Photocatalytic H2 Production by Visible Light on Cd0.5Zn0.5S Photocatalysts Modified with Ni(OH)2 by Impregnation Method.

Nowadays, the study of environmentally friendly ways of producing hydrogen as a green energy source is an increasingly important challenge. One of these potential processes is the heterogeneous photocatalytic splitting of water or other hydrogen sources such as H2S or its alkaline solution. The most common catalysts used for H2 production from Na2S solution are the CdS-ZnS type catalysts, whose efficiency can be further enhanced by Ni-modification. In this work, the surface of Cd0.5Zn0.5S composite was modified with Ni(II) compound for photocatalytic H2 generation. Besides two conventional methods, impregnation was also applied, which is a simple but unconventional modification technique for the CdS-type catalysts. Among the catalysts modified with 1% Ni(II), the impregnation method resulted in the highest activity, for which a quantum efficiency of 15.8% was achieved by using a 415 nm LED and Na2S-Na2SO3 sacrificial solution. This corresponded to an outstanding rate of 170 mmol H2/h/g under the given experimental conditions. The catalysts were characterized by DRS, XRD, TEM, STEM-EDS, and XPS analyses, which confirmed that Ni(II) is mainly present as Ni(OH)2 on the surface of the CdS-ZnS composite. The observations from the illumination experiments indicated that Ni(OH)2 was oxidized during the reaction, and that it therefore played a hole-trapping role.

Effects of Preparation Conditions on the Efficiency of Visible-Light-Driven Hydrogen Generation Based on Ni(II)-Modified Cd0.25Zn0.75S Photocatalysts.

Hydrogen as an environmentally friendly fuel can be produced by photocatalytic procedures from aqueous systems, utilizing H2S, an industrial side-product, by conversion and storage of renewable solar energy. Although composites of CdS and ZnS prepared by co-precipitation are very efficient in heterogeneous photocatalytic H2 generation, the optimal conditions for their synthesis and the effects of the various influencing factors are still not fully clarified. In this work, we investigated how the efficiency of Cd0.25Zn0.75S composites modified with Ni(II) was affected by the doping method, Ni-content, hydrothermal treatment, and presence of a complexing agent (ammonia) used in the preparation. The composition, optical, and structural properties of the photocatalysts prepared were determined by ICP, DRS, XRD, TEM, and STEM-EDS. Although hydrothermal treatment proved preferable for Ni-free composites, Ni-modification was more efficient for untreated composites precipitated from ammonia-containing media. The best efficiency (14.9% quantum yield at 380 nm irradiation, 109.8 mmol/g/h hydrogen evolution rate) achieved by surface modification with 0.1-0.3% Ni(II) was 15% and 20% better than those for hydrothermally treated catalyst and similarly prepared Pt-modified one, respectively. Structural characterization of the composites clearly confirmed that the Ni2+ ions were not embedded into the CdS-ZnS crystal lattice but were enriched on the surface of particles of the original catalyst in the form of NiO or Ni(OH)2. This co-catalyst increased the efficiency by electron-trapping, but its too high amount caused an opposite effect by diminishing the excitable surface of the CdS-ZnS particles.

Poly-NIPAM/Fe3O4/multiwalled carbon nanotube nanocomposites for kerosene removal from water.

Multiwalled carbon nanotubes (MWCNTs) were oxidized using a mixture of H2SO4 and HNO3, and the oxidized MWCNTS were decorated with magnetite (Fe3O4). Finally, poly-N-isopropyl acrylamide-co-butyl acrylate (P-NIPAM) was added to obtain P-NIPAM/Fe/MWCNT nanocomposites. The nanosorbents were characterized by various techniques, including X-ray diffraction, transmission electron microscopy, scanning electron microscopy, thermogravimetric analysis, and Brunauer-Emmett-Teller analysis. The P-NIPAM/Fe/MWCNT nanocomposites exhibited increased surface hydrophobicity. Owing to their higher adsorption capacity, their kerosene removal efficiency was 95%; by contrast, the as-prepared, oxidized, and magnetite-decorated MWCNTs had removal efficiencies of 45%, 55%, and 68%, respectively. The P-NIPAM/Fe/MWCNT nanocomposites exhibited a sorbent capacity of 8.1 g/g for kerosene removal from water. The highest kerosene removal efficiency from water was obtained at a process time of 45 min, sorbent dose of 0.005 g, solution temperature of 40 °C, and pH 3.5. The P-NIPAM/Fe/MWCNTs showed excellent stability after four cycles of kerosene removal from water followed by regeneration. The reason may be the increase in the positive charge of the polymer at pH 3.5 and the increased adsorption affinity of the adsorbent toward the kerosene contaminant. The pseudo second-order model was found to be the most suitable model for studying the kinetics of the adsorption reaction.

