Mechanical, bioactive, and long-lasting antibacterial properties of a Ti scaffold with gradient pores releasing iodine ions.

The ideal bone implant would effectively prevent aseptic as well as septic loosening by minimizing stress shielding, maximizing bone ingrowth, and preventing implant-associated infections. Here, a novel gradient-pore-size titanium scaffold was designed and manufactured to address these requirements. The scaffold features a larger pore size (900 µm) on the top surface, gradually decreasing to small sizes (600 µm to 300 µm) towards the center, creating a gradient structure. To enhance its functionality, the additively manufactured scaffolds were biofunctionalized using simple chemical and heat treatments so as to incorporate calcium and iodine ions throughout the surface. This unique combination of varying pore sizes with a biofunctional surface provides highly desirable mechanical properties, bioactivity, and notably, long-lasting antibacterial activity. The target mechanical aspects, including low elastic modulus, high compression, compression-shear, and fatigue strength, were effectively achieved. Furthermore, the biofunctional surface exhibits remarkable in vitro bioactivity and potent antibacterial activity, even under conditions specifically altered to be favorable for bacterial growth. More importantly, the integration of small pores alongside larger ones ensures a sustained high release of iodine, resulting in antimicrobial activity that persisted for over three months, with full eradication of the bacteria. Taken together, this gradient structure exhibits obvious superiority in combining most of the desired properties, making it an ideal candidate for orthopedic and dental implant applications.

Bioactivation Treatment with Mixed Acid and Heat on Titanium Implants Fabricated by Selective Laser Melting Enhances Preosteoblast Cell Differentiation.

Selective laser melting (SLM) is a promising technology capable of producing individual characteristics with a high degree of surface roughness for implants. These surfaces can be modified so as to increase their osseointegration, bone generation and biocompatibility, features which are critical to their clinical success. In this study, we evaluated the effects on preosteoblast proliferation and differentiation of titanium metal (Ti) with a high degree of roughness (Ra = 5.4266 ± 1.282 µm) prepared by SLM (SLM-Ti) that was also subjected to surface bioactive treatment by mixed acid and heat (MAH). The results showed that the MAH treatment further increased the surface roughness, wettability and apatite formation capacity of SLM-Ti, features which are useful for cell attachment and bone bonding. Quantitative measurement of osteogenic-related gene expression by RT-PCR indicated that the MC3T3-E1 cells on the SLM-Ti MAH surface presented a stronger tendency towards osteogenic differentiation at the genetic level through significantly increased expression of Alp, Ocn, Runx2 and Opn. We conclude that bio-activated SLM-Ti enhanced preosteoblast differentiation. These findings suggest that the mixed acid and heat treatment on SLM-Ti is promising method for preparing the next generation of orthopedic and dental implants because of its apatite formation and cell differentiation capability.

Osteoconductivity of bioactive Ti-6Al-4V implants with lattice-shaped interconnected large pores fabricated by electron beam melting.

Additive manufacturing has facilitated the fabrication of orthopedic metal implants with interconnected pores. Recent reports have indicated that a pore size of 600 µm is beneficial for material-induced osteogenesis. However, the complete removal of the metal powder from such small pores of implants is extremely difficult especially in electron beam melting (EBM). We therefore developed a new type of Ti-6Al-4V implant with lattice-shaped interconnected pores measuring 880-1400 µm, which allowed for the easy removal of metal powder. This implant was fabricated by EBM and treated with NaOH, CaCl2, heat, and water (ACaHW treatment) to render the metal surface bioactivity. In the present study, the mechanical and chemical property of the implants and the biocompatibility were evaluated. The SEM and micro-CT images demonstrated the 3D interconnectivity of the porous structures. The average porosity of the porous titanium implant was 57.5%. The implant showed maximum compressive load of 78.9 MPa and Young's modulus of 3.57 GPa which matches that of human cortical bone. ACaHW treatment of the porous Ti-6Al-4V implants induced apatite formation in simulated body fluid in vitro. The ACaHW-treated porous implants harvested from rabbit femoral bone showed direct bonding of bone to the metal surface without interposition of fibrous tissue. The porous ACaHW-treated implant had a higher affinity to the bone than the untreated one. The mechanical strength of implant fixation assessed using the push-out test was significantly higher in the ACaHW-treated implant than in untreated one. FE-SEM analysis and EDX mapping after push-out test of solid implants showed a lot of bone tissue patches on the surface of the ACaHW-treated implant. These results suggest that the new ACaHW-treated Ti-6Al-4V implant with lattice-shaped interconnected pores is a superior alternative to conventional materials for medical application.

