Micropatterned Silica Films with Nanohydroxyapatite for Y-TZP Implants.

This investigation aimed at developing micropatterned silica thin films (MSTFs) containing nanohydroxyapatite (nano-HA) microaggregates that were not completely covered by silica so that they could directly interact with the surrounding cells. The objectives were 1) to evaluate the effect of the presence of 2 films (MSTF with or without nano-HA addition) on the characteristic strength (σ0) and Weibull modulus ( m) of a yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) and 2) to evaluate the effect of these 2 films, as applied onto the Y-TZP surface, on the morphology, orientation, and proliferation of MG63 cells. Sol-gel process and soft lithography were used to apply the MSTF onto the Y-TZP specimens. Three experimental groups were produced: Y-TZP, Y-TZP + MSTF, and Y-TZP + MSTF + sprayed nano-HA. All surfaces were characterized by scanning electron microscopy and energy-dispersive X-ray spectroscopy and tested for 4-point flexural strength ( n = 30) in water at 37 °C. Weibull analysis was used to determine m and σ0 (maximum likelihood method). In vitro biological behavior was performed with human osteoblast-like cells (MG63). Y-TZP was successfully coated with MSFT and MSFT + nano-HA. Scanning electron microscopy micrographs indicated that the microaggregates of nano-HA were not entirely covered by the silica. There was no statistically significant difference among the experimental groups for σ0 and m. In the groups containing the films, the cells were elongated and aligned along the lines. The MSFT + nano-HA group showed significantly higher cell metabolic activity than that obtained for the Y-TZP group at day 7. This investigation was successful in producing an MSTF containing nano-HA microaggregates that remained exposed to the environment. The developed films did not jeopardize the structural reliability of a commercial Y-TZP, as confirmed by the Weibull statistics. The MG63 cells seeded over the films became elongated and aligned along the films' micropatterned lines. Y-TZP specimens coated with MSTF and nano-HA showed a higher cell metabolic activity and proliferation after 7 d of culture when compared with uncoated Y-TZP.

Association of carotid intima-media thickness and cardiovascular risk factors in women pre- and post-bariatric surgery.

BACKGROUND: Obesity is associated with cardiovascular risk factors (CVRFs), such as hypertension, hypertriglyceridemia, and low levels of high-density cholesterol (HDL-C). In obese patients with a body mass index (BMI) of >or=40 kg/m2 or 35-40 kg/m2 associated with CVRFs, weight loss may be achieved more effectively by bariatric surgery on reducing several CVRFs. Carotid intima-media thickness (C-IMT) is an indicator of early atherosclerosis, and may be correlated with CVRFs. Our objective was to correlate C-IMT with CVRFs before (baseline data) and after surgery, and to observe whether weight loss is followed by a regression of C-IMT. METHODS: Eighteen women who had undergone bariatric surgery participated in this study. Assessments were carried out on the baseline date, and 3, 6, and 12 months after surgery. Some of the CVRFs analyzed were: total cholesterol (TC) levels, HDL-C, triglycerides to HDL-C ratio (TG/HDL-C) and fasting plasma glucose. C-IMT was measured by B-mode ultrasound. RESULTS: A positive correlation was found between C-IMT and age and triglyceride level (p=0.002 and p=0.02, respectively). Six months after surgery, we found a significant reduction in C-IMT (p<0.05), which was significantly correlated with TG level and systolic pressure (p<0.05). CONCLUSION: The weight loss achieved with bariatric surgery resulted in regression of C-IMT. This regression could be observed 6 months following surgery, with an additional benefit at 12 months. Also, this finding was correlated with a reduction in triglyceride levels and systolic blood pressure.