RESUMO
Three-dimensional printing technology is constantly developing and has a wide range of applications; one application is electrical insulation, where the standard technology uses polymer-based filaments. Thermosetting materials (epoxy resins, liquid silicone rubbers) are broadly used as electrical insulation in high-voltage products. In power transformers, however, the main solid insulation is based on cellulosic materials (pressboard, crepe paper, wood laminates). There are a vast variety of transformer insulation components that are produced using the wet pulp molding process. This is a labor-intensive, multi-stage process that requires long drying times. In this paper, a new material, microcellulose-doped polymer, and manufacturing concept for transformer insulation components are described. Our research focuses on bio-based polymeric materials with 3D printability functionalities. A number of material formulations were tested and benchmark products were printed. Extensive electrical measurements were performed to compare transformer components manufactured using the traditional process and 3D printed samples. The results are promising but indicate that further research is still required to improve printing quality.
RESUMO
The increasing environmental awareness is driving towards novel sustainable high-performance materials applicable for future manufacturing technologies like additive manufacturing (AM). Cellulose is abundantly available renewable and sustainable raw material. This work focused on studying the properties of thermoplastic cellulose-based composites and their properties using injection molding and 3D printing of granules. The aim was to maximize the cellulose content in composites. Different compounds were prepared using cellulose acetate propionate (CAP) and commercial cellulose acetate propionate with plasticizer (CP) as polymer matrices, microcellulose (mc) and novel cellulose-ester additives; cellulose octanoate (C8) and cellulose palmitate (C16). The performance of compounds was compared to a commercial poly(lactic acid)-based cellulose fiber containing composite. As a result, CP-based compounds had tensile and Charpy impact strength properties comparable to commercial reference, but lower modulus. CP-compounds showed glass transition temperature (Tg) over 58% and heat distortion temperature (HDT) 12% higher compared to reference. CAP with C16 had HDT 82.1 °C. All the compounds were 3D printable using granular printing, but CAP compounds had challenges with printed layer adhesion. This study shows the potential to tailor thermoplastic cellulose-based composite materials, although more research is needed before obtaining all-cellulose 3D printable composite material with high-performance.
RESUMO
We describe herein a nanocellulose-alginate hydrogel suitable for 3D printing. The composition of the hydrogel was optimized based on material characterization methods and 3D printing experiments, and its behavior during the printing process was studied using computational fluid dynamics simulations. The hydrogel was biofunctionalized by the covalent coupling of an enhanced avidin protein to the cellulose nanofibrils. Ionic cross-linking of the hydrogel using calcium ions improved the performance of the material. The resulting hydrogel is suitable for 3D printing, its mechanical properties indicate good tissue compatibility, and the hydrogel absorbs water in moist conditions, suggesting potential in applications such as wound dressings. The biofunctionalization potential was shown by attaching a biotinylated fluorescent protein and a biotinylated fluorescent small molecule via avidin and monitoring the material using confocal microscopy. The 3D-printable bioactivated nanocellulose-alginate hydrogel offers a platform for the development of biomedical devices, wearable sensors, and drug-releasing materials.