Stand-Alone Anterior Cervical Discectomy and Fusion Using an Additive Manufactured Individualized Bioactive Porous Titanium Implant without Bone Graft: Results of a Prospective Clinical Trial.

The purpose of this study was to introduce our patient-specific bioactive porous titanium implant manufactured using selective laser melting (SLM) and to establish the efficacy and safety of the implant for stand-alone anterior cervical discectomy and fusion (ACDF) based on a prospective clinical trial. We designed a customized ACDF implant using patient-specific data and manufactured the implant using SLM. We produced a bioactive surface through a specific chemical and thermal treatment. Using this implant, we surgically treated four patients with cervical degenerative disc disease and evaluated the clinical and radiological results. We achieved successful bony union in all but one patient without autologous bone grafting within 1 year. We observed no implant subsidence during the follow-up period, and all clinical parameters improved significantly after surgery, with no reported implant-related adverse effects. Our customized bioactive porous titanium implant is a safe and promising implant for stand-alone ACDF.

Mechanical, Histological, and Scanning Electron Microscopy Study of the Effect of Mixed-Acid and Heat Treatment on Additive-Manufactured Titanium Plates on Bonding to the Bone Surface.

The additive manufacturing (AM) technique has attracted attention as one of the fully customizable medical material technologies. In addition, the development of new surface treatments has been investigated to improve the osteogenic ability of the AM titanium (Ti) plate. The purpose of this study was to evaluate the osteogenic activity of the AM Ti with mixed-acid and heat (MAH) treatment. Fully customized AM Ti plates were created with a curvature suitable for rat calvarial bone, and they were examined in a group implanted with the MAH-treated Ti in comparison with the untreated (UN) group. The AM Ti plates were fixed to the surface of rat calvarial bone, followed by extraction of the calvarial bone 1, 4, 8, and 12 weeks after implantation. The bonding between the bone and Ti was evaluated mechanically. In addition, AM Ti plates removed from the bone were examined histologically by electron microscopy and Villanueva-Goldner stain. The mechanical evaluation showed significantly stronger bone-bonding in the MAH group than in the UN group. In addition, active bone formation was seen histologically in the MAH group. Therefore, these findings indicate that MAH resulted in rapid and strong bonding between cortical bone and Ti.

Bioactive pedicle screws prepared by chemical and heat treatments improved biocompatibility and bone-bonding ability in canine lumbar spines.

BACKGROUND: Titanium (Ti)-6Al-4V alloy, which is widely used in spinal instrumentation with a pedicle screw (PS) system. However, significant clinical problems, including loosening and back-out of PSs, persist. During the last decade, a novel technology that produces bioactive Ti from chemical and heat treatments has been reported that induces the spontaneous formation of a hydroxyapatite (HA) layer on the surface of Ti materials. The purpose of this study was to study the effect of bioactivation of Ti-6Al-4V PSs on the ability of HA formation in vitro and its biocompatibility and bone-bonding ability in vivo. METHODS: Ti-6V-4Al alloy PSs were prepared and bioactivated by NaOH-CaCl2-heat-water treatments. The HA-forming ability of bioactive PSs in simulated body fluid (SBF) was evaluated by field emission scanning electron microscopy (FE-SEM) and energy dispersive X-ray analysis (EDX). Six 11-month-old female beagle dogs were used for the in vivo study. Bioactive and control (without bioactivation) PSs were left and right randomly placed from L1 to L6. One and three months after surgery, lumbar spines were removed for biomechanical and histological analyses. RESULTS: In vitro: The surface analysis of bioactive PSs by FE-SEM and EDX showed substantial HA deposits over the entire surface. In vivo: The mean extraction torque was significantly higher for bioactive PSs compared to controls PSs (P<0.01); there was no significant difference in pull-out strength between control and bioactive PSs. Histologically, the contact area between bone tissue and screw surface showed no significant trend to be greater in bioactive PSs compared to control PSs (P = 0.06). CONCLUSIONS: Bioactive PSs prepared by chemical and heat treatments formed layers of HA on the surface of screws in vitro that improved biocompatibility and bonding ability with bone in vivo. Bioactive PSs may reduce screw loosening to overcome the obstacles confronted in spinal instrumentation surgery.

