In Vitro Effect of the Length of Relocated Cervical Margin with Casting Post and Core, Prefabricated Fiber Post, and Polyethylene Fiber with a Composite Core on Fracture Resistance and Marginal Integrity.

Objective: This study aimed to assess the effect of length of the relocated cervical margin with casting post and core (CP), prefabricated fiber post and composite core (PFP), and polyethylene fiber-reinforced composite (PEFRC) on fracture resistance and marginal integrity. Materials and Methods: In this in vitro study, 70 sound human maxillary premolars were divided into seven groups according to the type of post and core system and length of the relocated cervical margin (n = 10): control (no preparation), PFP-3, PEFRC-3, CP-3 with 3 mm of cervical margin relocation (CMR), PFP-6, PEFRC-6, and CP-6 (with 6 mm of CMR). The samples were restored with zirconia crowns (except the control group). Epoxy resin replicas were fabricated before and after thermomechanical loading. Marginal integrity was assessed at the luting cement-core, core-tooth, and luting cement-enamel interfaces under a scanning electron microscope (SEM) (×200). Fracture resistance and failure mode were subsequently assessed. Data were analyzed by independent t-test, paired t-test, ANOVA, Tukey-Games Howell, Mann-Whitney, Kruskal-Wallis, Wilcoxon, Mann-Whitney with Bonferroni correction, and Fisher-Freeman-Halton tests (α = 0.05). Results: The marginal integrity of the groups with 3 mm of CMR followed the following order: PEFRC > PFP > CP at all interfaces (P < 0.05). In 6-mm CMR groups, this order was CP < PFP = PEFRC at the luting cement-core and (CP < PEFRC) = PFP at the core-tooth interface. No significant difference was found in fracture resistance when comparing the 3-mm CMR groups with each other (P > 0.05). PFP-6 showed higher FR than CP-6 (P < 0.001). PEFRC-6 had no significant difference with PFP-6 and CP-6 (P > 0.05). In each post and core system, 3-mm CMR groups showed higher marginal integrity and fracture resistance (P < 0.05). Conclusion: Increasing the length of the relocated cervical margin decreased the marginal integrity and fracture resistance of all three systems of CP, PFP, and PEFRC.

Fracture resistance and failure mode of endodontically treated premolars reconstructed by different preparation approaches: Cervical margin relocation and crown lengthening with complete and partial ferrule with three different post and core systems.

PURPOSE: To assess the fracture resistance and failure mode of endodontically treated premolars reconstructed by different preparation approaches: cervical margin relocation (CMR) and crown lengthening (CL) with complete ferrule (CLF) and partial ferrule (CLPF) with three different post and core systems. MATERIALS AND METHODS: In this in vitro study, 100 maxillary premolars were assigned to the following 10 groups according to their preparation approach and type of post and core system (n = 10): (I) control (intact teeth), (II) prefabricated fiber post (PFP) and composite core with CMR (PFP-CMR), (III) polyethylene fiber-reinforced composite (PEFRC) with CMR (PEFRC-CMR), (IV) casting post (CP) and core with CMR (CP-CMR), (V) PFP-CLPF, (VI) PEFRC-CLPF, (VII) CP-CLPF, (VIII) PFP-CLF, (IX) PEFRC-CLF, and (X) CP-CLF. After thermomechanical loading, the fracture resistance and failure mode were assessed. Data were analyzed statistically (α = 0.05). RESULTS: In all post and core systems, the CLPF approach had lower fracture resistance than CMR (p < 0.05); CLF showed higher fracture resistance than CLPF only in the PFP system (p = 0.038). In PEFRC and CP systems, the difference between CLF and CLPF was not significant (p > 0.05). No significant difference was found in fracture resistance of different post and core systems with the same preparation approach (p > 0.05). CLPF showed the highest frequency of favorable, and CLF showed the highest frequency of unfavorable fractures. CONCLUSION: CLPF yielded lower fracture resistance than CMR. The difference in fracture resistance was not significant between CLF and CMR but the frequency of unfavorable fractures was higher in CLF than in other groups.