Evaluation of the effects of decellularized extracellular matrix nanoparticles incorporation on the polyhydroxybutyrate/nano chitosan electrospun scaffold for cartilage tissue engineering.

Recent research focuses on fabricating scaffolds imitating the extracellular matrix (ECM) in texture, composition, and functionality. Moreover, specific nano-bio-particles can enhance cell differentiation. Decellularized ECM nanoparticles possess all of the mentioned properties. In this research, cartilage ECM, extracted from the cow's femur condyle, was decellularized, and ECM nanoparticles were synthesized. Finally, nanocomposite electrospun fibers containing polyhydroxybutyrate (PHB), chitosan (Cs) nanoparticles, and ECM nanoparticles were fabricated and characterized. TEM and DLS results revealed ECM nanoparticle sizes of 17.51 and 21.6 nm, respectively. Optimal performance was observed in the scaffold with 0.75 wt% ECM nanoparticles (PHB-Cs/0.75E). By adding 0.75 wt% ECM, the ultimate tensile strength and elongation at break increased by about 29 % and 21 %, respectively, while the water contact angle and crystallinity decreased by about 36° and 2 %, respectively. Uneven and rougher surfaces of the PHB-Cs/0.75E were determined by FESEM and AFM images, respectively. TEM images verified the uniform dispersion of nanoparticles within the fibers. After 70 days of degradation in PBS, the PHB-Cs/0.75E and PHB-Cs scaffolds demonstrated insignificant weight loss differences. Eventually, enhanced viability, attachment, and proliferation of the human costal chondrocytes on the PHB-Cs/0.75E scaffold, concluded from MTT, SEM, and DAPI staining, confirmed its potential for cartilage tissue engineering.

Evaluation of the effects of chitosan nanoparticles on polyhydroxy butyrate electrospun scaffolds for cartilage tissue engineering applications.

In this study, we synthesized and incorporated chitosan nanoparticles (Cs) into polyhydroxy butyrate (PHB) electrospun scaffolds for cartilage tissue engineering. The Cs nanoparticles were synthesized via an ionic gel interaction between Cs powder and tripolyphosphate (TPP). The mechanical properties, hydrophilicity, and fiber diameter of the PHB scaffolds with varying concentrations of Cs nanoparticles (1-5 wt%) were evaluated. The results of these evaluations showed that the scaffold containing 1 wt% Cs nanoparticles (P1Cs) was the optimum scaffold, with increased ultimate strength from 2.6 to 5.2 MPa and elongation at break from 5.31 % to 12.6 %. Crystallinity, degradation, and cell compatibility were also evaluated. The addition of Cs nanoparticles decreased crystallinity and accelerated hydrolytic degradation. MTT assay results showed that the proliferation of chondrocytes on the scaffold containing 1 wt% Cs nanoparticles were significantly higher than that on pure PHB after 7 days of cultivation. These findings suggest that the electrospun P1Cs scaffold has promising potential as a substrate for cartilage tissue engineering applications. This combination offers a promising approach for the fabrication of biomimetic scaffolds with enhanced mechanical properties, hydrophilicity, and cell compatibility for tissue engineering applications.