Osteogenic capacity of mixed-acid and heat-treated titanium mesh prepared by a selective laser melting technique.

The practical use of additive manufacturing to create artificial bone as a material for repairing complex bone defects is currently attracting attention. In this study, we compared the osteogenic capacity of materials composited by the method developed by Kokubo et al. of treating 3D-printed titanium (Ti) mesh with a mixture of H2SO4 and HCl and heating (mixed-acid and heat treatment) with that of materials subjected to conventional chemical treatment. Ti plates treated with this method have been found to promote highly active bone formation on their surface when inserted into rabbit tibial bone defects. No previous study has compared this method with other surface treatment methods. In this study, we used histological and other observations to compare the bone formation process in bone defects when Ti meshes prepared by the selective laser melting technique (SLM) and treated either with mixed acids and heat or with conventional chemical Ti surface treatments were implanted in a rat calvarial bone defect model. We found that both micro-computed tomography and observations of undecalcified ground sections showed that the best bone formation was observed in rats implanted with mesh treated with mixed acids and heat. Our results suggest that mixed-acid and heat-treated Ti mesh prepared by SLM may have a high osteogenic capacity in bone defects.

Strontium and magnesium ions released from bioactive titanium metal promote early bone bonding in a rabbit implant model.

We have previously developed the "alkali and heat treatment" method to confer bioactivity (bone-bonding ability) to titanium metal (Ti). As strontium (Sr) and magnesium (Mg) ions reportedly promote osteoblastic cell proliferation and differentiation and accelerate bone formation, we improved this method to induce the release of Sr (Sr-Ti) or Mg (Mg-Ti) ions from Ti in a previous study. Here, we evaluated the bioactivity of these novel surface treatments, Sr-Ti and Mg-Ti. In vitro evaluation of cell viability, expression of integrin ß1, ß catenin, and cyclin D1, osteogenic gene expression, alkaline phosphatase activity, and extracellular mineralization using MC3T3-E1 cells revealed that Sr-Ti and Mg-Ti enhanced proliferation and osteogenic differentiation. In rabbit in vivo studies, Sr-Ti and Mg-Ti also provided greater biomechanical strength and bone-implant contact than the positive control Ti (Ca-Ti), especially at the early stage (4-8weeks), and maintained these properties for a longer period (16-24weeks). Advantages of the improved method include process simplicity, applicability for any implant shape, and lack of adverse effects on implant composition and structure. Therefore, our treatment is promising for clinical applications to achieve early bone bonding. STATEMENT OF SIGNIFICANCE: Implantation into osteoporotic bone constitutes a challenging problem because of early migration or loosening of the implant, which is primarily due to insufficient initial fixation in porotic bone. Therefore, it is desirable to provide implants with a capacity for early bone bonding. We have achieved conferring early bone bonding ability to titanium metal by releasing strontium ions or magnesium ions. Our treatment is promising for clinical applications to achieve early bone bonding of orthopedic or dental Ti-based implants.

In vivo experimental study of anterior cervical fusion using bioactive polyetheretherketone in a canine model.

