Effects of potassium oxalate on knoop hardness of etch-and-rinse adhesives.

The objective of this study was to determine whether the hardness of etch-and-rinse adhesives may be affected by the pretreatment of acid-etched dentin with potassium oxalate desensitizer. Unerupted human third molars were cut into crown segments by removing the occlusal enamel and roots. The pulp chamber of these crown segments was connected to a syringe barrel filled with phosphate-buffered saline so that the moisture of dentin was maintained during the bonding procedures. Three etch-and-rinse adhesives-two two-step systems (Adper Single Bond 2 [SB], One-Step [OS]) and one three-step system (Adper Scotchbond Multi-Purpose [MP])-were applied to acid-etched dentin that had been treated (experimental groups) or not (control groups) with potassium oxalate (BisBlock). The Knoop hardness (KHN) of adhesives was taken at different sites of the outer surface of the adhesive-bonded dentin. The KHN of the three tested adhesives applied to acid-etched dentin treated with potassium oxalate was significantly lower than that exhibited by the respective controls (not treated with oxalate; p<0.05). Regardless of the adhesive, the treatment with potassium oxalate reduced the adhesives' KHN (p<0.05), with the OS system exhibiting the lowest KHN compared with the MP and SB systems.

Effect of air-drying on the solvent evaporation, degree of conversion and water sorption/solubility of dental adhesive models.

This study evaluated protocols to eliminate acetone from dental adhesives and their effect on the kinetic of water sorption and percent of conversion of these adhesives. Experimental methacrylate-based adhesives with increasing hydrophilicity (R2, R3, R5) were used as reference materials. Primer-like solutions were prepared by addition of 50 wt% acetone. Acetone elimination was measured gravimetrically before and after: a spontaneous evaporation, an application of air-drying at room temperature or application of 40°C air-drying. Protocols were performed from 15 to 60 s. Specimens of adhesive/acetone mixtures were photo-activated and tested for degree of conversion, water sorption and solubility. Data were analyzed by ANOVA and Bonferroni's tests (α = 0.05). Complete acetone elimination was never achieved, but it was significantly greater after the 40°C air-drying application. Higher acetone elimination was observed for the least hydrophilic adhesive. Longer periods for acetone evaporation and heated air-stream can optimize polymerization and reduce the water sorption/solubility of adhesive system models.