Synthesis of telechelic olefin polymers via catalyzed chain growth on multinuclear alkylene zinc compounds.

Multinuclear alkylene zinc (MAZ) compounds of the type EtZn-(R″-Zn)n-Et (R″ = ethyl and propyl branched alkylene groups) were synthesized by a simple one-step procedure in nonpolar hydrocarbon solvents from α,ω-dienes (e.g., 1,7-octadiene or 1,9-decadiene) and diethylzinc using a bis(salicylaldiminato)Zr(IV) complex, [(2-methylcyclohexyl)N═CH(2-O-C6H3-3,5-di-tert-butyl)]2ZrMe2, as a catalyst. The MAZ serves as a divalent reversible chain-transfer agent for olefin polymerization, resulting in telechelic Zn-metalated polyolefins whose molecular weights are controllable over a wide range. The Zn-terminated telechelics serve as a polymer precursor for further reactions and can be converted into a variety of telechelic functionalized polyolefins in high yield.

Oxo- and imidovanadium complexes incorporating methylene- and dimethyleneoxa-bridged calix[3]- and -[4]arenes: synthesis, structures and ethylene polymerisation catalysis.

Reaction of [V(X)(OR)3] (X=O, Np-tolyl; R=Et, nPr or tBu) with p-tert-butylhexahomotrioxacalix[3]areneH3, LH3, affords the air-stable complexes [{V(X)L}n] (X=O, n=1 (1); X=Np-tolyl, n=2 (2)). Alternatively, 1 is readily available either from interaction of [V(mes)3THF] with LH3, and subsequent oxidation with O2 or upon reaction of LLi3 with [VOCl3]. Reaction of [V(Np-tolyl)(OtBu)3] with 1,3-dimethylether-p-tert-butylcalix[4]areneH2, Cax(OMe)2(OH)2, afforded [{VO(OtBu)}2(mu-O)Cax(OMe)2(O)2].2 MeCN (42 MeCN), in which two vanadium atoms are bound to just one calix[4]arene ligand; the n-propoxide analogue of 4, namely [{VO(OnPr)}2(mu-O)Cax(OMe)2(O)2].1.5 MeCN (51.5 MeCN), has also been isolated from a similar reaction using [V(O)(OnPr)3]. Reaction of [VOCl3], LiOtBu, (Me3Si)2O and Cax(OMe)2(OH)2 gave [{VO(OtBu)Cax(OMe)2(O)2}2Li4O2].8 MeCN (68 MeCN), in which an Li4O4 cube (two of the oxygen atoms are derived from the calixarene ligands) is sandwiched between two Cax(OMe)2(O)2. The reaction between [V(Np-tolyl)(OtBu)3] and Cax(OMe)2(OH)2, afforded [V(Np-tolyl)(OtBu)2Cax(OMe)2(O)(OH)]5 MeCN (75 MeCN), in which two tert-butoxide groups remain bound to the tetrahedral vanadium atom, which itself is bound to the calix[4]arene through only one phenolic oxygen atom. Reaction of p-tert-butylcalix[4]areneH4, Cax(OH)4 and [V(Np-tolyl)(OnPr)3] led to loss of the imido group and formation of the dimeric complex [{VCax(O)4(NCMe)}2].6 MeCN (86 MeCN). Monomeric vanadyl oxo- and imidocalix[4]arene complexes [V(X)Cax(O)3(OMe)(NCMe)] (X=O (11), Np-tolyl (12)) were obtained by the reaction of the methylether-p-tert-butylcalix[4]areneH3, Cax(OMe)(OH)3, and [V(X)(OR)3] (R=Et or nPr). Vanadyl calix[4]arene fragments can be linked by the reaction of 2,6-bis(bromomethyl)pyridine with Cax(OH)4 and subsequent treatment with [VOCl3] to afford the complex [{VOCax(O)4}2(mu-2,6-(CH2)2C5H3N)].4 MeCN (134 MeCN). The compounds 1-13 have been structurally characterised by single-crystal X-ray diffraction. Upon activation with methylaluminoxane, these complexes displayed poor activities, however, the use of dimethylaluminium chloride and the reactivator ethyltrichloroacetate generates highly active, thermally stable catalysts for the conversion of ethylene to, at 25 degrees C, ultra-high-molecular-weight (>5, 500,000), linear polyethylene, whilst at higher temperature (80 degrees C), the molecular weight of the polyethylene drops to about 450,000. Using 1 and 2 at 25 degrees C for ethylene/propylene co-polymerisation (50:50 feed) leads to ultra-high-molecular-weight (>2,900,000) polymer with about 14.5 mol% propylene incorporation. The catalytic systems employing the methyleneoxa-bridged complexes 1 and 2 are an order of magnitude more active than the bimetallic complexes 5 and 13, which, in turn, are an order of magnitude more active than pro-catalysts 8, 11 and 12. These differences in activity are discussed in terms of the structures of each class of complex.

Vanadyl C and N-capped tris(phenolate) complexes: influence of pro-catalyst geometry on catalytic activity.

Vanadyl complexes of C or N-capped tripodal ligands, possessing distorted tetrahedral geometry at vanadium, serve as extremely active, thermally robust pro-catalysts for ethylene homo- and ethylene/propylene copolymerisation, whereas pseudo-octahedral pro-catalysts produce far lower activities.