Effect of processing of rapeseed under defined conditions in a pilot plant on chemical composition and standardized ileal amino acid digestibility in rapeseed meal for pigs.

Five rapeseed meals (RSM) were produced from a single batch of rapeseed in a large-scale pilot plant under standardized conditions. The objective was to evaluate the effect of residence time in the desolventizer/toaster (DT) on chemical composition and standardized ileal digestibility (SID) of AA in RSM. Four RSM, with 48, 64, 76, and 93 min residence time and using unsaturated steam in the DT, referred to as RSM48, RSM64, RSM76, and RSM93, respectively, and 1 low-glucosinolate RSM, which was subjected to sequential treatment with unsaturated steam, saturated steam, and dry heat in the DT, referred to as low-GSL RSM, were assayed. Six barrows (average initial BW = 22 ± 1 kg) were surgically fitted with a T-cannula at the distal ileum. Pigs were allotted to a 5 × 6 row × column design with 5 diets and 5 periods. The 5 RSM were included in a cornstarch-casein-based basal diet. In addition, basal ileal endogenous losses and SID of AA originating from casein were determined at the conclusion of the experiment in 2 additional periods by means of the regression method and using 3 graded levels of casein. The SID of AA in the 5 RSM was determined in difference to SID of AA originating from casein. The glucosinolates (GSL) were efficiently reduced, whereas NDF, ADF, ADL, and NDIN contents increased and reactive Lys (rLys) and Lys:CP ratio decreased as the residence time in the DT was increased from 48 to 93 min. The SID of most AA in RSM linearly decreased (P < 0.05) as the residence time in the DT increased from 48 to 93 min. Moreover, there was a linear decrease (P < 0.05) in SID of AA with increasing NDF, ADF, ADL, and NDIN contents in these RSM, whereas SID of AA linearly decreased (P < 0.05) with decreasing levels of GSL and rLys and a decreasing Lys:CP ratio. The decrease (P < 0.05) in SID of AA amounted from 3 up to 6 (percentage units) for most AA, except for SID of Cys and Lys, which decreased by 10 and 11%-units (P < 0.05), respectively, as the residence time in the DT was increased from 48 to 93 min. The SID in low-GSL RSM was for CP and most AA similar to RSM93 but lower ( < 0.05) compared to RSM48. It can be concluded that time and energy-intensive heat treatment results in lower contents of SID AA in RSM together with a reduction in GSL levels. The feed industry would most likely benefit from a rapid and accurate prediction of SID of AA, for example, based on content of NDIN, GSL, rLys or on Lys:CP ratio, in different batches of RSM used for feed manufacturing.

Effect of feeding level on ileal and total tract digestibility of nutrients and energy from soybean meal-based diets for piglets.

A total of 36 piglets with an initial body weight (BW) of 5.6 ± 0.7 kg, fitted with simple T-cannulas at the distal ileum, were used to evaluate the effect of three graded feeding levels (50, 75 or 100 g/kg BW(0.75) day) on apparent ileal digestibility (AID) and total tract digestibility (ATTD) of dry matter (DM), nitrogen (N) and energy, and on ATTD of organic matter (OM), ether extracts (EE), neutral detergent fibre (NDF), acid detergent fibre (ADF) and digestible (DE), metabolisable (ME) and net energy (NE) content in soybean meal (SBM)-casein-cornstarch-based diets. The AID of DM, N and energy and ATTD of NDF, ADF and EE in the diets were not affected (p > 0.05) by the feed intake (FI) level. There was a small decrease in ATTD of DM, N (CP), OM, ash and energy, and in DE, ME and NE content in the diets (p < 0.05) with increasing FI level. The net disappearance in the large intestine (in % of ileal recovery) decreased for DM, N and energy (p < 0.05) with increasing FI level. The design of the study allowed for estimating ileal endogenous loss of N and total tract endogenous loss of ash, N and EE, for estimating corresponding true ileal and total tract digestibility values, and for estimating urinary endogenous N loss. High variability in estimates of ileal endogenous N loss and total tract endogenous losses of N, EE and ash reflects great variation in individual endogenous losses between animals. Estimation of true total tract digestibility of N, EE and ash by regression analysis was affected by their decrease in ATTD with increasing FI level, as estimates for true digestibility were lower compared to their apparent values. The present results suggest that FI level can affect both apparent and true total tract nutrient digestibility in piglets.

