Influence of Incorporating Zirconium- and Barium-based Radiopaque Filler Into Experimental and Commercial Infiltrants.

OBJECTIVES: To evaluate how adding different concentrations of particles (barium or zirconium oxide 25%/45% by weight) to a commercial infiltrant (Icon) and an experimental infiltrant influences cohesive strength (CS), degree of conversion (DC), water sorption (WS), solubility (SL), radiopacity, and penetration depth. METHODS AND MATERIALS: Microtensile CS (n=10) was evaluated using a universal testing machine. DC (n=5) was evaluated in a Fourier-transform infrared spectrometer. Polymerized samples were dissected, weighed, and stored to obtain the final mass for WS and SL tests (n=10). Radiopacity analysis (n=5) was performed using a digital radiography system. Penetration depth analysis (n=5) was performed by confocal laser scanning microscopy. Analyses were performed using the R program, with a significance level of 5%, except for the penetration depth analyses, which were evaluated only qualitatively. RESULTS: The groups with 45% zirconium showed greater CS values, regardless of the infiltrant. Among the groups with no particle addition, those of the experimental infiltrant presented higher DC than those of Icon. The experimental infiltrant presented lower WS than Icon. All groups had SL below the ISO recommended levels. Radiopacity higher than 2.24 mmAl (enamel radiopacity) was observed only in the groups with 45% zirconium. All the groups achieved similar penetration depth, but the groups containing experimental infiltrant appear to have had longer tag extensions. CONCLUSIONS: Addition of 45% of zirconium presented good results for CS and WS, as well as SL below the ISO recommended standard, adequate radiopacity, and penetration depth similar to the other groups.

Effect of Cigarette Smoke on Resin Composite Bond Strength to Enamel and Dentin Using Different Adhesive Systems.

OBJECTIVE: To evaluate the microshear bond strength of composite resin restorations in dental blocks with or without exposure to cigarette smoke. METHOD: Eighty bovine dental blocks were divided into eight groups (n=10) according to the type of adhesive (Scotchbond Multi-Purpose, 3M ESPE, St Paul, MN, USA [SBMP]; Single Bond 2, 3M ESPE [SB]; Clearfil SE Bond, Kuraray Medical Inc, Okayama, Japan [CSEB]; Single Bond Universal, 3M ESPE [SBU]) and exposure to smoke (no exposure; exposure for five days/20 cigarettes per day). The adhesive systems were applied to the tooth structure, and the blocks received a composite restoration made using a matrix of perforated pasta. Data were statistically analyzed using analysis of variance and Tukey test (α<0.05). RESULTS: For enamel, there was no difference between the presence or absence of cigarette smoke (p=0.1397); however, there were differences among the adhesive systems (p<0.001). CSEB showed higher values and did not differ from SBU, but both were statistically different from SB. The SBMP showed intermediate values, while SB demonstrated lower values. For dentin, specimens subjected to cigarette smoke presented bond strength values that were lower when compared with those not exposed to smoke (p<0.001). For the groups without exposure to cigarette smoke, CSEB showed higher values, differing from SBMP. SB and SBU showed intermediary values. For the groups with exposure to cigarette smoke, SBU showed values that were higher and statistically different from SB and CSEB, which presented lower values of bond strength. SBMP demonstrated an intermediate value of bond strength. CONCLUSION: The exposure of dentin to cigarette smoke influenced the bonding strength of adhesives, but no differences were noted in enamel.

Influence of an intermediary base on the microleakage of simulated class II composite resin restorations.

The aim of this in vitro study was to qualitatively and quantitatively evaluate the microleakage of Class II cavities restored with a methacrylate-based composite (Filtek Z250, 3M ESPE) or silorane-based composite (Filtek LS, 3M ESPE), varying the application of an intermediary base, using a low-viscosity composite resin (Filtek Z350 Flow, 3M ESPE) or resin-modified glass ionomer cement (RMGIC) (Vitrebond, 3M ESPE) and no intermediary base (control groups). Sixty cavities were prepared on the proximal surfaces of bovine teeth and were randomly divided according to the experimental groups (n=10). Following the restorative procedures and thermocycling, the samples were immersed in methylene blue for two hours. The qualitative evaluation was made using a stereomicroscope, whereby two observers analyzed the infiltration level of the dye within the tooth/filling. Microleakage scores among the groups were compared using the Kruskal-Wallis test followed by the Mann-Whitney test (p≤0.05). The samples were then ground and the powder was prepared for quantitative analysis in an absorbance spectrophotometer. The results were statistically analyzed by analysis of variance and the Tukey test (p≤0.05). Results from the quantitative analysis showed that LS presented higher values of microleakage than did Z250. There was a significant difference between both composites concerning the intermediary materials, with the lowest values obtained using RMGIC as an intermediary base. Results from the qualitative analysis showed that there were no statistically significant differences between composites; however, there were significant differences for both composites concerning the intermediary materials, with the lowest values obtained using RMGIC as an intermediary. It is possible to conclude that using RMGIC as an intermediary base provided lower microleakage, indicating better sealing of the tooth-restoration interface.

