Pulsed laser deposited CoFe2O4 thin films as supercapacitor electrodes.

The influence of the substrate temperature on pulsed laser deposited (PLD) CoFe2O4 thin films for supercapacitor electrodes was thoroughly investigated. X-ray diffractometry and Raman spectroscopic analyses confirmed the formation of CoFe2O4 phase for films deposited at a substrate temperature of 450 °C. Topography and surface smoothness was measured using atomic force microscopy. We observed that the films deposited at room temperature showed improved electrochemical performance and supercapacitive properties compared to those of films deposited at 450 °C. Specific capacitances of about 777.4 F g-1 and 258.5 F g-1 were obtained for electrodes deposited at RT and 450 °C, respectively, at 0.5 mA cm-2 current density. The CoFe2O4 films deposited at room temperature exhibited an excellent power density (3277 W kg-1) and energy density (17 W h kg-1). Using electrochemical impedance spectroscopy, the series resistance and charge transfer resistance were found to be 1.1 Ω and 1.5 Ω, respectively. The cyclic stability was increased up to 125% after 1500 cycles due to the increasing electroactive surface of CoFe2O4 along with the fast electron and ion transport at the surface.

Surfactant-mediated growth of nanostructured zinc oxide thin films via electrodeposition and their photoelectrochemical performance.

Zinc oxide (ZnO) thin films were electrodeposited from an aqueous zinc acetate solution onto fluorine-doped thin oxide (FTO) coated conducting glass substrates. The effect of organic surfactants like polyvinyl pyrrolidone (PVP), sodium dodecyl sulfate (SDS), polyethylene glycol (PEG), ethylene glycol (EG) and polyvinyl alcohol (PVA) on their structural, morphological, optical and photoelectrochemical properties was studied. The x-ray diffraction patterns revealed the formation of phase-pure ZnO thin films. The films deposited using organic surfactants exhibit different surface morphologies. It was observed that the organic surfactants play important roles in modifying the surface morphology and size of the crystallites. A compact granular morphology was observed for the ZnO samples grown without organic surfactants. The films exhibit nanoparticles of size 100-150 nm for PVP, EG and PVA mediated growth. The vertically aligned thin and compact hexagonal crystallites stem from the SDS, whereas microporous corrugated morphology is observed for PEG-mediated growth. All the samples exhibit room temperature photoluminescence (PL). Oxygen vacancies contribute to the active luminescent centers for the emission of green light in ZnO thin films. PL gets quenched for the SDS surfactant. All the samples were post-treated with ethanol to remove stray surfactant molecules. FTIR study was used to confirm the removal of adsorbed surfactant molecules from the samples. Moreover the samples are photoelectrochemically (PEC) active and exhibit the highest photocurrent of 231 µA, a photovoltage of 492 mV and 0.42 fill factor for the ZnO:SDS films.