PEDOT:PSS Conductivity Enhancement through Addition of the Surfactant Tween 80.

Replacement of indium tin oxide with the intrinsically conducting polymer poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) has been of significant interest in recent years as a result of lower processing and material costs. In addition, the inclusion of additives has been reported to further enhance the conductivity, rheology, and wettability of PEDOT:PSS. In this study, Tween 80 was shown to decrease the sheet resistance of PEDOT:PSS films from approximately 1000 to 76 Ω□-1 at a 2.67 wt% surfactant concentration. Through X-ray diffraction, Raman spectroscopy, and atomic force microscopy, it was shown that the surfactant caused phase separation and structural ordering of the PEDOT and PSS components, leading to this improvement in conductivity. Furthermore, Tween 80 altered the rheological properties and decreased the surface tension of PEDOT:PSS, making coating common commodity polymers, often used as flexible substrates, more viable.

On the Solubility and Stability of Polyvinylidene Fluoride.

This literature review covers the solubility and processability of fluoropolymer polyvinylidine fluoride (PVDF). Fluoropolymers consist of a carbon backbone chain with multiple connected C-F bonds; they are typically nonreactive and nontoxic and have good thermal stability. Their processing, recycling and reuse are rapidly becoming more important to the circular economy as fluoropolymers find widespread application in diverse sectors including construction, automotive engineering and electronics. The partially fluorinated polymer PVDF is in strong demand in all of these areas; in addition to its desirable inertness, which is typical of most fluoropolymers, it also has a high dielectric constant and can be ferroelectric in some of its crystal phases. However, processing and reusing PVDF is a challenging task, and this is partly due to its limited solubility. This review begins with a discussion on the useful properties and applications of PVDF, followed by a discussion on the known solvents and diluents of PVDF and how it can be formed into membranes. Finally, we explore the limitations of PVDF's chemical and thermal stability, with a discussion on conditions under which it can degrade. Our aim is to provide a condensed overview that will be of use to both chemists and engineers who need to work with PVDF.

Electroactive polymers for sensing.

Electromechanical coupling in electroactive polymers (EAPs) has been widely applied for actuation and is also being increasingly investigated for sensing chemical and mechanical stimuli. EAPs are a unique class of materials, with low-moduli high-strain capabilities and the ability to conform to surfaces of different shapes. These features make them attractive for applications such as wearable sensors and interfacing with soft tissues. Here, we review the major types of EAPs and their sensing mechanisms. These are divided into two classes depending on the main type of charge carrier: ionic EAPs (such as conducting polymers and ionic polymer-metal composites) and electronic EAPs (such as dielectric elastomers, liquid-crystal polymers and piezoelectric polymers). This review is intended to serve as an introduction to the mechanisms of these materials and as a first step in material selection for both researchers and designers of flexible/bendable devices, biocompatible sensors or even robotic tactile sensing units.

Anisotropic colloidal micromuscles from liquid crystal elastomers.

Monodomain liquid crystal elastomers (LCEs) are new materials uniquely suitable for artificial muscles, as they undergo large reversible uniaxial shape changes, with strains of 20-500% and stresses of 10-100 kPa, falling exactly into the dynamic range of a muscle. LCEs exhibit little to no fatigue over thousands of actuation cycles. Their practical use has been limited, however, owing to the difficulty of synthesizing components, achieving consistent alignment during cross-linking across the whole material and often a high nematic-isotropic phase transition temperature. The most widely studied method for LC alignment involves mechanical stretching of the material during one of two cross-linking steps, which makes fabrication difficult to control and lends itself mainly to samples that can be easily grasped (with sizes of the order of mm). In this article, we describe a method of adapting the LCE synthesis to microscale objects, achieving monodomain alignment with a single cross-linking step, and lowering the cycling temperature. LCE precursor droplets are embedded in and then stretched in a polymer matrix at high temperature. Confinement of the uniaxially stretched droplets maintains the alignment achieved during stretching and allows us to eliminate one of the cross-linking steps and the variability associated with it. Adding a comonomer during the polymerization leads to lowering of the nematic-to-isotropic transition temperature (58 °C), significantly expanding the range of potential applications for these micromuscles. We demonstrate reversible thermal switching of the micromuscles in line with the largest strain changes observed for side-chain LCEs and a differential scanning calorimetry characterization of the material phase transitions. The method demonstrates the parallel fabrication of many microscale actuators and is amenable to further scale-up and manufacturing.

Localised actuation in composites containing carbon nanotubes and liquid crystalline elastomers.

A liquid crystalline elastomer-carbon nanotube (LCE-CNT) composite displays a reversible shape change property in response to light. The development of some systems such as tactile devices requires localised actuation of this material. A method is reported that combines mechanical stretching and thermal crosslinking of an LCE-CNT for creating sufficiently well-aligned liquid crystal units to produce localised actuation. The method demonstrates that it is feasible to optically drive a LCE-CNT film within a localised area, since only the walls of the stretched parts of the film contain aligned LC domains.