RESUMO
Imogolite nanotubes (INTs) form transparent aqueous liquid-crystalline solutions, with strong birefringence and X-ray scattering power. They provide an ideal model system for studying the assembly of one-dimensional nanomaterials into fibres, as well as offering interesting properties in their own right. Here, in situ polarised optical microscopy is used to study the wet spinning of pure INTs into fibres, illustrating the influence of process variables during extrusion, coagulation, washing and drying on both structure and mechanical properties. Tapered spinnerets were shown to be significantly more effective than thin cylindrical channels for forming homogeneous fibres; a result related to simple capillary rheology by fitting a shear thinning flow model. The washing step has a strong influence of structure and properties, combining the removal of residual counter-ions and structural relaxation to produce a less aligned, denser and more networked structure; the timescales and scaling behavior of the processes are compared quantitatively. Both strength and stiffness are higher for INT fibres with a higher packing fraction and lower degree of alignment, indicating the importance of forming a rigid jammed network to transfer stress through these porous, rigid rod assemblies. The electrostatically-stabilised, rigid rod INT solutions were successfully cross-linked using multivalent anions, providing robust gels, potentially useful in other contexts.
RESUMO
Imogolite nanotubes (INTs) display a range of useful properties and provide an ideal material system to study the assembly of nanomaterials into macroscopic fibers. A method of wet spinning pure, binder-free imogolite fibers has been developed using double-walled germanium imogolite nanotubes. The nanotube aspect ratio can be controlled during the initial synthesis and is critical to the spinning process. Fibers made from short nanotubes (<100 nm) have very low gel strengths, while dopes with longer nanotubes (500-1000 nm) are readily spinnable. The tensile behavior of the resulting imogolite nanotube fibers is strongly influenced by relative humidity (RH), with a modulus of 30 GPa at 10% RH compared to 2.8 GPa at 85% RH, as well as a change in failure mode. This result highlights the importance of inter-nanotube interactions in such assemblies and provides a useful strategy for further exploration. Interestingly, in the absence of a matrix phase, a degree of misorientation appears to improve load transfer between the individual INTs within the porous fiber, likely due to an increase in the number of interparticle contacts. Imogolite nanotubes are an appealing analogue to other nanotube fiber systems, and it is hoped that learnings from this system can also be used to improve carbon nanotube fibers.