Tribo-mechanical properties evaluation of HA/TiO2/CNT nanocomposite.

In this study, a combination of reverse microemulsion and hydrothermal techniques were used to synthesize HA. A hydrothermal method was used to synthesize HA/TiO2/CNT nanocomposite powders. Cold and hot isostatic pressing techniques were used to fabricate tablet-shaped samples. To investigate the biocompatibility and tribo-mechanical properties of HA/TiO2 and HA/TiO2/CNTs, four samples were prepared with different percentages of CNTs, namely, HA/TiO2 (S0), HA/TiO2/CNT (S1.0), HA/TiO2/CNT (S2.0), and HA/TiO2/CNT (S3.0). The microstructure and morphology of the HA/TiO2/CNTs were characterized by transmission electron microscopy, scanning electron microscopy, energy-dispersive X-ray spectroscopy, and X-ray diffraction. Hardness test results show that S3.0 displayed the highest surface hardness (285 HV) compared to other samples. The wear rate of HA/TiO2/CNT with the highest CNT content showed a decrease compared with those of the other samples. The results from nanoindentation tests showed that Young's modulus of the S3.0 sample was 58.1% greater than that of the S0 sample. Furthermore, the human MDA-MB-231 cell line demonstrated good binding to the surface of the samples in the in-vitro biocompatibility evaluation of the HA/TiO2/CNT composites.

Supercapacitor performance of porous nickel cobaltite nanosheets.

In this work, nickel cobaltite (NiCo2O4) nanosheets with a porous structure were fabricated on nickel foam as a working electrode for supercapacitor applications. The nanosheets were fabricated by electrochemical deposition of nickel-cobalt hydroxide on the nickel foam substrate at ambient temperature in a three-electrode cell followed by annealing at 300 °C to transform the coating into a porous NiCo2O4 nanosheet. Field emission scanning electron microscopy and transmission electron microscopy revealed a three-dimensional mesoporous structure, which facilitates ion transport and electronic conduction for fast redox reactions. For one cycle, the NiCo2O4 electrodeposited nickel foam has a high specific capacitance (1734.9 F g-1) at a current density (CD) of 2 A g-1. The electrode capacitance decreased by only approximately 12.7% after 3500 cycles at a CD of 30 A g-1. Moreover, a solid-state asymmetric supercapacitor (ASC) was built utilising the NiCo2O4 nanosheets, carbon nanotubes, and a polyvinyl alcohol-potassium hydroxide gel as the anode, cathode, and solid-state electrolyte, respectively. The ASC displayed great electrochemical properties with a 42.25 W h kg-1 energy density at a power density of 298.79 W kg-1.

Synthesis and Characterization of a NiCo2O4@NiCo2O4 Hierarchical Mesoporous Nanoflake Electrode for Supercapacitor Applications.

In this study, we synthesized binder-free NiCo2O4@NiCo2O4 nanostructured materials on nickel foam (NF) by combined hydrothermal and cyclic voltammetry deposition techniques followed by calcination at 350 °C to attain high-performance supercapacitors. The hierarchical porous NiCo2O4@NiCo2O4 structure, facilitating faster mass transport, exhibited good cycling stability of 83.6% after 5000 cycles and outstanding specific capacitance of 1398.73 F g-1 at the current density of 2 A·g-1, signifying its potential for energy storage applications. A solid-state supercapacitor was fabricated with the NiCo2O4@NiCo2O4 on NF as the positive electrode and the active carbon (AC) was deposited on NF as the negative electrode, delivering a high energy density of 46.46 Wh kg-1 at the power density of 269.77 W kg-1. This outstanding performance was attributed to its layered morphological characteristics. This study explored the potential application of cyclic voltammetry depositions in preparing binder-free NiCo2O4@NiCo2O4 materials with more uniform architecture for energy storage, in contrast to the traditional galvanostatic deposition methods.

Properties Investigation of GO/HA/Pt Composite Thin Film.

Hydroxyapatite/graphene oxide/platinum (HA/GO/Pt) nanocomposite was synthesized and electrodeposited on a pure zirconium substrate. The coated zirconium was annealed at 200, 300, 400, and 600°C in vacuum furnace in presence of argon gas. The structure and morphology of the coated samples were characterized. Biocompatibility and wear and corrosion resistances of specimens were examined. The result of corrosion tests shows that the graphene into HA/Pt composites significantly improves their corrosion resistance. The wear tests results of uncoated and coated samples before and after annealing show that coated samples annealed at 300°C had better wear resistance compared with uncoated and coated samples at other temperatures. Furthermore, the biocompatibility test shows that the coatings improved the cell attachment and proliferation compared to the pure zirconium substrate.