RESUMO
Integrating tunneling magnetoresistance (TMR) effect in memristors is a long-term aspiration because it allows to realize multifunctional devices, such as multi-state memory and tunable plasticity for synaptic function. However, the reported TMR in different multiferroic tunnel junctions is limited to 100%. This work demonstrates a giant TMR of -266% in La0.6Sr0.4MnO3(LSMO)/poly(vinylidene fluoride)(PVDF)/Co memristor with thin organic barrier. Different from the ferroelectricity-based memristors, this work discovers that the voltage-driven florine (F) motion in the junction generates a huge reversible resistivity change up to 106% with nanosecond (ns) timescale. Removing F from PVDF layer suppresses the dipole field in the tunneling barrier, thereby significantly enhances the TMR. Furthermore, the TMR can be tuned by different polarizing voltage due to the strong modification of spin-polarization at the LSMO/PVDF interface upon F doping. Combining of high TMR in the organic memristor paves the way to develop high-performance multifunctional devices for storage and neuromorphic applications.
RESUMO
Silicon carbide (SiC) sublimation is the most promising option to achieve transfer-free graphene at the wafer-scale. We investigated the initial growth stages from the buffer layer to monolayer graphene on SiC(0001) as a function of annealing temperature at low argon pressure (10 mbar). A buffer layer, fully covering the SiC substrate, forms when the substrate is annealed at 1600 °C. Graphene formation starts from the step edges of the SiC substrate at higher temperature (1700 °C). The spatial homogeneity of the monolayer graphene was observed at 1750 °C, as characterized by Raman spectroscopy and magneto-transport. Raman spectroscopy mapping indicated an AG-graphene/AG-HOPG ratio of around 3.3%, which is very close to the experimental value reported for a graphene monolayer. Transport measurements from room temperature down to 1.7 K indicated slightly p-doped samples (p ≃ 1010 cm-2) and confirmed both continuity and thickness of the monolayer graphene film. Successive growth processes have confirmed the reproducibility and homogeneity of these monolayer films.