BACKGROUND: Polyetheretherketone (PEEK) is a widely accepted biomaterial, especially in the field of spinal surgery. However, PEEK is not able to directly integrate with bone tissue, due to its bioinertness. To overcome this drawback, various studies have described surface coating approaches aimed at increasing the bioactivity of PEEK surfaces. Among those, it has been shown that the recently developed sol-gel TiO2 coating could provide PEEK with the ability to bond with bone tissue in vivo without the use of a bone graft. OBJECTIVE: This in vivo experimental study using a canine model determined the efficacy of bioactive TiO2-coated PEEK for anterior cervical fusion. METHODS: Sol-gel-derived TiO2 coating, which involves sandblasting and acid treatment, was used to give PEEK bone-bonding ability. The cervical interbody spacer, which was designed to fit the disc space of a beagle, was fabricated using bioactive TiO2-coated PEEK. Both uncoated PEEK (control) and TiO2-coated PEEK spacers were implanted into the cervical intervertebral space of beagles (n = 5 for each type). After the 3-month survival period, interbody fusion success was evaluated based on µ-CT imaging, histology, and manual palpation analyses. RESULTS: Manual palpation analyses indicated a 60% (3/5 cases) fusion (no gap between bone and implants) rate for the TiO2-coated PEEK group, indicating clear advantage over the 0% (0/5 cases) fusion rate for the uncoated PEEK group. The bony fusion rate of the TiO2-coated PEEK group was 40% according to µCT imaging; however, it was 0% of for the uncoated PEEK group. Additionally, the bone-implant contact ratio calculated using histomorphometry demonstrated a better contact ratio for the TiO2-coated PEEK group than for the uncoated PEEK group (mean, 32.6% vs 3.2%; p = 0.017). CONCLUSIONS: The TiO2-coated bioactive PEEK implant demonstrated better fusion rates and bone-bonding ability than did the uncoated PEEK implant in the canine anterior cervical fusion model. Bioactive PEEK, which has bone-bonding ability, could contribute to further improvements in clinical outcomes for spinal interbody fusion.

Two-in-One Biointerfaces-Antimicrobial and Bioactive Nanoporous Gallium Titanate Layers for Titanium Implants.

The inhibitory effect of gallium (Ga) ions on bone resorption and their superior microbial activity are attractive and sought-after features for the vast majority of implantable devices, in particular for implants used for hard tissue. In our work, for the first time, Ga ions were successfully incorporated into the surface of titanium metal (Ti) by simple and cost-effective chemical and heat treatments. Ti samples were initially treated in NaOH solution to produce a nanostructured sodium hydrogen titanate layer approximately 1 µm thick. When the metal was subsequently soaked in a mixed solution of CaCl2 and GaCl3, its Na ions were replaced with Ca and Ga ions in a Ga/Ca ratio range of 0.09 to 2.33. 8.0% of the Ga ions were incorporated into the metal surface when the metal was soaked in a single solution of GaCl3 after the NaOH treatment. The metal was then heat-treated at 600 °C to form Ga-containing calcium titanate (Ga-CT) or gallium titanate (GT), anatase and rutile on its surface. The metal with Ga-CT formed bone-like apatite in a simulated body fluid (SBF) within 3 days, but released only 0.23 ppm of the Ga ions in a phosphate-buffered saline (PBS) over a period of 14 days. In contrast, Ti with GT did not form apatite in SBF, but released 2.96 ppm of Ga ions in PBS. Subsequent soaking in hot water at 80 °C dramatically enhanced apatite formation of the metal by increasing the release of Ga ions up to 3.75 ppm. The treated metal exhibited very high antibacterial activity against multidrug resistant Acinetobacter baumannii (MRAB12). Unlike other antimicrobial coating on titanium implants, Ga-CT and GT interfaces were shown to have a unique combination of antimicrobial and bioactive properties. Such dual activity is essential for the next generation of orthopaedic and dental implants. The goal of combining both functions without inducing cytotoxicity is a major advance and has far reaching translational perspectives. This unique dual-function biointerfaces will inhibit bone resorption and show antimicrobial activity through the release of Ga ions, while tight bonding to the bone will be achieved through the apatite formed on the surface.

Fabrication of dense α-alumina layer on Ti-6Al-4V alloy hybrid for bearing surfaces of artificial hip joint.