Effect of particle size and heat treatment of soybean meal on standardized ileal digestibility of amino acids in growing pigs.

A study with growing barrows was conducted to evaluate of variations in particle size and degree of heat treatment during processing on standardized ileal digestibility (SID) of AA in soybean (Glycine max) meal (SBM). A commercial SBM batch was visually identified as being overtoasted due to its brownish color and was separated into small and large particles using a 1-mm sieve. In addition, 3 SBM were produced from 1 batch of soybean and exposed to different processing conditions (temperature and direct steam contact) referred to as mild (105°C; 34 min), medium (115°C; 45 min), and strong (139°C; 7 min). In total, 5 SBM-corn (Zea mays) starch-based diets were formulated to contain SBM as the sole protein source. This experiment was conducted according to a 6 × 6 Latin square design using 6 barrows (23 kg initial BW) fitted with a T-cannula at the distal ileum. With increasing particle size, SID of His and some dispensable AA increased (P < 0.05). Lower SID values in small compared to large SBM particles indicate more pronounced heat damage possibly due to increased surface area. The SID of CP and AA was lowest in the mild, intermediate in the strong, and highest in the medium toasted SBM (P < 0.001). These differences in SID are reflected in varying contents of trypsin inhibitors, Lys, reactive Lys, and NDF. In conclusion, both differences in particles size and variations in thermal processing conditions of SBM may affect SID of CP and AA.

High-voltage electron microscope high-temperature in situ straining experiments to study dislocation dynamics in intermetallics and quasicrystals.

The dynamic behaviour of dislocations in several intermetallic alloys, studied by in situ straining experiments in a high-voltage electron microscope, is compared at room temperature and at high temperatures. In contrast to room temperature, the dislocations move viscously at high temperatures, which is explained by diffusion processes in the dislocation cores. In quasicrystals, the viscous dislocation motion can be interpreted by models on the cluster scale.

High-Temperature In Situ Straining Experiments in the High-Voltage Electron Microscope.

: Design rules are described here for high-temperature straining stages for transmission electron microscopy. Temperatures above 1000 degreesC can be attained by electron bombardment of the specimen grips. Thermal equilibrium can be reached in a short time by carrying off the heat by water cooling. Some applications of this stage are described. Ferroelastic deformation was observed at 1150 degreesC in t' and partially stabilized zirconia, which changes the microstructure for successive dislocation plasticity. In the oxide-dispersion-strengthened alloy INCOLOY MA 956, dislocations are impeded by oxide particles and move smoothly between the particles. At high temperatures, both the resting and traveling times control the average dislocation velocity. In MoSi2 single crystals of a soft orientation, dislocations with 1/2<111> Burgers vectors are created in localized sources and move on {110} planes in a viscous manner. The dislocations in Al-Pd-Mn single quasicrystals are oriented in preferred crystallographic directions and move in a viscous way as well. On the basis of in situ observations, conclusions are drawn for interpreting macroscopic deformation behavior at high temperatures.

Quantitative tensile-tilting stages for the high voltage electron microscope.

This paper describes a soft and a hard tensile stage for the high voltage electron microscope. Both stages can be combined with a top entry double tilting stage. The devices are driven by thermal expansion elements operating against water cooled parts. The drive mechanism shows smooth action with a relatively low response time and good long-time stability. The stages are equipped with strain gauge bridges for force and elongation measurements. The soft stage has a maximum load of 13 g, and a hard one reaches 1.5 kg.