities. Three weld tools for weld radii of 4, 5, and 6 mm were made to join 6061-T6 aluminum sheets. Performance evaluations of the three weld tools compared fracture behavior, microstructure, micro-hardness distribution, and welding temperature of welds in lap-shear specimens. For welds made by the three weld tools under identical processing conditions, failure loads were approximately proportional to tool size. Failure modes, microstructures, and micro-hardness distributions were similar. Welding temperatures correlated with frictional heat generation rate densities. Because the three weld tools sufficiently met all design objectives, the proposed approach is considered a simple and feasible guideline for preliminary tool design.

Fabrication of Porous Materials from Natural/Synthetic Biopolymers and Their Composites.

Biopolymers and their applications have been widely studied in recent years. Replacing the oil based polymer materials with biopolymers in a sustainable manner might give not only a competitive advantage but, in addition, they possess unique properties which cannot be emulated by conventional polymers. This review covers the fabrication of porous materials from natural biopolymers (cellulose, chitosan, collagen), synthetic biopolymers (poly(lactic acid), poly(lactic-co-glycolic acid)) and their composite materials. Properties of biopolymers strongly depend on the polymer structure and are of great importance when fabricating the polymer into intended applications. Biopolymers find a large spectrum of application in the medical field. Other fields such as packaging, technical, environmental, agricultural and food are also gaining importance. The introduction of porosity into a biomaterial broadens the scope of applications. There are many techniques used to fabricate porous polymers. Fabrication methods, including the basic and conventional techniques to the more recent ones, are reviewed. Advantages and limitations of each method are discussed in detail. Special emphasis is placed on the pore characteristics of biomaterials used for various applications. This review can aid in furthering our understanding of the fabrication methods and about controlling the porosity and microarchitecture of porous biopolymer materials.