Multiparameter Optimization of Naphthyridine Derivatives as Selective α5-GABAA Receptor Negative Allosteric Modulators.

The discovery and characterization of novel naphthyridine derivatives with selective α5-GABAAR negative allosteric modulator (NAM) activity are disclosed. Utilizing a scaffold-hopping strategy, fused [6 + 6] bicyclic scaffolds were designed and synthesized. Among these, 1,6-naphthyridinones were identified as potent and selective α5-GABAAR NAMs with metabolic stability, cardiac safety, and beneficial intellectual property (IP) issues. Relocation of the oxo acceptor function and subsequent modulation of the physicochemical properties resulted in novel 1,6-naphthyridines with improved profile, combining good potency, selectivity, ADME, and safety properties. Besides this, compound 20, having the most balanced profile, provided in vivo proof of concept (POC) for the new scaffold in two animal models of cognitive impairment associated with schizophrenia (CIAS).

The Photocatalytic and Antibacterial Performance of Nitrogen-Doped TiO2: Surface-Structure Dependence and Silver-Deposition Effect.

Catalysts for visible-light-driven oxidative cleaning processes and antibacterial applications (also in the dark) were developed. In order to extend the photoactivity of titanium dioxide into the visible region, nitrogen-doped TiO2 catalysts with hollow and non-hollow structures were synthesized by co-precipitation (NT-A) and sol-gel (NT-U) methods, respectively. To increase their photocatalytic and antibacterial efficiencies, various amounts of silver were successfully loaded on the surfaces of these catalysts by using a facile photo-deposition technique. Their physical and chemical properties were evaluated by using scanning electron microscopy (SEM), transmission electron microscopy-energy dispersive X-ray spectroscopy (TEM-EDS), Brunauer-Emmett-Teller (BET) surface area, X-ray diffraction (XRD), and diffuse reflectance spectra (DRS). The photocatalytic performances of the synthesized catalysts were examined in coumarin and 1,4-hydroquinone solutions. The results showed that the hollow structure of NT-A played an important role in obtaining high specific surface area and appreciable photoactivity. In addition, Ag-loading on the surface of non-hollow structured NT-U could double the photocatalytic performance with an optimum Ag concentration of 10-6 mol g-1, while a slight but monotonous decrease was caused in this respect for the hollow surface of NTA upon increasing Ag concentration. Comparing the catalysts with different structures regarding the photocatalytic performance, silverized non-hollow NT-U proved competitive with the hollow NT-A catalyst without Ag-loading for efficient visible-light-driven photocatalytic oxidative degradations. The former one, due to the silver nanoparticles on the catalyst surface, displayed an appreciable antibacterial activity, which was comparable to that of a reference material practically applied for disinfection in polymer coatings.

Characterization of kaolinite-ammonium acetate complexes prepared by one-step homogenization method.

Although kaolinite-ammonium acetate complexes are of interest in the area of kaolinite nanocomposites, the structures of these complexes have remained largely elusive. Experimental and molecular simulation analysis is used to investigate their structures, revealing that two types of water-containing kaolinite-ammonium acetate complex exist. A cost-efficient one-step homogenization method was used to synthesize these complexes. The effect of the aging time and the amount of reagents on the intercalation were characterized experimentally by X-ray diffraction, thermogravimetry, Fourier transform infrared spectroscopy and scanning electron microscopy. The optimal degree of intercalation was obtained by using two orders of magnitude lower amount of reagents than in the case of the solution method. It was found that the so far less investigated 1.7-nm complex has higher water content than the 1.4-nm one. For both complexes, our molecular simulations predict the double-layered structure of the acetate ions, which is usually assumed in the case of the kaolinite-acetate complexes. For the 1.7-nm complex, however, a quasi-triple-layered structure of water molecules instead of the double-layered one was calculated.