Recent advances in hip replacements are focused towards producing reliable bearing surfaces to enhance their longevity. In this perspective, progressive attempts have been made to improve the wear resistance of polyethylene to eliminate osteolysis and mechanical reliability of brittle alumina ceramics, but in vain. It is proposed that both high wear resistance and mechanical reliability can be retained if a thin layer of dense alumina is formed onto high toughness Ti-6Al-4V alloy. For this purpose, we devised a unique methodology in which a layer of Al metal was deposited onto the Ti alloy substrate by cold spraying (CS), followed by a heat treatment to form Al3Ti reaction layer at their interface to improve adhesion and subsequent micro-arc oxidation (MAO) treatment to transform Al to alumina layer. An optimal MAO treatment of cold sprayed Al formed an adherent and dense α-alumina layer with high Vickers hardness matching with that of sintered alumina used as a femoral head. Structure-phase-property relationships in dense α-alumina layer have been revealed and discussed in the light of our research findings. The designed alumina/Ti alloy hybrid might be a potential candidate for reliable bearing surfaces of artificial hip joint.

Bioactivity of sol-gel-derived TiO2 coating on polyetheretherketone: In vitro and in vivo studies.

A polyetheretherketone (PEEK) surface was modified using a sol-gel-derived TiO2 coating in order to confer bone-bonding ability. To enhance the bonding strength of the coating layer, pretreatment with either O2 plasma or sandblasting was performed prior to sol-gel coating. Additionally, post-treatment with acid was carried out to confer apatite (calcium phosphate)-forming ability to the surface. Biomechanical and histological analyses performed using an in vivo rabbit tibia model showed that PEEK surfaces modified with sol-gel-derived TiO2 and acid post-treatment had better bone-bonding properties than uncoated PEEK surfaces. These modified surfaces also performed well in terms of their in vitro cell responses due to their modified surface chemistries and topographies. Although O2 plasma or sandblasting treatment were, for the most part, equivocal in terms of performance, we conclude that sol-gel-derived TiO2 coating followed by acid post-treatment significantly improves the bone bonding ability of PEEK surfaces, thus rendering them optimal for their use in surgical implants. STATEMENT OF SIGNIFICANCE: The role of polyetheretherketone (PEEK) as an alternative biomaterial to conventional metallic implant materials has become increasingly important. However, its low bone bonding ability is yet to be resolved. This in vivo and in vitro investigation on the functionalization of PEEK surfaces highlights the utility of this material in clinical interventions that require implants, and may extend range of applications of PEEK.

Bioactive treatment promotes osteoblast differentiation on titanium materials fabricated by selective laser melting technology.

Selective laser melting (SLM) technology is useful for the fabrication of porous titanium implants with complex shapes and structures. The materials fabricated by SLM characteristically have a very rough surface (average surface roughness, Ra=24.58 µm). In this study, we evaluated morphologically and biochemically the specific effects of this very rough surface and the additional effects of a bioactive treatment on osteoblast proliferation and differentiation. Flat-rolled titanium materials (Ra=1.02 µm) were used as the controls. On the treated materials fabricated by SLM, we observed enhanced osteoblast differentiation compared with the flat-rolled materials and the untreated materials fabricated by SLM. No significant differences were observed between the flat-rolled materials and the untreated materials fabricated by SLM in their effects on osteoblast differentiation. We concluded that the very rough surface fabricated by SLM had to undergo a bioactive treatment to obtain a positive effect on osteoblast differentiation.

Additive-manufactured patient-specific titanium templates for thoracic pedicle screw placement: novel design with reduced contact area.

PURPOSE: Image-based navigational patient-specific templates (PSTs) for pedicle screw (PS) placement have been described. With recent advances in three-dimensional computer-aided designs and additive manufacturing technology, various PST designs have been reported, although the template designs were not optimized. We have developed a novel PST design that reduces the contact area without sacrificing stability. It avoids susceptibility to intervening soft tissue, template geometric inaccuracy, and difficulty during template fitting. METHODS: Fourteen candidate locations on the posterior aspect of the vertebra were evaluated. Among them, locations that had high reproducibility on computed tomography (CT) images and facilitated accurate PS placement were selected for the final PST design. An additive manufacturing machine (EOSINT M270) fabricated the PSTs using commercially pure titanium powder. For the clinical study, 36 scoliosis patients and 4 patients with ossification of the posterior longitudinal ligament (OPLL) were treated with thoracic PSs using our newly developed PSTs. We intraoperatively and postoperatively evaluated the accuracy of the PS hole created by the PST. RESULTS: Based on the segmentation reproducibility and stability analyses, we selected seven small, round contact points for our PST: bilateral superior and inferior points on the transverse process base, bilateral inferior points on the laminar, and a superior point on the spinous process. Clinically, the success rates of PS placement using this PST design were 98.6 % (414/420) for scoliosis patients and 100 % (46/46) for OPLL patients. CONCLUSION: This study provides a useful design concept for the development and introduction of patient-specific navigational templates for placing PSs.

