Island organization of TiO2 hierarchical nanostructures induced by surface wetting and drying.

We report on the reorganization and bundling of titanium oxide nanostructured layers, induced by wetting with different solvents and subsequent drying. TiO(2) layers are deposited by pulsed laser deposition and are characterized by vertically oriented, columnar-like structures resulting from assembling of nanosized particles; capillary forces acting during evaporation induce bundling of these structures and lead to a micrometer-size patterning with statistically uniform islands separated by channels. The resulting surface is characterized by a hierarchical, multiscale morphology over the nanometer-micrometer length range. The structural features of the pattern, i.e., characteristic length, island size, and channel width, are shown to depend on properties of the liquid (i.e., surface tension) and thickness and density of the TiO(2) layers. The studied phenomenon permits the controlled production of multiscale hierarchically patterned surfaces of nanostructured TiO(2) with large porosity and large surface area, characterized by superhydrophilic wetting behavior without need for UV irradiation.

Electronic structure of cluster assembled nanostructured TiO(2) by resonant photoemission at the Ti L(2,3) edge.

The electronic structure of cluster assembled nanostructured TiO(2) thin films has been investigated by resonant photoemission experiments with photon energies across the Ti L(2,3) edge. The samples were produced by supersonic cluster beam deposition with a pulsed microplasma cluster source. The valence band shows resonance enhancements in the binding energy region between 4 and 8 eV, populated by O 2p and hybridized Ti 3d states, and in the region about 1 eV below the Fermi level associated with defects related Ti 3d states. The data show that in as-deposited films Ti atoms are mainly fully (sixfolds) coordinated to oxygen atoms in octahedral symmetry and only a small fraction is in a broken symmetry environment. Since resonant photoemission is closely linked to the local electronic and structural configurations around the Ti atom, it is possible to correlate the resonant photoemission intensity and lineshape with the presence of defects of the films and with the degree of hybridization between the titanium and oxygen atoms.