Water-mediated potassium acetate intercalation in kaolinite as revealed by molecular simulation.

Molecular simulations are suitable tools to study the adsorption and intercalation of molecules in clays. In this work, a recently proposed thermodynamically consistent force field for inorganic compounds (INTERFACE, Heinz H, Lin TJ, Mishra RK, Emami FS (2013) Langmuir 29:1754-1765), which enables accurate simulations of inorganic-organic interfaces, was tested for a two-sheet type clay mineral. All-atom NpT molecular dynamics simulations were used to describe the characteristics (basal spacing, loading, molecular orientation) of some intercalate complexes of kaolinite with potassium acetate and the results were compared with the available experimental data. The most probable structural configurations of the kaolinite/potassium acetate intercalate complexes were determined from the simulations. Our examinations confirmed some supposed (single- or double-layered) arrangements of guest molecules. The need of interlayer water in the intercalate complex, which can be produced by the basic synthesis procedure in air atmosphere, was verified.

Simulation-assisted evidence for the existence of two stable kaolinite/potassium acetate intercalate complexes.

Recent molecular simulation findings with several kaolinite intercalate complexes raised the question of the existence of more than one stable state, which has not been confirmed by experimental observations yet. Kaolinite/potassium acetate intercalate complexes were synthesized and examined by X-ray diffraction, and a molecular simulation study was performed for the system. Consistent with the suggestion from the simulations, an additional stable basal spacing was found experimentally at d(001)=1.168nm besides the well-known one at d(001)=1.403nm.

Simulation and experimental study of intercalation of urea in kaolinite.

Experimental measurements and molecular simulations were used to describe the characteristics of the kaolinite/urea intercalation compound. The intercalation compound was synthesized by a mechanochemical method and examined by X-ray diffraction and thermogravimetry. Additionally, a series of NpT (constant particle number-pressure-temperature) simulations was performed to identify thermodynamically stable basal spacings. From the simulations the most probable molecular orientations were determined for single and double layered arrangements of urea molecules that develop between the layers of kaolinite.

Kaolinite-urea complexes obtained by mechanochemical and aqueous suspension techniques--a comparative study.

Intercalation compounds of low- and high-defect kaolinites have been prepared by direct reaction with urea aqueous solution as well as by co-grinding with urea in the absence of water (mechanochemical intercalation). The complexes formed were studied by X-ray diffraction, thermal analysis, DRIFT spectroscopy, and scanning electron microscopy. In aqueous solution the degree of intercalation for the low- and high-defect kaolinites was found to be 77 and 65%, respectively. With mechanochemical intercalation, both kaolinites were almost fully expanded after 1 h of grinding. Based on the results of DRIFT spectroscopy, a structural model for the bonding of urea to the siloxane surface is proposed. The kaolinite-urea intercalation compounds produced by mechanochemical intercalation have crystallite sizes lower than those obtained by the aqueous solution method.

Investigation of mechanochemically modified kaolinite surfaces by thermoanalytical and spectroscopic methods.

The effect of mechanochemical activation (dry grinding), formamide intercalation, and thermal deintercalation on high- and low-defect kaolinite surfaces was studied by thermogravimetry and diffuse reflectance Fourier transform infrared spectroscopy. These investigations were completed with specific surface area and pore size distribution measurements. The surface acidity of the ground and the ground-and-intercalated kaolinites was probed with ammonia adsorption. The surface area and the pore volume as well as the amount of adsorbed ammonia increased with the rate of mechanochemical activation. At the same time the thermally deintercalated minerals showed increased surface area but decreased pore volume with the time of grinding. Adsorbed ammonia was detected as ammonium ion in the 1400-1500 cm(-1) spectral range.

Surface modification of mechanochemically activated kaolinites by selective leaching.

