High-Selective CO2 Capture in Amine-Decorated Al-MOFs.

Amine-functionalized metal-organic framework (MOF) material is a promising CO2 captor in the post-combustion capture process owing to its large CO2 working capacity as well as high CO2 selectivity and easy regeneration. In this study, an ethylenediamine (ED)-decorated Al-based MOFs (named ED@MOF-520) with a high specific area and permanent porosity are prepared and evaluated to study the adsorption and separation of CO2 from N2. The results show that ED@MOF-520 adsorbent displays a superior CO2 capture performance with a CO2/N2 separation factor of 50 at 273 K, 185% times increase in the CO2/N2 separation efficiency in comparison with blank MOF-520. Furthermore, ED@MOF-520 exhibits a moderate-strength interaction with 29 kJ mol-1 adsorption heat for CO2 uptake, which not only meets the requirement of CO2 adsorption but also has good cycle stability. This work provides a promising adsorbent with a high CO2/N2 separation factor to deal with carbon peak and carbon neutrality.

Tailoring Amine-Functionalized Ti-MOFs via a Mixed Ligands Strategy for High-Efficiency CO2 Capture.

Amine-functionalized metal-organic frameworks (MOFs) are a promising strategy for the high-efficiency capture and separation of CO2. In this work, by tuning the ratio of 1,3,5-benzenetricarboxylic acid (H3BTC) to 5-aminoisophthalic acid (5-NH2-H2IPA), we designed and synthesized a series of amine-functionalized highly stable Ti-based MOFs (named MIP-207-NH2-n, in which n represents 15%, 25%, 50%, 60%, and 100%). The structural analysis shows that the original framework of MIP-207 in the MIP-207-NH2-n (n = 15%, 25%, and 50%) MOFs remains intact when the mole ratio of ligand H3BTC to 5-NH2-H2IPA is less than 1 to 1 in the resulting MOFs. By the introduction of amino groups, MIP-207-NH2-25% demonstrates outstanding CO2 capture performance up to 3.96 and 2.91 mmol g-1, 20.7% and 43.3% higher than those of unmodified MIP-207 at 0 and 25 °C, respectively. Furthermore, the breakthrough experiment indicates that the dynamic CO2 adsorption capacity and CO2/N2 separation factors of MIP-207-NH2-25% are increased by about 25% and 15%, respectively. This work provides an additional strategy to construct amine-functionalized MOFs with the maintenance of the original MOF structure and high performance of CO2 capture and separation.