Bismuth-oxide nanoparticles: study in a beam and as deposited.

Bi2O3 is a promising material for solid-oxide fuel cells (SOFC) due to the high ionic conductivity of some phases. The largest value is reached for its δ-phase, but it is normally stable at temperatures too high for SOFC operation, while nanostructured oxide is believed to have more suitable stabilization temperature. However, to manufacture such a material with a controlled chemical composition is a challenging task. In this work, we investigated the fabrication of nanostructured Bi2O3 films formed by deposition of free Bi-oxide nanoparticles created in situ. The particle-production method was based on reactive sputtering and vapour aggregation. Depending on the fabrication conditions, the nanoparticles contained either a combination of Bi-metal and Bi-oxide, or only Bi-oxide. Prior to deposition, the free particles were probed in the beam - by synchrotron-based photoelectron spectroscopy (PES), which allowed assessing their composition "on the-fly". The nanoparticle films obtained after deposition were studied by PES, scanning electron microscopy, transmission electron microscopy, and electron diffraction. The films' chemical composition, grain dimensions, and crystal structure were probed. Our analysis suggests that our method produced Bi-oxide films in more than one polymorph of Bi2O3.

Tin-oxide nanoparticles deposited from a beam: what happens to the composition?

The debate around the oxidation states occurring in laboratory-prepared tin-oxide samples has been for a long time an obstacle for an unambiguous assignment of characterization studies performed on such samples. In particular the changes in the Sn core-level energies caused by oxidation - i.e. the chemical shifts - as measured by photoelectron spectroscopy (PES) have been under discussion. The assignment problem is especially pronounced for nanoscale structures, which are important for photovoltaics, electronics, catalysis, and gas sensing. The reasons for the difficulties lie both in the natural properties of tin oxides, which can have substantial deficiencies of oxygen and tin in the lattice, and in the shortcomings of the fabrication and PES-characterization procedures themselves. Our recent PES study on tin-oxide nanoparticles fabricated by vapour-aggregation gave a chemical shift two times larger than earlier reported for Sn(iv) oxide for the Sn 4d level. The implemented fabrication technique forms an in-vacuum beam of particles whose composition can be both controlled and characterized by PES. In the present work SnO and SnO2 nanoparticles fabricated this way were deposited from the beam and probed by PES directly, as well as after exposure to air. The deposited nanoparticle films were also imaged by TEM (Transmission Electron Microscopy). The effects of the deposition process and exposure to air on the chemical composition were studied. The PES study of deposited SnO2 nanoparticles in the Sn 4d and Sn 3d core-level regions revealed the same core level shift as for unsupported nanoparticles, indicating that the chemical composition is preserved in the deposition process. The TEM study demonstrated a crystalline structure of separate SnO2 particles with lattice constants close to the macroscopic Sn(iv)-oxide. The PES study on the particles exposed to air showed changes in the composition. For the film of initially SnO particles a higher intermediate oxide was created. For the SnO2 nanoparticle film a lower, but strong, intermediate oxide was observed, likely at the surface.

Metal-passivated PbS nanoparticles: fabrication and characterization.

Organic-shell-free PbS nanoparticles have been produced in the size range relevant for quantum-dot solar cells (QDSCs) by a vapor aggregation method involving magnetron reactive sputtering. This method creates a beam of free 5-10 nm particles in a vacuum. The dimensions of the particles were estimated after their deposition on a substrate by imaging them using ex situ SEM and HRTEM electron microscopy. The particle structure and chemical composition could be deduced "on the fly", prior to deposition, using X-ray photoelectron spectroscopy (XPS) with tunable synchrotron radiation. Our XPS results suggest that under certain conditions it is possible to fabricate particles with a semiconductor core and 1 to 2 monolayer shells of metallic lead. For this case the absolute energy of the highest occupied molecular orbital (HOMO) in PbS has been determined to be (5.0 ± 0.5) eV below the vacuum level. For such particles deposited on a substrate HRTEM has confirmed the XPS-based conclusions on the crystalline PbS structure of the semiconductor core. Absorption spectroscopy on the deposited film has given a value of ∼1 eV for the lowest exciton. Together with the valence XPS results this has allowed us to reconstruct the energy level scheme of the particles. The results obtained are discussed in the context of the properties of PbS QDSCs.

Photon energy dependent valence band response of metallic nanoparticles.

We show that the valence band response to photon impact in metallic nanoparticles is highly energy dependent. This is seen as drastic variations of cross sections in valence photoionization of free and initially charge-neutral nanosized metal clusters. The effect is demonstrated in a combined experimental and theoretical study of Rb clusters. The experimental findings are interpreted theoretically using a jellium model and superatom description. The variations are attributed to the changing overlap with the photon energy between the wave functions of diffuse delocalized valence electrons and continuum electrons producing a series of minima in the cross section.