Effect of tooth bleaching on bond strength of enamel-dentin cavities restored with silorane- and dimethacrylate-based materials.

The aim of this study was to evaluate the influence of tooth bleaching on the push-out bond strength of a composite resin based on dimethacrylates and silorane to cavities that involve both enamel and dentin. A total of 80 bovine incisors were sectioned on the buccal surface to obtain specimens (10 × 10 mm) presenting enamel and dentin (1-mm thick each substrate). The specimens were randomly distributed into eight groups (n=10), according to the bleaching protocol (1--none; 2--10% carbamide peroxide [CP] for 21 days, six hours each day; 3--three applications of 35% hydrogen peroxide [HP] in 15-minute sessions, one session every seven days for three weeks; 4--10% CP for 18 days, six hours each day + three applications of 35% HP in 15-minute sessions, one session every seven days for three weeks) and the restorative system applied (Adper Single Bond 2 + Filtek Supreme; Filtek Silorane adhesive and composite resin). After treatment, cavities were made (1.2-mm diameter on dentin; 1.5-mm diameter on enamel) with a diamond bur. At 24 hours after restoration, a push-out bond strength test was performed at a crosshead speed of 0.5 mm/min. The bleaching treatments did not significantly affect the bond strengths of either restorative system to enamel-dentin. Regardless of the bleaching treatment, the dimethacrylate-based resin system exhibited significantly higher bond strengths to enamel-dentin than did the silorane-based system.

Effect of preheating resin composite and light-curing units on the microleakage of Class II restorations submitted to thermocycling.

This in vitro study evaluated microleakage in Class II cavities restored with dental composite and varying light-curing units and the temperature of the composite when subjected to a thermocycling test. Ninety cavities were prepared on the proximal surfaces of bovine teeth and randomly divided according to the light-curing mode (QTH-420 mW/cm2, LED 2nd generation-1100 mW/cm2, or LED 3rd generation-700 mW/cm2) and temperature of the resin composite (23°C, 54°C and 60°C). Following the restorative procedures and thermocycling, the samples were immersed in methylene blue for 12 hours. The samples were ground and the powder prepared for analysis in an absorbance spectrophotometer. All the results were statistically analyzed using the nonparametric tests of Kruskal-Wallis and Dunn (p ≤ 0.05). The results showed that there was no statistical difference between the light-curing modes at a temperature of 23°C. For 54°C, QTH showed a microleakage mean that was significantly lower than those of the LED groups, and for 60°C, QTH had a microleakage mean significantly lower than that of the LED 2nd generation group. There was no statistical difference between the temperatures of the resin composite when LEDs were used. For QTH, 54°C showed statistically lower microleakage than 23°C. The group preheated to 60°C showed no difference when compared to the group heated to 23°C. Preheating the resin composite (54°C and 60°C) did not improve the microleakage means when high-irradiance LED was used; however, it decreased the microleakage means when a QTH with low irradiance was used.

Effect of eugenol exposure time and post-removal delay on the bond strength of a self-etching adhesive to dentin.

OBJECTIVES: This study evaluated the effects of the exposure time of eugenol-based provisional restorative material and the time elapsed between the provisional material removal and the adhesive procedure on the bond strength of the composite to dentin. MATERIALS AND METHODS: Human third molars were sectioned into two halves that were enclosed in resin cylinders. The cavities were prepared over the buccal/lingual faces with diamond burs. Zinc oxide and eugenol (ZOE) provisional material was inserted into cavities and left for 24 hours, 7 days or 14 days. The cavities not restored with ZOE were used as controls. After ZOE removal or over fresh dentin (control), self-etching Adper SE Plus was applied immediately, after a 7- or 14-day delay. The cavity was restored with non-eugenol provisional material during this delay period. Cylinders of resin cement were built-up over the hybridized dentin. A shear load was applied to the cylinders at a crosshead speed of 0.5 mm/minute until failure. The data were statistically analyzed using two-way ANOVA and Tukey's tests (α=0.05). RESULTS: Using IRM as a provisional restoration for 24 hours followed by its removal and immediate adhesive application resulted in the lowest values of shear bond strength. There was no significant difference between the other experimental conditions. CONCLUSIONS: The use of IRM for 24 hours adversely affected the shear bond strength of a self-etching adhesive to dentin. The recovery of the proper bond strength occurred one week after IRM removal.

