Boron-Doped Polygonal Carbon Nano-Onions: Synthesis and Applications in Electrochemical Energy Storage.

Doping of carbon nanostructures with heteroatoms, such as boron or nitrogen, is one of the most effective ways to change their properties to make them suitable for various applications. Carbon nano-onions (CNOs) doped with boron (B-CNOs) were prepared by annealing (1650 °C) nanodiamond particles (NDs) under an inert He atmosphere in the presence of B. Their physicochemical properties were measured using transmission (TEM) and scanning (SEM) electron microscopy, X-ray photoelectron spectroscopy (XPS), 10 B and 11 B solid-state magic-angle spinning (MAS) NMR spectroscopy, X-ray powder diffraction (XRD), Raman spectroscopy, porosimetry, and differential-thermogravimetric analyses (TGA-DTG). These properties were systematically discussed for the undoped and B-doped CNO samples. The amount of substitutional B in the CNO samples varied from 0.76 to 3.21 at. %. The TEM, XRD, and Raman analyses revealed that the increased amount of B doping resulted in decreased interlayer spacing and polygonization of the structures, which in turn led to their unusual physicochemical properties. All synthesized materials were tested as electrodes for electrochemical capacitors. The B-CNOs with low concentration of doping agent exhibited higher reversible capacitances, mainly owing to the formation of hydrophilic polygonal nanostructures and higher porosity.

Influence of the Synthetic Conditions on the Structural and Electrochemical Properties of Carbon Nano-Onions.

Thermal annealing of nanodiamonds with diameters of a few nanometers (in an inert atmosphere and at temperatures in the range: 1500-1800 °C) leads to the formation of carbon nano-onions (CNOs) with diameters between 5 and 6 nm, which correspond to nanostructures with six to eight graphitic layers. The resulting spherical CNO structures were thermally modified under different atmospheres and characterized by SEM, TEM, thermogravimetric analysis and spectroscopic (Raman and diffuse reflectance infrared Fourier transform/FTIR) spectroscopy. The electrochemical properties of the CNOs prepared under different conditions were determined and compared. The results reveal that the CNOs show different structures with predominant spherical "small" carbon nano-onions. The aim of this article is to investigate the impact of the CNO's synthesis conditions on the resulting structures and study the effect of further thermal modifications on the sizes, shapes and homogeneity of these carbon nanostructures.

Chemical versus electrochemical synthesis of carbon nano-onion/polypyrrole composites for supercapacitor electrodes.

The development of high-surface-area carbon electrodes with a defined pore size distribution and the incorporation of pseudo-active materials to optimize the overall capacitance and conductivity without destroying the stability are at present important research areas. Composite electrodes of carbon nano-onions (CNOs) and polypyrrole (Ppy) were fabricated to improve the specific capacitance of a supercapacitor. The carbon nanostructures were uniformly coated with Ppy by chemical polymerization or by electrochemical potentiostatic deposition to form homogenous composites or bilayers. The materials were characterized by transmission- and scanning electron microscopy, differential thermogravimetric analyses, FTIR spectroscopy, piezoelectric microgravimetry, and cyclic voltammetry. The composites show higher mechanical and electrochemical stabilities, with high specific capacitances of up to about 800 F g(-1) for the CNOs/SDS/Ppy composites (chemical synthesis) and about 1300 F g(-1) for the CNOs/Ppy bilayer (electrochemical deposition).