Obtaining Cellulose Nanocrystals from Olive Tree Pruning Waste and Evaluation of Their Influence as a Reinforcement on Biocomposites.

The objective of this work is to improve the mechanical properties of polylactic acid (PLA) by incorporating cellulose nanocrystals (CNC) previously obtained from a cellulose pulp extracted from olive tree pruning (OTP) waste. Composites were manufactured by melt processing and injection moulding to evaluate the effect of the introduction of CNC with conventional manufacturing methods. This OTP-cellulose pulp was subjected to a further purification process by bleaching, thus bringing the cellulose content up to 86.1%wt. This highly purified cellulose was hydrolysed with sulfuric acid to obtain CNCs with an average length of 267 nm and a degradation temperature of 300 °C. The CNCs obtained were used in different percentages (1, 3, and 5%wt.) as reinforcement in the manufacture of PLA-based composites. The effect of incorporating CNC into PLA matrix on the mechanical, water absorption, thermal, structural, and morphological properties was studied. Maximum tensile stress and Young's modulus improved by 87 and 58%, respectively, by incorporating 3 and 5%wt. CNC. Charpy impact strength increased by 21% with 3%wt. These results were attributed to the good dispersion of CNCs in the matrix, which was corroborated by SEM images. Crystallinity index, glass transition, and melting temperatures were maintained.

Effect of Olive Pit Reinforcement in Polylactic Acid Biocomposites on Environmental Degradation.

Polylactic acid (PLA) is a biomaterial widely used as an alternative to petroleum-based polymeric matrices in plastic components. PLA-based biocomposites reinforced with lignocellulosic waste are currently receiving special attention owing to their mechanical properties, low toxicity, recyclability, and biodegradability. The influence of the percentage of waste on their properties and resistance to degradation are some of the points of great relevance. Therefore, a series of PLA-based biocomposites containing different percentages of olive pits (5, 15, 25 and 40% wt.) were manufactured and characterized both (a) immediately after manufacture and (b) after one year of storage under environmental conditions. The results obtained were analyzed to evaluate the influence of the incorporation of olive pits on the resistance to degradation (measured through Carbonyl Indices, CI), mechanical properties (tensile, flexural and impact strength), structure (Fourier Transform Infrared Spectroscopy, FT-IR; and, X-ray Diffraction, XRD), morphology (Scanning Electron Microscopy, SEM) and water absorption capacity of the manufactured materials. PLA degradation, corroborated by Differential Scanning Calorimetry (DSC), FT-IR, and XRD, resulted in a decrease in tensile and flexural strengths and an increase in the tensile and flexural moduli. This trend was maintained for the biocomposites, confirming that reinforcement promoted the PLA degradation.

Manufacture and Characterization of Recycled Polypropylene and Olive Pits Biocomposites.

The present work studies the use of olive pit (OP) as a reinforcement in the manufacture of composites based on a post-consumer recycled polypropylene (rPP). In this way, it is feasible to provide added value from olive pits, a by-product resulting from the olive industry operations, while promoting the circular economy and reducing the use of fossil-based polymers. For this purpose, suitable samples were manufactured using 25 wt% and 40 wt% of OP. Additionally, the effect of incorporating additives was studied: (a) a process control additive (PA), and (b) a coupling agent of maleic anhydride grafted polypropylene (MAPP). The results showed an improvement in Young's and flexural modulus with the OP addition. The incorporation of PA did not present any significant improvement in the properties of the materials, nevertheless it facilitated the biocomposite manufacturing process. As for the coupling agent, it significantly improved the mechanical properties, achieving the best results with the addition of the two types of additives and 40 wt% of OP. Moreover, the thermal properties were maintained, and there was an increase in crystallinity in all composites compared to rPP. According to the results of the fracture surface analysis, the coupling agent improves reinforcement-polymer matrix cohesion.

Advanced Photonic Thin Films for Solar Irradiation Tuneability Oriented to Greenhouse Applications.

The world population is growing by 1 billion people every 10 years. There will come a time when there will be more people to feed but less land to grow food. Greenhouses can be the solution to this problem because they provide the highest production yield per m2 and also use less water, provide food safety, and offer high quality. Photosynthetic active radiation (PAR) favors vegetable growth with a specific blue and red light ratio. Thus, increasing the amount of red light improves chlorophyll absorption and photosynthetic efficiency. In this article, we present a hybrid system that combines luminescent materials and photonic crystals for better management of the light reaching the greenhouse. The luminescent dyes considered herein are combined ensuring a Förster resonance energy transfer (FRET) nonradiative mechanism to enhance the absorption range. The designed photonic crystal maximizes reflections in the Near-Infrared (NIR) range, and therefore, thermal losses are minimized. Thus, by converting harmful or ineffective radiation for plant growth to the PAR region, we aim to demonstrate growth-condition enhancement for the different vegetables that have been used as a model.

Synthesis and Characterisation of Acrylic Resin-Al Powder Composites Suitable for Additive Manufacturing.

Stereolithography is an additive manufacturing technology commonly used to build either prototypes or final parts. Nevertheless, the manufacture of structural parts has been ruled out owing to the poor mechanical properties of conventional UV-curable resins. Moreover, the inventory of available commercial resins is still limited and they exhibit low thermal and electrical conductivity values. In this work, some composite materials were designed using Al microparticles dispersed within an SLA commercial resin matrix. These composites overcame the difficulties caused by the light scattering effect during the photopolymerisation process in the SLA technology. Dispersion of the filler was characterised by means of SEM/EDX and AFM. The composites exhibited improved thermal and mechanical behaviour in comparison with the pristine resin. The simplicity of the synthesis method used to prepare the composites provides a convenient starting point to explore new ways of designing composites for SLA with improved mechanical and functional properties.

Development of Surface-Coated Polylactic Acid/Polyhydroxyalkanoate (PLA/PHA) Nanocomposites.

This work reports on the design and development of nanocomposites based on a polymeric matrix containing biodegradable Polylactic Acid (PLA) and Polyhydroxyalkanoate (PHA) coated with either Graphite NanoPlatelets (GNP) or silver nanoparticles (AgNP). Nanocomposites were obtained by mechanical mixing under mild conditions and low load contents (<0.10 wt %). This favours physical adhesion of the additives onto the polymer surface, while the polymeric bulk matrix remains unaffected. Nanocomposite characterisation was performed via optical and focused ion beam microscopy, proving these nanocomposites are selectively modified only on the surface, leaving bulk polymer unaffected. Processability of these materials was proven by the fabrication of samples via injection moulding and mechanical characterisation. Nanocomposites showed enhanced Young modulus and yield strength, as well as better thermal properties when compared with the unmodified polymer. In the case of AgNP coated nanocomposites, the surface was found to be optically active, as observed in the increase of the resolution of Raman spectra, acquired at least 10 times, proving these nanocomposites are promising candidates as surface enhanced Raman spectroscopy (SERS) substrates.