Effect of remaining dentine structure and thermal-mechanical aging on the fracture resistance of bovine roots with different post and core systems.

AIM: To evaluate the influence of remaining dentine thickness around post and core systems and the thermo-mechanical stresses on fracture resistance of bovine roots. METHODOLOGY: This study involved 288 bovine incisor roots with standardized dimensions. Roots were randomly distributed into 24 groups (n = 12) according to root conditions [intact, semi-weakened, or weakened] and post and core systems [custom cast core, composite resin core, prefabricated metallic post, or prefabricated carbon fibre post], submitted or not to thermomechanical aging [5000 thermal cycles and 100 000 mechanical cycles at a 135-degree angle to the long axis of the root]. Specimens were submitted to a tangential compressive load (135 degrees angle) at a crosshead speed of 0.5 mm min(-1) until failure. Fracture resistance data were analyzed using 3-way anova and Tukey test: alpha = 5%. RESULTS: Roots restored with composite resin cores demonstrated no resistance to mechanical aging. No statistically significant difference was observed between aged and nonaged specimens involving all post-systems. Roots restored with custom cast cores had the highest fracture strength, followed by prefabricated metallic posts and carbon fibre posts, regardless of root conditions and thermomechanical aging. The remaining dentine thickness affected significantly roots restored with custom cast cores; weakened roots had a lower fracture resistance. CONCLUSIONS: Although custom cast cores had a higher fracture resistance when compared to the other techniques, the results were highly dependent on remaining dentine thickness. Prefabricated posts performed in a similar manner in intact, semi-weakened and weakened roots reinforced with composite resin.

Effect of different filling materials in combination with intraradicular posts on the resistance to fracture of weakened roots.

The preservation and restoration of severely weakened pulpless teeth is a difficult and relatively unpredictable procedure. This study evaluated the resistance to fracture of experimentally weakened bovine roots internally reconstructed with different filling materials in combination with prefabricated post compared with restored roots that were relatively intact. The roots of 75 mandibular bovine incisors with similar bulks were selected. Of these, 60 were internally prepared to standardized dimensions, thereby simulating weakness. All roots were filled with different restorative materials. The specimens were submitted to the fracture resistance testing with the application of a tangential compressive loading at an angle of 135 degrees in relation to the long axes of the roots. Results indicated statistically significant differences in relation to the root conditions. Weakened roots were less resistant to fracture than were controls. The roots restored with the resin cement demonstrated the lowest fracture resistance values, but statistically significant differences were observed only when compared with those restored by the resin-modified glass-ionomer cement. Resin-modified glass-ionomer cement, polyacid-modified resin composite and resin composite behaved similarly without statistically significant differences among them. None of the materials evaluated were capable of achieving the fracture resistance recorded for unweakened controls.

Effect of different filling materials in combination with intraradicular posts on the resistance to fracture of weakened roots / Efeito dos diferentes materiais obturados em combinação com pinos intra-radiculares na resistência da fratura de raízes frágeis

The preservation and restoration of severely weakened pulpless teeth is a difficult and relatively unpredictable procedure. This study evaluated the resistance to fracture of experimentally weakened bovine roots internally reconstructed with different filling materials in combination with prefabricated post compared with restored roots that were relatively intact. The roots of 75 mandibular bovine incisors with similar bulks were selected. Of these, 60 were internally prepared to standardized dimensions, thereby simulating weakness. All roots were filled with different restorative materials. The specimens were submitted to the fracture resistance testing with the application of a tangential compressive loading at an angle of 135 in relation to the long axes of the roots. Results indicated statistically significant differences in relation to the root conditions. Weakened roots were less resistant to fracture than were controls. The roots restored with the resin cement demonstrated the lowest fracture resistance values, but statistically significant differences were observed only when compared with those restored by the resin-modified glass-ionomer cement. Resin-modified glass-ionomer cement, polyacid-modified resin composite and resin composite behaved similarly without statistically significant differences among them. None of the materials evaluated were capable of achieving the fracture resistance recorded for unweakened controls