Effect of pore size on bone ingrowth into porous titanium implants fabricated by additive manufacturing: An in vivo experiment.

Selective laser melting (SLM) is an additive manufacturing technique with the ability to produce metallic scaffolds with accurately controlled pore size, porosity, and interconnectivity for orthopedic applications. However, the optimal pore structure of porous titanium manufactured by SLM remains unclear. In this study, we evaluated the effect of pore size with constant porosity on in vivo bone ingrowth in rabbits into porous titanium implants manufactured by SLM. Three porous titanium implants (with an intended porosity of 65% and pore sizes of 300, 600, and 900µm, designated the P300, P600, and P900 implants, respectively) were manufactured by SLM. A diamond lattice was adapted as the basic structure. Their porous structures were evaluated and verified using microfocus X-ray computed tomography. Their bone-implant fixation ability was evaluated by their implantation as porous-surfaced titanium plates into the cortical bone of the rabbit tibia. Bone ingrowth was evaluated by their implantation as cylindrical porous titanium implants into the cancellous bone of the rabbit femur for 2, 4, and 8weeks. The average pore sizes of the P300, P600, and P900 implants were 309, 632, and 956µm, respectively. The P600 implant demonstrated a significantly higher fixation ability at 2weeks than the other implants. After 4weeks, all models had sufficiently high fixation ability in a detaching test. Bone ingrowth into the P300 implant was lower than into the other implants at 4weeks. Because of its appropriate mechanical strength, high fixation ability, and rapid bone ingrowth, our results indicate that the pore structure of the P600 implant is a suitable porous structure for orthopedic implants manufactured by SLM.

In vivo study of the early bone-bonding ability of Ti meshes formed with calcium titanate via chemical treatments.

Alkali and heat (AH) treatment forming sodium titanate has been shown to connect bioinert Ti metal and bone tissue. Artificial joints treated with this method have achieved extensive clinical application. Recently a new chemical treatment of Alkali-Calcium-Heat-Water (ACaHW) treatment forming calcium titanate was proposed. Notably, the apatite-forming ability of this treatment is greater than that of AH treatment, as verified in vitro. However, the early bone-bonding abilities of the two treatments have not been compared in vivo. To simulate clinical application, we treated a commercially pure Ti (Cp-Ti) mesh implant with AH or ACaHW. Then, using mechanical and histological methods, we compared the bone-bonding abilities of the two treatments early during the implantation process (2-4 weeks); untreated Cp-Ti mesh was used as a control. Because the mesh structure might influence bone-bonding ability, we compared these bonding abilities with values obtained at 4 and 8 weeks using a Cp-Ti implant with a plate structure. In the mesh group, histological comparisons at 2 and 3 weeks indicated that ACaHW treatment resulted in a bone-bonding ability similar to that of AH treatment; ACaHW exhibited a greater bonding ability than AH at 4 weeks. However, in tests of the plate group at later time points, such differences were not apparent. The results obtained here indicate that during the early stage of embedment, ACaHW treatment of Cp-Ti mesh implants yields a higher bone-bonding ability than AH treatment, thus providing a positive reference for future clinical applications.

Custom-made titanium devices as membranes for bone augmentation in implant treatment: Modeling accuracy of titanium products constructed with selective laser melting.

