Structural Regulation Enables High Interfacial Functionality for Ni-Rich Single-Crystalline Cathodes.

Ni-rich single-crystalline layered cathodes have garnered significant attention due to their high energy density and thermal stability. However, they experience severe capacity degradation caused by lattice strain and interfacial side reactions during practical applications. In this study, an effective yttrium modification method is employed to stabilize the structure of Ni-rich single-crystalline LiNi0.83Mn0.05Co0.12O2 (SC-NMC83) to solve these issues. This innovative approach successfully immobilizes oxygen within the material, preventing crack formation while simultaneously broadening the diffusion path of Li+. The yttrium-modified sample (SC-NMC83-Y) exhibits a superior capacity retention compared to the SC-NMC83 sample, with values of 90% and 76.1% after 100 cycles, respectively. This work demonstrates the promising potential of a doping strategy for Ni-rich single-crystalline cathodes and paves a pathway for its practical implementation, such as all-solid-state batteries.

Ultra-thin and Mechanically Stable LiCoO2-Electrolyte Interphase Enabled by Mg2+ Involved Electrolyte.

LiCoO2 (LCO) cathode materials have attracted significant attention for its potential to provide higher energy density in current Lithium-ion batteries (LIBs). However, the structure and performance degradation are exacerbated by increasing voltage due to the catastrophic reaction between the applied electrolyte and delithiated LCO. The present study focuses on the construction of physically and chemically robust Mg-integrated cathode-electrolyte interface (MCEI) to address this issue, by incorporating Magnesium bis(trifluoromethanesulfonyl)imide (Mg[TFSI]2) as an electrolyte additive. During formation cycles, the strong MCEI is formed and maintained its 2 nm thickness throughout long-term cycling. Notably, Mg is detected not only in the robust MCEI, but also imbedded in the surface of the LCO lattice. As a result, the parasitic interfacial side reactions, surface phase reconstruction, particle cracking, Co dissolution and shuttling are considerably suppressed, resulting in long-term cycling stability of LCO up to 4.5 V. Therefore, benefit from the double protection of the strong MCEI, the Li||LCO coin cell and the Ah-level Graphite||LCO pouch cell exhibit high capacity retention by using Mg-electrolyte, which are 88.13% after 200 cycles and 90.4% after 300 cycles, respectively. This work provides a novel approach for the rational design of traditional electrolyte additives.