Retention Forces for Drops on Microstructured Superhydrophobic Surfaces.

Accurate models of retention forces between drops and superhydrophobic (SH) surfaces are required to predict drop dynamics on the surface. This retention force is, in turn, useful in modeling heat transfer rates for dropwise condensation on a SH surface. Drop contact angle distribution and base area on SH surfaces are essential factors for predicting retention forces. The present work measures the contact angle distribution and base area shapes of various drop sizes over a wide range of solid fraction for inclined microstructured SH surfaces at the point of drop departure. Base area shape was found to be well approximated using two ellipses with different aspect ratios, and the contact angle distribution was found to be best fit by a sigmoid function. At an incline near the roll-off angle, drop base area for surfaces with solid fraction close to 1 and close to 0 were found to be nearly circular, whereas the base area of drops on surfaces with an intermediate solid fraction deviated from circular behavior. In this work, maximum advancing and minimum receding contact angles were found as a function of solid fraction and used to calculate retention forces. Contact angle distribution and base area shapes are then used to calculate retention forces between drops and SH surfaces. These calculations are compared with the component of measured drop weight acting parallel to the plane on a tilted surface for validation. Previous retention force studies that investigate base area shape and contact angle distribution for smooth surfaces are not applicable for microstructured SH surfaces. The work shows that using a sigmoid contact angle distribution and modified base area shape yields retention forces that are on average 50% better than previously reported methods. Retention forces for smooth and SH surfaces calculated in this study were used to suggest retention force factor values for varying solid fraction surfaces.

Surfactant addition and alternating current electrophoretic oscillation during size fractionation of nanoparticles in channels with two or three different height segments.

An array of parallel planar nanochannels containing two or three segments with varying inner heights was fabricated and used for size fractionation of inorganic and biological nanoparticles. A liquid suspension of the particles was simply drawn through the nanochannels via capillary action. Using fluorescently labeled 30 nm polyacrylonitrile beads, different trapping behaviors were compared using nanochannels with 200-45 nm and 208-54-30 nm height segments. Addition of sodium dodecyl sulfate (SDS) surfactant to the liquid suspension and application of an AC electric field were shown to aid in the prevention of channel clogging. After initial particle trapping at the segment interfaces, significant particle redistribution occurred when applying a sinusoidal 8V peak-to-peak oscillating voltage with a frequency of 150 Hz and DC offset of 4V. Using the 208-54-30 nm channels, 30 nm hepatitis B virus (HBV) capsids were divided into three fractions. When the AC electric field was applied to this trapped sample, all of the virus particles passed through the interfaces and accumulated at the channel ends.