OBJECTIVE: The purpose of this study was to verify the modeling accuracy of various products, and to produce custom-made devices for bone augmentation in individual patients requiring implantation. MATERIALS AND METHODS: Two-(2D) and three-dimensional (3D) specimens and custom-made devices that were designed as membranes for guided bone regeneration (GBR) were produced using a computer-aided design (CAD) and rapid prototyping (RP) method. The CAD design was produced using a 3D printing machine and selective laser melting (SLM) with pure titanium (Ti) powder. The modeling accuracy was evaluated with regard to: the dimensional accuracy of the 2D and 3D specimens; the accuracy of pore structure of the 2D specimens; the accuracy of porosity of the 3D specimens; and the error between CAD design and the scanned real product by overlapped images. RESULTS: The accuracy of the 2D and 3D specimens indicated precise results in various parameters, which were tolerant in ISO 2768-1. The error of overlapped images between the CAD and scanned data indicated that accuracy was sufficient for GBR. In integrating area of all devices, the maximum and average error were 292 and 139 µm, respectively. CONCLUSIONS: High modeling accuracy can be achieved in various products using the CAD/RP-SLM method. These results suggest the possibility of clinical applications.

Novel artificial hip joint: A layer of alumina on Ti-6Al-4V alloy formed by micro-arc oxidation.

In many hip replacement surgeries, monolithic alumina is used as a femoral head due to its high wear resistance. However, it is liable to fracture under load bearing operations in artificial joints. We propose a promising way to overcome this limitation by forming a dense alumina layer onto a relatively tough substrate such as Ti-6Al-4V alloy to obtain high wear resistance on a material that can sustain relatively high toughness. For this purpose, Al metal powders were deposited onto Ti-6Al-4V alloy by cold spraying in N2 atmosphere. Interfacial adhesion between Al and the Ti alloy was improved by the formation of a reaction layer of Al3Ti between them by heating at 640 °C for 1h in air. Subsequently, micro-arc oxidation treatment was performed to oxidize Al. The oxidized layer was composed of an outer porous layer of γ-alumina and inner-most dense layer of α-alumina. The α-alumina layer was almost fully densified and exhibited high Vickers hardness almost equal to that of alumina ceramics used as the femoral head. Thus, the newly developed dense alumina/Ti alloy can be potentially used to produce the reliable bearing surfaces of artificial hip joint.

Apatite-forming PEEK with TiO2 surface layer coating.

Polyetheretherketone (PEEK) is widely used in orthopedic implants, such as spinal fusion devices, because of its moderate elastic modulus, as well as relatively high mechanical strength. However, it does not bond to living bone, and hence it needs autograft to be fixed to the bone. In this study, we attempted to add bone-bonding properties to PEEK by coating with TiO2 synthesized by the sol-gel process. When a TiO2 sol solution consisting of titanium isopropoxide, water, ethanol, and nitric acid was deposited on a PEEK substrate without any pretreatment, the formed TiO2 gel layer was easily peeled off after subsequent treatments. However, when the same solution was deposited on PEEK that was preliminarily subjected to UV or O2 plasma treatment, the deposited TiO2 gel layer strongly adhered to the substrate even after subsequent treatments. The strong adhesion was attributed to the interaction among the C-O, C=O, and O-C=O groups on the PEEK owing to the UV or O2 plasma treatment and the Ti-O bond of the TiO2 gel. Apatite did not form on the as-formed TiO2 gel layer in a simulated body fluid (SBF) even within 3 days; however, apatite formed after soaking in 0.1 M HCl solution at 80 °C for 24 h. This apatite formation was attributed to positive surface charge of the TiO2 gel layer induced by the acid treatment. The PEEK with the TiO2 gel layer coating formed by the proposed process is expected to bond to living bone, because a positively charged titanium oxide which facilitates the formation of apatite in SBF within a short period is known to bond to living bone.

Treatment of a unicameral bone cyst in a dog using a customized titanium device.

A 4-year-old Shih-Tzu, referred for an enlarged left carpus, was diagnosed with a unicameral bone cyst. A customized titanium device was inserted into cystic lesion and fixed by titanium screws. Sufficient strength of the affected bone with the device inserted to maintain limb function was established after resection of contents of cystic lesion. There was no deterioration of the lesion of bone cyst, and acceptable function of the affected limb with no clinical signs of lameness was maintained during 36 months follow-up. The results of this study demonstrated that bone cyst curettage and use of a customized titanium device could provide an effective alternative treatment of huge lesion of unicameral bone cysts with the intent of preventing pathologic fractures.