Highly Magnetizable Crosslinked Chloromethylated Polystyrene-Based Nanocomposite Beads for Selective Molecular Separation of 4-Aminobenzoic Acid.

In this work, we describe the preparation and characterization of highly magnetizable chloromethylated polystyrene-based nanocomposite beads. For synthesis optimization, acid-resistant core-shelled maghemite (γ-Fe2O3) nanoparticles are coated with sodium oleate and directly incorporated into the organic medium during a suspension polymerization process. A crosslinking agent, ethylene glycol dimethacrylate, is used for copolymerization with 4-vinylbenzyl chloride to increase the resistance of the microbeads against leaching. X-ray diffraction, inductively coupled plasma atomic emission spectroscopy, thermogravimetric analysis, scanning electron microscopy, transmission electron microscopy, and optical microscopy are used for bead characterization. The beads form a magnetic composite consisting of ∼500 nm-sized crosslinked polymeric microspheres, embedding ∼8 nm γ-Fe2O3 nanoparticles. This nanocomposite shows large room temperature magnetization (∼24 emu/g) due to the high content of maghemite (∼45 wt %) and resistance against leaching even in acidic media. Moreover, the presence of superficial chloromethyl groups is probed by Fourier transform infrared and X-ray photoelectron spectroscopy. The nanocomposite beads displaying chloromethyl groups can be used to selectively remove aminated compounds that are adsorbed on the beads, as is shown here for the molecular separation of 4-aminobenzoic acid from a mixture with benzoic acid. The high magnetization of the composite beads makes them suitable for in situ molecular separations in environmental and biological applications.

Magnetic ionic liquids produced by the dispersion of magnetic nanoparticles in 1-n-butyl-3-methylimidazolium bis(trifluoromethanesulfonyl)imide (BMI.NTf2).

̀This paper reports on the advancement of magnetic ionic liquids (MILs) as stable dispersions of surface-modified γ-Fe(2)O(3), Fe(3)O(4), and CoFe(2)O(4) magnetic nanoparticles (MNPs) in a hydrophobic ionic liquid, 1-n-butyl 3-methylimidazolium bis(trifluoromethanesulfonyl)imide (BMI.NTf(2)). The MNPs were obtained via coprecipitation and were characterized using powder X-ray diffraction, transmission electron microscopy, Raman spectroscopy and Fourier transform near-infrared (FT-NIR) spectroscopy, and magnetic measurements. The surface-modified MNPs (SM-MNPs) were obtained via the silanization of the MNPs with the aid of 1-butyl-3-[3-(trimethoxysilyl)propyl]imidazolium chloride (BMSPI.Cl). The SM-MNPs were characterized by Raman spectroscopy and Fourier transform infrared-attenuated total reflectance (FTIR-ATR) spectroscopy and by magnetic measurements. The FTIR-ATR spectra of the SM-MNPs exhibited characteristic absorptions of the imidazolium and those of the Fe-O-Si-C moieties, confirming the presence of BMSPI.Cl on the MNP surface. Thermogravimetric analysis (TGA) showed that the SM-MNPs were modified by at least one BMSPI.Cl monolayer. The MILs were characterized using Raman spectroscopy, differential scanning calorimetry (DSC), and magnetic measurements. The Raman and DSC results indicated an interaction between the SM-MNPs and the IL. This interaction promotes the formation of a supramolecular structure close to the MNP surface that mimics the IL structure and is responsible for the stability of the MIL. Magnetic measurements of the MILs indicated no hysteresis. Superparamagnetic behavior and a saturation magnetization of ~22 emu/g could be inferred from the magnetic measurements of a sample containing 50% w/w γ-Fe(2)O(3) SM-MNP/BMI.NTf(2).