Low- and high-defect kaolinites mechanochemically activated for different periods of time have been treated with sulfuric acid solution. These modified materials were analyzed using a combination of X-ray diffraction, thermogravimetry, chemical analysis, diffuse reflectance Fourier transform infrared spectroscopy, as well as specific surface area and pore size distribution measurements. In addition to the mechanochemically amorphized part, the disordered and the adequately distorted phases also reacted with sulfuric acid. The specific surface areas of the leached samples of the partially or the completely amorphized materials were found to be greater than those of the thermally amorphized ones. The acid treatment results in a greater total pore volume for the partially amorphized materials than for the totally amorphized mineral. The partially amorphized high-defect kaolinite was proved to be more soluble than the low-defect kaolinite under similar conditions.

Modification of kaolinite surfaces through mechanochemical activation with quartz: A diffuse reflectance infrared fourier transform and chemometrics study.

Studies of kaolinite surfaces are of industrial importance. One useful method for studying the changes in kaolinite surface properties is to apply chemometric analyses to the kaolinite surface infrared spectra. A comparison is made between the mechanochemical activation of Kiralyhegy kaolinites with significant amounts of natural quartz and the mechanochemical activation of Zettlitz kaolinite with added quartz. Diffuse reflectance infrared Fourier transform (DRIFT) spectra were analyzed using principal component analysis (PCA) and multi-criteria decision making (MCDM) methods, the preference ranking organization method for enrichment evaluations (PROMETHEE) and geometrical analysis for interactive assistance (GAIA). The clear discrimination of the Kiralyhegy spectral objects on the two PC scores plots (400-800 and 800-2030 cm(-1)) indicated the dominance of quartz. Importantly, no ordering of any spectral objects appeared to be related to grinding time in the PC plots of these spectral regions. Thus, neither the kaolinite nor the quartz are systematically responsive to grinding time according to the spectral criteria investigated. The third spectral region (2600-3800 cm(-1), OH vibrations), showed apparent systematic ordering of the Kiralyhegy and, to a lesser extent, Zettlitz spectral objects with grinding time. This was attributed to the effect of the natural quartz on the delamination of kaolinite and the accompanying phenomena (i.e., formation of kaolinite spheres and water). The mechanochemical activation of kaolinite and quartz, through dry grinding, results in changes to the surface structure. Different grinding times were adopted to study the rate of destruction of the kaolinite and quartz structures. This relationship (i.e., grinding time) was classified using PROMETHEE and GAIA methodology.

Identification of superactive centers in thermally treated formamide-intercalated kaolinite.

The thermal behavior of a formamide-intercalated mechanochemically activated (dry-ground) kaolinite was investigated by thermogravimetry-mass spectrometry (TG-MS) and diffuse reflectance Fourier transform infrared spectroscopy (DRIFT). After the removal of adsorbed and intercalated formamide, a third type of bonded reagent was identified in the temperature range 230-350 degrees C decomposing in situ to CO and NH3. The presence of formamide decomposition products, as well as CO2 and various carbonates identified by DRIFT spectroscopy, indicates the formation of superactive centers as a result of mechanochemical activation and heat treatment (thermal deintercalation). The structural variance of surface species decreases with the increase of grinding time. The unground mineral contains a small amount of weakly acidic and basic centers. After 3 h of grinding, the number of acidic centers increases significantly, while on further grinding the superactive centers show increased basicity. With the increase of grinding time and treatment temperature the number of bicarbonate- and bidentate-type structures decreases in favor of the carboxylate- and monodentate-type ones.

A spectroscopic study of mechanochemically activated kaolinite with the aid of chemometrics.

The study of kaolinite surfaces is of industrial importance. In this work we report the application of chemometrics to the study of modified kaolinite surfaces. DRIFT spectra of mechanochemically activated kaolinites (Kiralyhegy, Zettlitz, Szeg, and Birdwood) were analyzed using principal component analysis (PCA) and multicriteria decision making (MCDM) methods, PROMETHEE and GAIA. The clear discrimination of the Kiralyhegy spectral objects on the two PC scores plots (400-800 and 800-2030 cm(-1)) indicated the dominance of quartz. Importantly, no ordering of any spectral objects appeared to be related to grinding time in the PC plots of these spectral regions. Thus, neither the kaolinite nor the quartz, are systematically responsive to grinding time according to the spectral criteria investigated. The third spectral region (2600-3800 cm(-1)OH vibrations), showed apparent systematic ordering of the Kiralyhegy and, to a lesser extent, Zettlitz spectral objects with grinding time. This was attributed to the effect of the natural quartz on the delamination of kaolinite and the accompanying phenomena (i.e., formation of kaolinite spheres and water). With the MCDM methods, it was shown that useful information on the basis of chemical composition, physical properties and grinding time can be obtained. For example, the effects of the minor chemical components (e.g., MgO, K(2)O, etc.) indicated that the Birdwood kaolinite is arguably the most pure one analyzed. In another MCDM experiment, some support was obtained for the apparent trend with grinding time noted in the PC plot of the OH spectral region.

