GaSb quantum dots (QDs) have been grown by droplet epitaxy within InAlAs barrier layers on an InP (001) substrate. The droplet growth mode facilitates a larger size (average height â¼4.5 nm) and a lower density (â¼6.3 × 109 cm-2) for the QDs than would be expected for the 4% lattice mismatch between GaSb and InAlAs. A type-II band alignment between the GaSb QDs and the InAlAs barriers is revealed by photoluminescence (PL) through a prominent blue-shift of â¼0.11 eV resulting from a six orders of magnitude increase in excitation power. Further confirmation of the type-II nature of these QDs is found through time-resolved PL studies showing a biexponential decay with a long carrier lifetime of â¼10.9 ns. These observations reveal new information for understanding the formation and properties of GaSb/InAlAs/InP QDs, which may be an optimum system for the development of both efficient memory cells and photovoltaic devices.
RESUMO
Photoluminescence (PL) is investigated as a function of the excitation intensity and temperature for lattice-matched InGaAs/InAlAs quantum well (QW) structures with well thicknesses of 7 and 15 nm, respectively. At low temperature, interface fluctuations result in the 7-nm QW PL exhibiting a blueshift of 15 meV, a narrowing of the linewidth (full width at half maximum, FWHM) from 20.3 to 10 meV, and a clear transition of the spectral profile with the laser excitation intensity increasing four orders in magnitude. The 7-nm QW PL also has a larger blueshift and FWHM variation than the 15-nm QW as the temperature increases from 10 to ~50 K. Finally, simulations of this system which correlate with the experimental observations indicate that a thin QW must be more affected by interface fluctuations and their resulting potential fluctuations than a thick QW. This work provides useful information on guiding the growth to achieve optimized InGaAs/InAlAs QWs for applications with different QW thicknesses.