Investigation of Factors Causing Nonuniformity in Luminescence Lifetime of Fast-Responding Pressure-Sensitive Paints.

Factors that cause nonuniformity in the luminescence lifetime of pressure-sensitive paints (PSPs) were investigated. The lifetime imaging method of PSP does not theoretically require wind-off reference images. Therefore, it can improve measurement accuracy because it can eliminate errors caused by the deformation or movement of the model during the measurement. However, it is reported that the luminescence lifetime of PSP is not uniform on the model, even under uniform conditions of pressure and temperature. Therefore, reference images are used to compensate for the nonuniformity of the luminescence lifetime, which significantly diminishes the advantages of the lifetime imaging method. In particular, fast-responding PSPs show considerable variation in luminescence lifetime compared to conventional polymer-based PSPs. Therefore, this study investigated and discussed the factors causing the nonuniformity of the luminescence lifetime, such as the luminophore solvent, luminophore concentrations, binder thickness, and spraying conditions. The results obtained suggest that the nonuniformity of the luminophore distribution in the binder caused by the various factors mentioned above during the coating process is closely related to the nonuniformity of the luminescence lifetime. For example, when the thickness of the binder became thinner than 8 µm, the fast-responding PSPs showed a tendency to vary significantly in the luminescence lifetime. In addition, it was found that the luminescence lifetime of fast-responding PSP could be changed in the depth direction of the binder depending on the coating conditions. Therefore, it is important to distribute the luminophore uniformly in the binder layer to create PSPs with a more uniform luminescence lifetime distribution.

Evaluation of the Characteristics and Coating Film Structure of Polymer/Ceramic Pressure-Sensitive Paint.

Polymer/ceramic pressure-sensitive paint (PC-PSP), which incorporates a high percentage of particles in the binder layer, is proposed in order to improve the characteristics of PSP. The procedure for embedding particles into the binder layer was modified. In the conventional procedure, dye is adsorbed onto a polymer/ceramic coating film (denoted herein as a dye-adsorbed (D-adsorbed) PSP). In the new procedure, the mixture of a dye and particles is adsorbed onto a polymer coating film (denoted herein as the particle/dye-adsorbed (PD-adsorbed) PSP). The effect of particle mass content on PSP characteristics was investigated. In addition, the effect of solvent on PSP characteristics and film structure were evaluated for the PD-adsorbed PSP. As a result, the difference in the PSP characteristics between the two types of PSP was clarified. Although surface roughness and time response increase with increased mass content of particles for both D- and PD-adsorbed PSPs, the critical pigment volume concentration (CPVC) for the PD-adsorbed PSP is smaller than that of the D-adsorbed PSP (88 wt% and 93 wt%, respectively). The PD-adsorbed PSP has a higher frequency response comparing with the D-adsorbed PSP while maintaining the same surface roughness. Observation by scanning electron microscope showed that the CPVC of the PC-PSP is governed primarily by surface structure. The coating film structure can be roughly classified into two states depending on the particle mass content. One is a state in which the coating film consisted of two layers: a lower particle-rich layer and an upper polymer-rich layer. This type of structure was observed in the PD-adsorbed PSP as well as in the D-adsorbed PSP. In the other state, polymer and particles are homogeneously distributed in the film, and pores are formed. This difference in the coating structure results in a change in the time response.