Modification of low- and high-defect kaolinite surfaces: implications for kaolinite mineral processing.

A comparison is made of the mechanochemical activation of three low- and one high-defect kaolinite using a combination of X-ray diffraction, thermal analysis, and DRIFT spectroscopy. The effect of mechanochemical alteration of the kaolinites is greater for the low-defect kaolinites. The effectiveness of the mechanochemical treatment is represented by the slope of the d(001) peakwidth-grinding time line. High-defect kaolinite is not significantly altered by the grinding treatment. The effect of mechanochemical treatment on peakwidth was independent of the presence of quartz; the quartz acts as an additional grinding medium. The effectiveness of the mechanochemical treatment depends on the crystallinity of the kaolinite. Two processes are identified in the mechanochemical activation of the kaolinite: first the delamination of kaolinite appears to take place in the first hour of grinding and second a recombination process results in the reaggregation of the ground crystals. During this process proton hopping occurs and reaction to form water takes place. This water is then adsorbed and coordinated to surface-active sites created during mechanochemical treatment.

The effect of mechanochemical activation upon the intercalation of a high-defect kaolinite with formamide.

The effect of mechanochemical activation upon the intercalation of formamide into a high-defect kaolinite has been studied using a combination of X-ray diffraction, thermal analysis, and DRIFT spectroscopy. X-ray diffraction shows that the intensity of the d(001) spacing decreases with grinding time and that the intercalated high-defect kaolinite expands to 10.2 A. The intensity of the peak of the expanded phase of the formamide-intercalated kaolinite decreases with grinding time. Thermal analysis reveals that the evolution temperature of the adsorbed formamide and loss of the inserting molecule increases with increased grinding time. The temperature of the dehydroxylation of the formamide-intercalated high-defect kaolinite decreases from 495 to 470 degrees C with mechanochemical activation. Changes in the surface structure of the mechanochemically activated formamide-intercalated high-defect kaolinite were followed by DRIFT spectroscopy. Fundamentally the intensity of the high-defect kaolinite hydroxyl stretching bands decreases exponentially with grinding time and simultaneously the intensity of the bands attributed to the OH stretching vibrations of water increased. It is proposed that the mechanochemical activation of the high-defect kaolinite caused the conversion of the hydroxyls to water which coordinates the kaolinite surface. Significant changes in the infrared bands assigned to the hydroxyl deformation and amide stretching and bending modes were observed. The intensity decrease of these bands was exponentially related to the grinding time. The position of the amide C=O vibrational mode was found to be sensitive to grinding time. The effect of mechanochemical activation of the high-defect kaolinite reduces the capacity of the kaolinite to be intercalated with formamide.

A DRIFT spectroscopic study of potassium acetate intercalated mechanochemically activated kaolinite.

Kaolinite has been mechanochemically activated by dry grinding for periods of time up to 10 h. The kaolinite was then intercalated with potassium acetate and the changes in the structure followed by DRIFT spectroscopy. Intercalation of the kaolinite with potassium acetate is difficult and only the layers, which remain hydrogen bonded, are intercalated. The mechanochemical activation of the kaolinite may be followed by the loss of intensity of the hydroxyl-stretching vibrations. The intensity of the 3695 and 3619 cm(-1) bands reach a minimum after 10 h of grinding. The observation of a band at 3602 cm(-1) is indicative of the intercalation of the kaolinite with potassium acetate. The degree of intercalation decreases with mechanochemical treatment. The effect of exposure of the intercalated mechanochemically activated kaolinite to moist air results in de-intercalation. The effect of the mechanochemical treatment is loss of layer stacking, which prevents the intercalation of the kaolinite.